What is the value of shear stress if thetorque exerted on a 6 mm diameterbrass specimen was 20 N.m.?J =32TDT =2JSelect one:O a. 471.5 kPaO b. 127.234 MPaC. 471.5 GPaO d. 0.4715 GPa

Given data: The diameter of the bar is D=6 mm The torque on the bar is T=20 Nm=20×103 Nmm

Answered: What is the value of shear stress if…

What is the value of shear stress if the torque exerted on a 6 mm diameter brass specimen was 20 N.m.? TD T = 2J D4 32 Select one: O a. 471.5 kPa O b. 127.234 MPa O c. 471.5 GPa O d. 0.4715 GPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: What is the value of shear stress if the torque exerted on a 6 mm diameter brass specimen was 20…

Q: Conventional stresses are calculated based on the actual area of specimen at any instant. Select…

A: Conventional stresses are calculated based on the actual area of specimen at any instant. Select…

Q: Quiz-3: (Optional) Find the stresses which may induced in each rod if temperature is increases by…

A: Thermal stresses developed in a material when there is restriction provided to expand. Considering a…

Q: A rod of diameter 6 mm is subjected to a tensile load of 15 kN. Then MPa is the value of tensile…

A: Tensile Stress = Load Applied/ Area of Cross Section.

Q: The following stresses were measured for a specimen: 011 = 94 MPa; 022 = 155 MPa; ơ12 = 85 MPa…

Q: Load and shape of the below knee prostheses can be modelled as two cylindrical members. Determine…

Q: Q1) (7 marks ) In the Brinell hardness test, a force F is applied to the surface of a material…

A: Other measure of hardness: Rockwell hardness test: It is used to determine the Rockwell hardness of…

Q: 09:A tensile stress is to be applied along the long axis of a cylindrical brass rod that has…

Q: 2. Determine the deformation of the steel rod shown in Fig. 2 under the given loads (E=29x10 psi).…

Q: 3. If the ultimate shear strength of steel plate is 45,000 psi, what force is necessary to punch a…

A: Given data:

Q: The rod has a diameter of 40 mm (Figure 1) It is subjected to the force system F, = 1300 N, F, = 615…

Q: TENSILE TEST DATA LO (mm) DO (mm) 80 Mild steel 6 Extension Load Stress Strain (mm) (Mpa) ???…

A: according to the given data

Q: Part A Determine the average normal stress developed in rod AB if the load has a mass of 44 kg. The…

A: Data given - M = 44 kg dAB = 8 mm

Q: TENSILE TEST DATA DO (mm) LO (mm) 6.05 Mild steel 76 Radian Torque 0??? Degree Shear stess Shear…

Q: Required information A centric load P is applied to the granite block shown. The resulting maximum…

A: Calculated force P.

Q: 38)A tensile test specimen has a gage length=3.0 inches and a diameter= .75 inches. Yielding occurs…

A: Given data:Gauge length = 3 inchesDiameter d = 0.75 inchesLoad at yield point = 38000…

Q: rigid bar with negligible weight B 0.75 m 1.5 m 2 m A = 300 mm? A = 250 mm? A = 5 mm E = 200 GPa

Q: A rod specimen of ductile cast iron was tested in a torsion-testing machine. The rod diameter was 32…

Q: a 12mm thick steel tire has a width of 110mm and an internal diameter of 800mm. It is heated and…

A: Thickness, t= 12 mm Width, w= 110 mm Internal diameter of the tire, d= 800 mm Wheel diameter, D=…

Q: .A solid rod of 12 mm diameter was tested for tensile strength with the gauge length of 50 mm. Final…

Q: E = 200 gPA deformation BC deformationn AB $ total defomation of ABCD 0 -0.75 mm O-1.4375 mm 02mm…

A: To find: The deformation in BC, AB and total deformation. Given: The modulus of elasticity is E=200…

Q: Which of the following is true for an infinitesimal stress element? (T in the options below refers…

A: Given strain are complimentary shear strain with equal magnitude.

