To provide some perspective on the dimensions of atomic defects, consider a metal specimen that has a dislocation density of 104 mm-2. Suppose that all the dislocations in 1000 mm3 (1 cm3) were somehow removed and linked end to end. How far (in miles) would this chain extend? Now suppose that the density is increased to 1010 mm-2 by cold working. What would be the chain length of dislocations in 1000 mm3 of material?

To provide some perspective on the dimensions of atomic defects, consider a metal specimen that has a dislocation density of 104 mm-2. Suppose that all the dislocations in 1000 mm3 (1 cm3) were somehow removed and linked end to end. How far (in miles) would this chain extend? Now suppose that the density is increased to 1010 mm-2 by cold working. What would be the chain length of dislocations in 1000 mm3 of material?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

To put lattice defects in perspective, consider a metal blank that has a dislocation density of 10^3 mm^-2 suppose all the dislocations in 1000 mm^3 are linked together as a chain.How long will this chain be in km? Now suppose that dislocation density increases to (10^10) mm^-2 with cold deformation. How long will the chain be now?
4.26(a) Iron (r = 0.124 nm, G = 70 GPa) is being deformed to a shear strain of0.3. Assuming a constant dislocation density equal to 1010 cm−2, what isthe average distance each dislocation has to move?(b) Assuming that the strain rate is 10−2 s−1, what is the average dislocationvelocity?
Consider an aluminum polycrystal with a grain size of 10 μm. If a dislocationsource at the center of a grain emits dislocations under an appliedshear stress of 50 MPa that pile up at the grain boundaries, what is the stressexperienced by a grain boundary? Take G = 26 GPa and b = 0.3 nm.
(3) The Burgers vector of a dislocation is 0.25 nm in a crystal. The shear modulus G = 40 GPa. Estimate the dislocation energy per unit length in this crystal.
Calculate the dislocation spacing of a low-angle tilt boundary in aluminumfor θ = 0.5◦. Take G = 26.1 GPa, v = 0.345, and rAl = 0.143 nm.
Which can cross-slip––an edge dislocation, a screw dislocation, or a mixed dislocation? Why?
A sample of cold-worked metal has a dislocation density of 5x1014 [m/m3]. What is the total length of the dislocation line present in the sample of 1 cm3? If the sample is made of Cu, calculate the total stored elastic energy in [J/m] within the sample for [110] slip direction.
Calculate the dislocation density in tungsten if the stress is controlled by the stress necessary to operate a Frank-Read source. The stress in the plane is 31 Mpa. Take G = 275 Gpa
The flow stress for an alloy is 115 Mpa when its dislocation density is 10^6 cm^-2 and 207 Mpa when its dislocation density is 10^8 cm^-2. When the flow stress is 359 Mpa, Find the dislocation density.
more than one answer is possible for this question. Dislocation movement is facilitated by: a) Large number of slip planes b)Decreasing impurity atom concentration c) Decreasing grain size d)High angles of misalignment between grains
5.1 Calculate the dislocation spacing in a symmetrical tilt boundary (θ =0.5◦) in a copper crystal.
Explain why BCC (body-centered cubic) materials generally have higher mechanical strength values than FCC (face-centered cubic) materials in terms of (a) slip systems and (b) extended dislocations.