Create a design mix using the ACI DESIGN MIXPROCEDURE with the following parameters:Non-Air Entrained ConcreteRequired Strength = 3500 psiRequired Slump = 6 inchesMaximum Size of CA = 25 mm%3DFineness Modulus of CA = 2.60Unit Weight of CA = 1600 Kg/m3SG of Water = 1.00SG of Cement = 3.15SG of CA = 2.84SG of FA = 2.40%3DIf this mix design is to be used for a concretepavement that is 1 Km long, 3.75 m wide, and 280mm thick, determine the following:1. How many Liters of water needed for theproject?2. How many Kilos of cement needed for theproject?3. How many Kilos of coarse aggregatesneeded for the project?4. How many Kilos of fine aggregates neededfor the project?5. If a concrete mixer can hold 8 cubic metersof fresh concrete, how many concrete mixeris needed for the whole project?

Answered: Image /qna-images/answer/3aed5f55-e2f5-4877-a4bc-e12a14cceb33.jpg

Answered: mix using the ACI DESIGN

Engineering

Civil Engineering

mix using the ACI DESIGN

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Design the concrete mix according to the following conditions:Design Environment• Building beamo Required design strength = 27.6 MPao Minimum dimension = 150 mmo Minimum space between rebar = 40 mmo Minimum cover over rebar = 40 mmo Statistical data indicate a standard deviation of compressive strengthof 2.1 MPa is expected (more than 30 samples).• Only air entrainer is allowed.• Moderate Sulphate exposure.• Available Materialso Air entrainer:▪ Manufacture specification 6.3 mL/1% air/100 kg cement.o Coarse aggregate:▪ 19 mm nominal maximum size▪ River gravel (rounded)▪ Bulk oven-dry specific gravity = 2.55▪ Absorption = 3.6▪ Oven-dry rodded density = 1761 kg/m3▪ Moisture content = 2.5o Fine aggregate:▪ Natural sand▪ Bulk oven-dry specific gravity = 2.659▪ Absorption = 0.5▪ Moisture content = 2▪ Fineness modulus = 2.47o Cement▪ Type II (Moderate Sulphate Resistant)▪ Specific Gravity = 3.15Based on this information, find the following and summarize the findings in a table.a) Required…
Design the concrete mix according to the following conditions:Design EnvironmentBuilding frameRequired design strength = 27.6 MPaMinimum dimension = 150 mmMinimum space between rebar = 40 mmMinimum cover over rebar = 40 mmStatistical data indicate a standard deviation of compressive strength of2.1 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification 6.3 mL/1% air/100 kg cement.Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded)Bulk oven-dry specific gravity = 2.55, absorption = 3.6,Oven-dry rodded density = 1761 kg/m3Moisture content = 2.5,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.659, absorption = 0.5,Moisture content = 2,Fineness modulus = 2.47
Design a concrete mix for the following conditions and constraints using the absolute volume method:Design EnvironmentBuilding frameRequired design strength = 27.6 MPaMinimum dimension = 150 mmMinimum space between rebars = 40 mmMinimum cover over rebars = 40 mmStatistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples)Only air entrainer is allowedAvailable MaterialsAir EntrainerManufacturer specification 6.3 ml/1% air / 100 kg cementCoarse aggregate19 mm nominal maximum size, river gravel (rounded)Bulk oven dry specific gravity = 2.55, Absorption = 0.3%Oven dry-rodded density = 1761 kg/m3Moisture content = 2.5%Fine aggregateNatural sandBulk oven-dry specific gravity = 2.659, Absorption = 0.5%Moisture content = 2%Fineness modulus = 2.47
(ASAP PLEASE) Design a concrete mix for the following conditions and constraints using the Absolute Volume Method. The material description are as follows: I. Design Environment i. Retaining Wall exposed to moderate sulfate exposure ii. Required Design Compressive Strength = 27.6 MPa iii. Standard Deviation of Compressive Strength of 1.8 MPa is expected (25 sample only) iv. Minimum dimension = 200 mm v. Minimum space between re-bars = 50 mm vi. Minimum cover over re-bars = 50 mm vii. Maximum Slump is required viii. Only air entrained is allowed II. Available Materials i. Air Entrained – Manufacture Specification 5.5ml/1% air/100 kg cement (use maximum or +2% air content) ii. Coarse Aggregates 25 mm Nominal Maximum Aggregate Size Rounded River Gravel (Note: apply water…
Design a concrete mix for the following conditions and constraints using the Absolute Volume Method. The material description are as follows: I. Design Environment i. Retaining Wall exposed to moderate sulfate exposure ii. Required Design Compressive Strength = 27.6 MPa iii. Standard Deviation of Compressive Strength of 1.8 MPa is expected (25 sample only) iv. Minimum dimension = 200 mm v. Minimum space between re-bars = 50 mm vi. Minimum cover over re-bars = 50 mm vii. Maximum Slump is required viii. Only air entrained is allowed II. Available Materials i. Air Entrained – Manufacture Specification 5.5ml/1% air/100 kg cement (use maximum or +2% air content) ii. Coarse Aggregates 25 mm Nominal Maximum Aggregate Size Rounded River Gravel (Note: apply water content reduction) Bulk Oven-dry specific gravity = 2.65 Absorption = 0.2%…
