Question 5. Some hypothetical alloy is composed of 42.5 wt% of metal A and 57.5 wt% of metal B. If the densities of metals A and B are 4.35 and 6.27 g/cm3, respectively, whereas their respective atomic weights are 91.4 and 105.3 g/mol, determine whether the crystal structure for this alloy is simple cubic, face-centered cubic, or body-centered cubic. ASsume a unit cell edge length of 0.395 nm.

Question 5. Some hypothetical alloy is composed of 42.5 wt% of metal A and 57.5 wt% of metal B. If the densities of metals A and B are 4.35 and 6.27 g/cm3, respectively, whereas their respective atomic weights are 91.4 and 105.3 g/mol, determine whether the crystal structure for this alloy is simple cubic, face-centered cubic, or body-centered cubic. ASsume a unit cell edge length of 0.395 nm.

Understanding Motor Controls

4th Edition

ISBN:9781337798686

Author:Stephen L. Herman

Publisher:Stephen L. Herman

Chapter44: Semiconductors

Section: Chapter Questions

Problem 4RQ

See similar textbooks

Similar questions

What is the atomic radius of nickel (in A) if it follows an FCC crystal structure, given that Nickel has a density of 8.9 g/mL and an atomic weight of 58.7 g/mol. Solution please. Thankyou
How many vacancies per cubic centimeter are there in gold, at ambienttemperature, assuming a lattice parameter of 0.408 nm? Gv = 1.4 × 10−19.
Calculate the number of vacancies per cubic meter in iron at 880 °C. The energy for vacancy formation is 1.08 eV/atom. The density and atomic weight for Fe are 7.65 g/cm3 and 55.85 g/mol, respectively. Express your result in exponential form with 1 decimal place.
Prof that the relation between atomic radius and lattice constant for FCC is a- 4r/V3 ? Question #3/ The atomic weight 207.2 (g/mol), crystal structure FCC, and atomic radius 0.175 nm, compute the theoretical densities of lead
The Cu3Au crystal structure is similar to the FCC crystal structure, but it does not have the FCC lattice. What is the crystal structure of Cu3Au if it has a basis of Au (0, 0, 0), Cu (0, 1/2,1/2), Cu (1/2, 0, 1/2), and Cu (1/2, 1/2, 0)? a. HCP b. Primitive cubic c. BCC d. BCT
Calculate the number of vacancies per cubic meter for some metal, M, at 811°C. The energy for vacancy formation is 0.89 eV/atom, while the density and atomic weight for this metal are 6.96 g/cm3 (at 811°C) and 55.72 g/mol, respectively.
Calculate the number of vacancies per cubic meter in iron at 855°C. The energy of vacancy formation is 1.08 eV/atom. Futhermore, the density & atomic weight are 7.65g/cm3 & 55.85 g/mol respectively.
Zinc hasthe hexagonal close-packed crystal structure. The lattice parameters for zinc are a = 0.26648 nm and c = 0.49470 nm, and the atomic radius is 0.1332 nm. Note that zinc does not have the ideal atomicpacking facto1: a)What is the number of atoms per unit cell in the hexagonal close-packed structure? b)Determine the atomic packing factor of the Zn unit c)Is the c/a ratio for zinc greater than or less than the ideal HCP c/a ratio? Will slip be harder or easier in zinc compared to the ideal HCP structure? Explain your answer fully.
The density of pure aluminum calculatedfrom crystallographic data is expected tobe 2.69955 g cm3.(a) Design an aluminum alloy that has adensity of 2.6450 g cm3(b) Design an aluminum alloy that has adensity of 2.7450 g cm3. The density of pure aluminum calculatedfrom crystallographic data is expected tobe 2.69955 g cm3.(a) Design an aluminum alloy that has adensity of 2.6450 g cm3.(b) Design an aluminum alloy that has adensity of 2.7450 g cm3.
Long Question：What are different types of lattice defects?Note: submit assignment in word format
The density of a sample of HCP beryllium is 1.844 g/cm 3 , and the lattice parameters are a 0 = 0.22858 nm and c 0 = 0.35842 nm. Calculate (a) the fraction of the lattice points that contains vacancies: and (b) the total number of vacancies in a cubic centimetre of Be
1. When Au comes into contact with Ag, it creates a solid solution that is called a substitutional solid solution. Calculate the amount of Au atoms per cubic centimeter in an Ag–Au alloy with 10% Au and 90% Ag. Pure Au has a density of 19.32 g/cm3 and pure Ag has a density of 10.49 g/cm3. 2. What is the atomic radius of nickel (in A) if it follows an FCC crystal structure, given that Nickel has a density of 8.9 g/mL and an atomic weight of 58.7 g/mol. 3. If 25 grains per square inch are measured at 100x magnification, what is the ASTM grain size number of the metal specimen?