ensile stress is applied in the 101) direction. The magnitude of this tensile stress is 4 MPa, and the ritical resolved shear stress is 2.0 MPa. In this problem, we are interested in determining whether or not the rystal will slip in the [1 0 0] direction on the (0 1 2) plane. a) What is the direction of the tensile stress? Write your answer within the box below: b) What is the slip direction of interest? Write your answer within the box below: c) What is the direction normal to the slip plane? Write your answer within the box below: d) What is the resolved shear stress? Fill in answers within the boxes below: ieneral equation for the resolved shear stress: "alue of the tensile stress: ieneral equation for the angle between two direction vectors: he symbol for the angle between the tensile stress vector and the slip direction: he symbol for the angle between the tensile stress vector and the vector normal to the slip plane:

ensile stress is applied in the 101) direction. The magnitude of this tensile stress is 4 MPa, and the ritical resolved shear stress is 2.0 MPa. In this problem, we are interested in determining whether or not the rystal will slip in the [1 0 0] direction on the (0 1 2) plane. a) What is the direction of the tensile stress? Write your answer within the box below: b) What is the slip direction of interest? Write your answer within the box below: c) What is the direction normal to the slip plane? Write your answer within the box below: d) What is the resolved shear stress? Fill in answers within the boxes below: ieneral equation for the resolved shear stress: "alue of the tensile stress: ieneral equation for the angle between two direction vectors: he symbol for the angle between the tensile stress vector and the slip direction: he symbol for the angle between the tensile stress vector and the vector normal to the slip plane:

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A single crystal of an FCC metal isoriented so that the [001] direction is parallel to an applied stress of 5000 psi. Calculate the resolved shear stress acting on the (111) slip plane in the [110] and [101] slip directions. Which slip system(s) will become active first?
Consider a metal single crystal oriented such that the normal to the slip plane and the slip direction are at angles of 43.1° and 47.9°, respectively, with the tensile axis. If the critical resolved shear stress is 20.7 MPa (3000 psi), will an applied stress of 45 MPa (6500 psi) cause the single crystal to yield? If not, what stress will be necessary?
Calculate resolved shear stress on the (111) [01̅1] slip system of a unit cell in an FCC nickel single crystal if a stress of 13.0 GPa is applied in the [001] direction of a unit cell. Draw the diagram for mentioned slip system.
A single crystal of FCC metal is oriented so that the [001] direction is parallel to an applied stress of 5000 psi. Calculate the resolved shear stress on the (111) slip plane in the [1bar 10] and [01bar 1] slip directions.
A single crystal of an FCC metal is oriented so that the [001] direction is parallel to an applied stress of 34.47MPa. Calculate the resolved shear stress acting on the (111) slip plane in the [-110], and [10-1] slip directions. Which slip system(s) will become active first?
Determine the critical resolved shear stress on a BCC single crystal if a normal stress of 10 MPa along [100] direction causes slip system on (110) plan along [1-11], one-bar one-one, direction.
If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions. Which of the following is the critical resolved shear stress on the slip plane in the slip direction? Group of answer choices 24.49 MPa 34.65 MPa 12.25 MPa 102 MPa
4. Assume the critical resolved shear stress of a single crystal metal is 5.5 MPa on the slip system. Please (a) calculate the corresponding tensile stress applied along the direction that can cause such slip, and (b) what is the corresponding Schimd factor?
Consider a metal single crystal oriented such that the normal to the slip plane and the slip direction are at angles of 35.5° and 25.4° , respectively, with the tensile axis. If the critical resolved shear stress is 25 MPa, will an applied stress of 30 MPa cause the single crystal to yield? If not, what stress will be necessary? (1)Yes it is enough to yield (2)No it is not enough to yield, 31 Mpa will be enoug (3)No it is not enough to yield, 32 Mpa will be enough (4)No it is not enough to yield, 33 Mpa will be enough (5)No it is too much to yield, 24 Mpa or smaller should it be
A single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is applied parallel to the [100] direction. If the critical resolved shear stress for this material is 1.18 MPa, calculate the magnitude of applied stress necessary to cause slip to occur on the (111) plane in the [1-10] direction.
6.8 The stress axis in an FCC crystal makes angles of 31◦ and 62◦ with thenormal to the slip plane and with the slip direction, respectively. The appliedstress is 10 MN/m2.
If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions. Which of the following is the value of cos(lambda) for the angle lambda between the force direction and the slip direction? Group of answer choices 0.707 0.316 0.632 0.500