Design the concrete mix according to the following conditions: Design Environment Building frame Required design strength = 27.6 MPa Minimum dimension = 150 mm Minimum space between rebar = 40 mm Minimum cover over rebar = 40 mm Statistical data indicate a standard deviation of compressive strength of 2.1 MPa is expected (more than 30 samples). Only air entrainer is allowed. Available Materials Air entrainer: Manufacture specification 6.3 ml/1% air/100 kg cement. Coarse aggregate: 19 mm nominal maximum size, river gravel (rounded) Bulk oven-dry specific gravity = 2.55, Absorption = 0.3% Oven-dry rodded density = 1761 kg/m3 Moisture content = 2% Fineness modulus = 2.47
Choose the correct answer from the followings Use ACI method to design a concrete mix which is required to obtain f'c28 = 34.5MPa and a slump of 75mm . The fineness modulus of the aggregate is 3.0 , the bulk density of coarse aggregate is 1600 kg/m² and the maximum size is 25. Both the specific gravity of fine and coarse aggregate are 2.68. neglect the absorption and total moisture content . 1- The W/C ratio is * a-0.74 b-0.48 c-0.57 d-0.61 2- The cement content is * 420 kg/m3 240 kg/m3 204 kg/m3 402 kg/m3 3- The carse aggregate content is * 1140 kg/m3 1004 kg/m3 1040 kg/m3 1400 kg/m3 4- The fine aggregate content is * 807 kg/m3 780…
Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, subjected to freezingRequired design strength = 21 MPaSlab thickness = 300 mmStatistical data indicate a standard deviation of compressive strength of1.7 MPa is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 9.5 mL/1% air/100 kgcement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 1922 kg/m3Moisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68
Design the concrete mix according to the following conditions: Design environment Tennis court, subjected to freezing Required design strength =21 MPa Slab thickness=300 mm Statistical data indicate a standard deviation of compressive strength of 3.7 MPa is expected (for 50 samples) Only air entrainer is allowed Available materials: Air=7% Air entertainer: Manufacturer specification is 9.0 ML /1% air/100kg cement Slump=50 mm Coarse aggregate: 50 mm nominal maximum size, crushed stone Bulk volume oven-dry specific gravity=2.61, absorption=2.8%, oven-dry rodded density=1870 kg/m3 Moisture content=1% Fine aggregate: Natural sand Bulk oven-dry specific gravity=2.54, absorption=3.4% Moisture content= 4.5% Fineness modulus=2.60 Cement: Type I, relative density=3.1
You are working on a concrete mix design that requires each cubic yard ofconcrete to have 0.45 water–cement ratio, 1165 kg/m3 of dry gravel, 4% air content, and 335 kg/m3 of cement. The available gravel has a specific grav-ity of Ggravel = 2.7, a moisture content of 1.6%, and absorption of 2.4%. The available sand has a specific gravity of Gsand = 2.5, a moisture content of4.8%, and absorption of 1.5%. For each cubic meter of concrete needed onthe job, calculate the mass of cement, moist gravel, moist sand, and waterthat should be added to the batch. Summarize and total the mix design whenfinished (don’t include air entrainer in summary).
How many pounds of sand will you need with the following batch design of one cubic yard? The concrete will not have Air Entrainment. You are asked to develop a mix design for 1cy with the following requirements. Desired strength of 3,545psi concrete. The sp. gr. of the fine agg is given as 2.7. The fineness modulus of the fine aggregate is 2.98. The course aggregate has a sp. gr. of 2.86, a max aggregate size of 2", and a dry rodded weight of 116. The air content is to be 2% and the slump is 5 to 6 in.
Design the concrete mix according to the following conditions:Design EnvironmentPavement slab, Bozeman, Montana (cold climate)Required design strength = 3000 psiSlab thickness = 12 in.Statistical data indicate a standard deviation of compressive strength of250 psi is expected (more than 30 samples).Only air entrainer is allowed.Available MaterialsAir entrainer: Manufacture specification is 0.15 fl oz/1% air/100 lb cement.Coarse aggregate: 2 in. nominal maximum size, crushed stoneBulk oven-dry specific gravity = 2.573, absorption = 2.8,Oven-dry rodded density = 120 pcfMoisture content = 1,Fine aggregate: Natural sandBulk oven-dry specific gravity = 2.540, absorption = 3.4,Moisture content = 4.5,Fineness modulus = 2.68