The yield stresses (oy) have been measured using steel and aluminum specimens of various grain sizes, as follows: Material D (um) σν (MPa) Steel 60.5 160 136 128 Aluminum 11.1 235 100 223 (a) Determine the coefficients o and kỵ in the Hall- Petch for these two materials. (b) Determine the yield stress in each material for a grain size of d=26 um.

The yield stresses (oy) have been measured using steel and aluminum specimens of various grain sizes, as follows: Material D (um) σν (MPa) Steel 60.5 160 136 128 Aluminum 11.1 235 100 223 (a) Determine the coefficients o and kỵ in the Hall- Petch for these two materials. (b) Determine the yield stress in each material for a grain size of d=26 um.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

From the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the coefficient of gradation.
(b) The yield stress for a metal changes from 450 Nmm-2to 610 Nmm-2 when the average grain diameter decrease from 0.043 mm to 0.022 mm. Determine the yield stressfor the same metal with an average grain diameter of 0.030 mm.
From the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the uniformity coefficient.
The engineering yield strength of an alloy is 80 ksi.
A copper-zinc alloy has the following properties: Grain Diameter (mm) Strength (MPa) 0.015 170 MPa 0.025 158 MPa 0.035 151 MPa 0.050 145 MPa Determine (a) the constants in the Hall-Petch equation; and (b) the grain size required to obtain a strength of 200 MPa.
Under which of the conditions below is the generalized Hooke’s law applicable for use in analysis? a. When the material distorts due to any of the normal stresses b. When the material has a negative value for Poisson’s ratio c. When the material exceeds its proportional limit but still remains elastic d. When the material’s cross-section changes along one direction Which of the following statements is false about the Poisson’s ratio? a. It is a dimensionless quantity b. It relates the modulus of elasticity E and the modulus of rigidity G c. It has a single value for isotropic and homogeneous materials d. Its magnitude is equal to the negative ratio of the longitudinal strain to the lateral strain.
Determine the percentage of ductility of a metal alloy having the following tensile stress-strain diagram.
If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force direction) at a tensile stress of 50 MPa, slip will occur in the [0 1 1] direction on the (1 1 -1) plane. Use this information to answer the following questions. Which of the following is the value of cos(lambda) for the angle lambda between the force direction and the slip direction? Group of answer choices 0.707 0.316 0.632 0.500
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.
Computational analysis has determined that a particular design of glass ceramic component has a maximum allowable tensile stress of 16 MPa Your development team has suggested that a specific grade of Wollastonite with a Youngs Modulus of 90 GPa and a specific surface energy of 0.062 J/m2 may be suitable. What would be the maximum allowable size of any internal pores or defects in the glass ceramic component? (This question has only one correct answer) a. 27.75 µm b. 13.88 mm c. 14.65 mm d. 29.29 µm e. 27.75 mm f. 13.88 µm g. 14.65 µm
the behaviour of graphite materials under stress
In order to find out the effects of the grain sizes on the mechanical strength of a metal, three different grain sizes of 10 µm, 500 nm and 10 nm were produced. What will be the yield stresses of these same metals at different average grain sizes? The yield strength for a grain or reference point is 78 MPa, while the material proportional constant is 29.2 MPa-mm1/2.