What is the Young’s modulus in GPa AВ1 MaterialAluminum2 FormCylinder3 Diameter12.8 mm50.8 mm4 Gauge Length5 Tensile TestingTo Failure78 Load (N)Length (mm)9 050.810 733050.85111 1510050.90212 2310050.95213 3040051.00314 3440051.05415 3840051.30816 4130051.81617 4480052.83218 4620053.84819 4730054.86420 4750055.8821 4610056.89622 4480057.65823 4260058.4224 3640059.18225

Calculate the initial length. Li=50.8 mm Calculate the average of final lengths. Lf=53.6416 mm

Answered: What is the Young’s modulus in GPa

Engineering

Mechanical Engineering

What is the Young’s modulus in GPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. Question 1 ;Determine the elastic energy absorption capacity (in N.mm) of that specimen. Question 2; Determine the plastic energy absorption capacity (in N.mm) of that specimen.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Determine the true stress (in MPa) at yield point. - Determine the true stress (in MPa) at point of ultimate strength. - Determine the true stress (in MPa) at fracture point. - Determine the true strain (in mm/mm) at yield point. (Use at least five decimal units) - Determine the true strain (in mm/mm) at point of ultimate strength. (Use at least five decimal units) - Determine the true strain (in mm/mm) at fracture point. (Use at least five decimal units)
I want answers to all four questions if possible. Thanks for help :) Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) - Determine the toughness index number (in N.mm/mm3) of the material.
Question Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the yield strength (in MPa) of the material. - Calculate the percent elongation of the specimen at yield point. (Use at least five decimal units) - Calculate the stiffness (in MPa) of the specimen material. - Calculate the ultimate strength (in MPa) of the material. - Calculate the percent elongation of the specimen at point of ultimate strength.
a . Sketch stress strain curve if the result shown in table represent the force and extension happened in steel, and show Mechanical properties that we get from tensile test on curve? (10p)Note : Lo=80 mm , Do=10 mm , use excel to plot the curve ExtensionLoad(mm) (N)0 0.900.83 4694.341.67 4831.412.50 4781.083.33 4918.834.17 4926.585.00 5257.075.83 5437.016.66 5575.888.33 5775.189.16 5847.5210.83 5965.4111.67 6010.5312.50 6042.5713.33 6072.2614.16 6092.9315.00 6113.2416.67 6140.3617.50 6146.3718.33 6148.1419.16 6149.1725.00 5940.2125.83 5675.3326.67 4725.52b. What is meant by modulus of rigidity? if it increases what does happen to material? (2p)
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
The following data were obtained during a tensile test of an alluminium alloy specimen. Initial diameter = 18mm Original gauge length = 45mm Final gauge length = 53mm Load at elastic limit = 82kN Yield load = 93kN Maximum load = 168kN Determine the Yield stress - answer to be provided in MPa correct to 3 decimal
Specimen (Rebar) Original Length Length when it was clamped Diameter (mm) Internal Diameter (mm) External 1 300 mm 163mm 10 15.030 2 300 mm 180 mm 10.020 14.386 3 300 mm 197mm 9.40 15.028 Dimension of Specimen Specimen A0 P max Tensile strength Modulus of elasaticity Percent Elongation 1 474 N 179.381 2.776 MPa 19.76 MPa 13.4% 2 475 N 159.070 2.895 MPa 18.74 MPa 16.67% 3 485 N 179.381 2.706 MPa 20.058 Mpa 13.4% Result of testing Observation What is the possible discussion of these tablesP.S THIS IS NOT GRADED, ITS JUST EXAMPLES
The following results were obtained in a tensile test on a mild steel specimen of original diameter 28 mm and gauge length 56 mm. Load at limit of proportionality : 96 kN Extension at 96 kN load : 0.068 mm Load at yield point : 105 kN Maximum load : 170 kN When the two parts were fitted together after being broken, the length between gauge length was found to be 65.8 mm and the diameter at the neck was 18.8 mm. Calculate: (a). E, (b).σy, (c).σu, (d). PRIA and PE
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
In a stress strain curve of mild steel, the elastic limit will be before the limit of proportionality . Select one: True False