7.12 Consider a metal single crystal oriented such O that the normal to the slip plane and the slip di- rection are at angles of 60° and 35°, respectively, with the tensile axis. If the critical resolved shear stress is 6.2 MPa (900 psi), will an applied stress of 12 MPa (1750 psi) cause the single crystal to yield? If not, what stress will be necessary?

7.12 Consider a metal single crystal oriented such O that the normal to the slip plane and the slip di- rection are at angles of 60° and 35°, respectively, with the tensile axis. If the critical resolved shear stress is 6.2 MPa (900 psi), will an applied stress of 12 MPa (1750 psi) cause the single crystal to yield? If not, what stress will be necessary?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

From the work of D. C. Jillson, Trans. AIME 188, 1129 (1950), the following data were taken relating to the deformation of zinc single crystals. The crystals have a normal cross-sectional area of 122 x 10-6 m2. ϕ = angle between loading axis and normal to slip plane λ = angle between loading axis and slip direction F = force acting on crystal when yielding begins a. Identify the slip system for this material. b. Calculate the resolved shear τRSS and normal σn stresses acting onthe slip plane when yielding begins. c. From your calculations, does τRSS or σn control yielding? d. Plot the Schmid factor versus the normal stress P/ A0 acting on the rod. At what Schmid factor value are these experimentally-measured yield loads at a minimum? Does this make sense?
A metal with a hexagonal close packed structure is being pulled in tension, with the normal to its basal plane (0001) at 60° to the tensile axis and with the slip direction [1120] at 40° to the tensile axis. What tensile stress (in psi) is necessary to reach the critical resolved shear stress, τc, of 0.94 MPa (136 psi)?
Consider a metal single crystal oriented such that the normal to the slip plane and the slip direction are at angles of 35.5° and 25.4° , respectively, with the tensile axis. If the critical resolved shear stress is 25 MPa, will an applied stress of 30 MPa cause the single crystal to yield? If not, what stress will be necessary? (1)Yes it is enough to yield (2)No it is not enough to yield, 31 Mpa will be enoug (3)No it is not enough to yield, 32 Mpa will be enough (4)No it is not enough to yield, 33 Mpa will be enough (5)No it is too much to yield, 24 Mpa or smaller should it be
4. Assume the critical resolved shear stress of a single crystal metal is 5.5 MPa on the slip system. Please (a) calculate the corresponding tensile stress applied along the direction that can cause such slip, and (b) what is the corresponding Schimd factor?
Consider an iron single crystal with CCC crystal structure oriented in such a way that a tensile stress is applied to the along one direction [010]. a) Calculate the shear stress resolved along a plane (110) and a direction when a tensile stress of 52 MPa is applied. The normal to the slip plane forms 45° with traction direction. the direction of slip forms 55º with the traction direction. b) If the slip occurs in one plane (110) and in one direction and the critical resolved shear stress is 30 MPa, calculate the magnitude of tensile stress that must be applied to initiate the flow.
A single crystal of aluminum is oriented for a tensile test such that its slip plane normal makes an angle of 28.1° with the tensile axis. Three possible slip directions make angles of 62.4°, 72.0°, and 81.1° with the same tensile axis. (a) Which of these three slip directions is most favored? (b) If plastic deformation begins at a tensile stress of 1.95 MPa (280 psi), determine the critical resolved shear stress for aluminum.
Consider a single crystal of BCC iron oriented such that tensile stress is applied along a[010] direction. Compute the resolved shear stress along a (110) plane and in a [1⃑ 1 1]direction when a tensile stress of 50 MPa is applied. If Slip occurs on a (110) plane and ina [1⃑ 1 1] direction and the critical resolved shear stress is 25 MPa, calculate themagnitude of the applied tensile stress necessary to initiate yielding.
Determine the critical resolved shear stress on a BCC single crystal if a normal stress of 10 MPa along [100] direction causes slip system on (110) plan along [1-11], one-bar one-one, direction.
A metal with a hexagonal close packed structure is being pulled in tension, with the normal to its basal plane (0001) at 60° to the tensile axis and with the slip direction [1120] at 40° to the tensile axis. What tensile stress (in psi) is necessary to reach the critical resolved shear stress, τc, of 0.94 MPa (136 psi)? Answer in psi
Consider a single crystal oriented such that the slip direction and normal to the slip plane are at angles 42.7° and 48.3°, respectively, with the tensile axis. If the critical resolved shear stress is 27.1 MPa, what applied stress (in MPa) will be necessary to cause the single crystal to yield?
A monocrystal of a CCC metal is oriented so that the direction [001] is parallel to an applied voltage. Consider that the critical effective shear stress required for the slip is 83 MPa and calculate the magnitude of the applied stress necessary to start the slip in the direction [111] of the sliding planes (110), (011) and ( 101).
If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions. Which of the following is the critical resolved shear stress on the slip plane in the slip direction? Group of answer choices 24.49 MPa 34.65 MPa 12.25 MPa 102 MPa