Q: Q1-A/ In a tensile test on a metal specimen, true strain = 0.08 at a stress = 265 MPa. When the true…

Q: 7 Principal stresses of a point in a critical section of a machine component are: ₁= 80 MPa 0₂= 5…

Q: Problem 1·16 At a point in a structural member subjected to plane stress, the state of stress is :…

A: At a location in a structural part that has been exposed to plane stress, we know.If the yield…

Q: How can I solve for the %0.2 offset strain and the calculated stress? Original diameter : 6mm…

A: Stress is ratio of force applied on a material to the material's cross-sectional area. Strain is…

Q: A steel bolt and nut are tightened around an aluminum sleeve. Find the internal forces as the nut is…

A: Since the connection between the steel bolt and aluminum sleeve is rigid, thus the force experienced…

Q: 2. A steel bar, whose cross section is 0.60 inch by 4.10 inches, was tested in ension. An axial load…

Q: steel bar

A: C. No stress

Q: P=670 lb a=1.5 in b=0.5 in. c=1.0 in. d= 2.0 in What is the average shear stress in the wood…

Q: If the engineering stress is 100 MPa, and the corresponding engineering strain is 0.0015, what is…

A: Given Data: Engineering Stress σE=100 Mpa Engineering Strain ε=0.0015

Q: 2-1. A standard steel specimen of Į in. dia- meter elongated 0.0087 in. in an 8 in. gage length when…

A: Given dataDiameter of the steel specimen d=0.5inElongation of the steel specimen e = 0.0087inGauge…

Q: man value of axial force and corresponding stress values. an value of torque and corresponding…

Q: 2t, Use G = 772 GPa. Ifl= 4 m, t= 3 mm b= 80 mm, ano F= 112KN. Determine the maximum shear stress…

A: Given: The shear modulus, G = 77.2 GPa The length of beam, L = 4 m The thickness of cross-section, t…

Q: 1. A rod will be selected to support a tensile load of 74 kN. If the allowable tensile stress of the…

A: It is required to choose correct option

Q: A 4ft long rod with a 0.29 inch diameter is subjected to a 10,130Ib tensile load. What is the…

Q: The principal stresses at the critical point of a part were found to be as shown. Using the…

Q: The ultimate shear strength of a 12 mm thick steel plate is 380 MPa. What force is necessary to…

A: The ultimate shear strength of a 12 mm thick steel plate is 380 MPa. What force is necessary to…

Q: 36. A steel bar is heated from room temperature to 80oC while it is free to expand. The bar will…

A: Internal resistance offered by the object per unit normal area when external force is applied is…

Q: What is the value of shear stress if the torque exerted on a 6 mm diameter brass specimen was 20…

Q: A machine member is subjected to fluctuating stress O =0, cos(8 t). The endurance limit of the…

A: GIVEN DATA - σ=σo cos(8πt) σe=350MPa FACTOR OF SAFETY N=3.5 WE HAVE TO FIND VALYE OF ALLOWABLE…

Q: The brass has a shear modulus (G) of 40 GPa. In the torsion test calculated results, (G) was found…

Q: If a safety factor of 3 is required, the maximum allowable stress that can be applied for a design…

Q: 82. A machine component made of a ductile material is subjected to a variable loading with omin =-50…

Q: The results of a tensile test are: Diameter of the specimen Gauge length Load at limit of…

A: Given Diameter, d = 10 mm Gauge length, l = 40 mm

Q: Q. No 2. gauge length of 60 mm. Following observations were recorded: A mild steel rod of 12 mm…

A: Given Diameter =d(o)=12 mm Length =L(o)=60mm Final length =L(f)=80 mm Final diameter =d(f)= 7 mm…

Q: he principal stresses at a point in a critical section of a machine component are sigma_{1} = 60MPa,…

