The following curve is a result of a tensile test. The gauge length was 2 in, and the specimen diameter was 0.505 in The fracture area was round with a diameter of 0.391 in. Remember to com20000Force (pounds force)15000100005000016. The yield strength is0 0.2%O 80,000 plO 12.000 p060,000 pl85,000 p0.10.2Extension (inch)0.30.4

According to the given data Force and extension diagram is given We need to find Yield strength at…

The following curve is a result of a tensile test. The gauge length was 2 in, and the specimen diameter was 0.505 in The fracture area was round with a c 20000 Force (pounds force) 15000 10000 5000 0 O 0.2% O 80.000 pl O 12.000 pi Ⓒ60,000 pl O 85,000 psi 0 16. The yield strength is 0.1 0.2 Extension (inch) 0.3 0.4

The following curve is a result of a tensile test. The gauge length was 2 in, and the specimen diameter was 0.505 in The fracture area was round with a c 20000 Force (pounds force) 15000 10000 5000 0 O 0.2% O 80.000 pl O 12.000 pi Ⓒ60,000 pl O 85,000 psi 0 16. The yield strength is 0.1 0.2 Extension (inch) 0.3 0.4

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
6. State your answers to the following questions.Strain Gauge represents the deformation of a material through a change in resistance. If so, explain how temperature will affect the strain gauge in the experimental environment.①:In this experiment, the Strain Gauge measures the strain in micro units. Explain one possible error factor when applying a load by hanging a weight on the material with the strain gauge attached. (Hint: It is easy to shake by hanging the weight using a thread)①:
Specimen (Rebar) Original Length Length when it was clamped Diameter (mm) Internal Diameter (mm) External 1 300 mm 163mm 10 15.030 2 300 mm 180 mm 10.020 14.386 3 300 mm 197mm 9.40 15.028 Dimension of Specimen Specimen A0 P max Tensile strength Modulus of elasaticity Percent Elongation 1 474 N 179.381 2.776 MPa 19.76 MPa 13.4% 2 475 N 159.070 2.895 MPa 18.74 MPa 16.67% 3 485 N 179.381 2.706 MPa 20.058 Mpa 13.4% Result of testing Observation What is the possible discussion of these tablesP.S THIS IS NOT GRADED, ITS JUST EXAMPLES
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
The strains measured by a rosette strain gauge are
A tension test was performed on a specimen having an original diameter of 12.5 mm and a gage length of 50mm. The data are listed in the table below: Complete the following: Plot the stress-strain curve. Label the y-axis every 50 MPa, and the x-axis every 0.05 mm/mm. Plot the linear portion of the stress-strain curve (first 5 points). Label the y-axis every 50 MPa, and the x-axis every 0.001 mm/mm. Determine the approximate Modulus of Elasticity Determine the approximate Ultimate Stress Determine the approximate Fracture Stress Determine the approximate Modulus of Resilience Determine the approximate Modulus of Toughness Other Requirements: Provide an example hand-written calculation showing how you calculated one point on the curve. Remember to properly label your plots and provide axis labels with units. Hand sketched plots will not be accepted. Use Excel or similar software.
Question Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the yield strength (in MPa) of the material. - Calculate the percent elongation of the specimen at yield point. (Use at least five decimal units) - Calculate the stiffness (in MPa) of the specimen material. - Calculate the ultimate strength (in MPa) of the material. - Calculate the percent elongation of the specimen at point of ultimate strength.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
An engine part is being tested with a load of 65 000 lb. The allowable tensile stress is 10000 psi ,modulus of elasticity 40×106 psi . If the original length of specimen is 40 inches with elongation not exceeding 0.0155 inches, what diameter of the specimen is rejected.
we are to find the sheer strain, sheer stress and modulus of rigidity. table,specimen length,gauge length and diameter are given. specimen length= 140mm gauge length= 77.09mm diameter= 5mm