A: Given:σ1=60 MPaσ2=5 MPaσ3=-40 MPaσy=200 MPa

Q: Given: Tie rods in a press machine are steel alloy AISI 5160 OQT 1000 - Diameter: D= 2.00 in. E 30 x…

A: Given data as per the question Diameter of rod =2 in E =30×106Psi Length =68.5 in Axial force =40000…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

What is the value of shear stress if the
torque exerted on a 6 mm diameter
brass specimen was 20 N.m.?
J =
32
TD
T =
2J
Select one:
O a. 471.5 kPa
O b. 127.234 MPa
C. 471.5 GPa
O d. 0.4715 GPa

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Find the original cross sectional area anf original length from the given information about a tensile test done on a specimen
How can I solve for the %0.2 offset strain and the calculated stress? Original diameter : 6mm Original length : 30mm Fracture diameter : 4.54mm
A 10000N tensile force is used to pull a cylindrical rod with an initial diameter of 2 cm. During the pull, the rod's diameter decreases to 1.8 cm. What is the true stress?i ll rate. S
A rod with diameter 12mm is initially measured and market at exactly 250mm apart. This material has an ultimate of 400MPa. After a tensile load applied, distance between the marks was measured to be 250.26mm. E= 200GPa Determine : A. strain of the rod stress in the rod. B. the stress in the rod C. the factor of safety for the situation
A) An engineer works for a company that has many gray cast iron rods of different diameters and would like to design an equivalent rod that could handle a force of P= 10.0 kipkip without fracturing. What is the minimum diameter that this new rod must have to support P? B)A tensile test is being conducted on a steel-rod specimen with a gauge length of L0 = 4.0 in and an initial diameter of d0 = 0.75 in. If the final length of the rod at fracture is Lf= 5.53 in , find the percent elongation of the rod at fracture.
A tensile force of 10 kN is applied on a 0.02-m diameter and 2-m long rod. After applying theload, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. The lateral (transverse) strain is?
Engineering stress and strain are calculated using the actual cross-sectional area and length of the specimen. True or false?
A test piece is cut from a brass bar and subjected to a tensile test. With a load of 6.4 kN the test piece, of diameter 11.28 mm, extends by 0.04 mm over a gauge length of 50 mm. Determine: (i) the stress, (ii) the strain, (iii) the modulus of elasticity. (b) A spacer is turned from the same bar. The spacer has a diameter of 28 mm and a length of 250 mm, both measurements being made at 20~ The temperature of the spacer is then increased to 100~ the natural expansion being entirely prevented. Taking the coefficient of linear expansion to be 18 x 10-6/~ determine: (i) the stress in the spacer, (ii) the compressive load on the spacer. rC.G.] [64 MN/m 2, 0.0008, 80 GN/m 2, 115.2 MN/m 2, 71 kN.] Could you please answer thisquestion fully? If you use * could you please explain what you mean by it! Thank You :)
Manufacturing engineering- A single strain gauge is mounted to measure the axial strain in a simple tensile member the recorded strain is 200 microstrain, what is the axial stress ? a) If the member is of steel? b) if the member is of aluminium ? The modulus of elasticity of steel is 200 GPa and that of aluminium is 70 GPa
A square bar subjected to a tensile load of 100KN having a gauge length of 200mm, extends to a length of 0.19mm. Given the tensile strength as 200 MPa, determine, (i) Side of the bar (express in mm) (ii) Final length (express in mm) (ii) Modulus of elasticity (express in GPa)
A square bar subjected to a tensile load of 100kN having a gauge length of 200mm extends to a length of 0.19mm . Given the tensile strength as 200 MPa , determine ( 1 ) Side of the bar ( express in mm ) Final length ( express in mm ) Modulus of elasticity ( express )
In a plane stress condition, the components of stress at a point are sigma_{x}= 20MPa , sigma_{y} = 80MPa , Ty = 40 MPa . What is the maximum shear stress (in MPa) at the point?