10. Calculate the store energy in 1 cm³ of iron crystal due to presence of 10$ cm/cm³ of screw dislocations.The shear modulus of iron is 8.6x101ºPa and Burgers vector equals 2.48x10-10 m. Assume that radius ofdislocation core is equal to b.

Answer: Stored energy = 3.2 x 10-3 Joule/cm3

Answered: 10. Calculate the store energy in 1 cm³…

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A sample of cold-worked metal has a dislocation density of 5x1014 [m/m3]. What is the total length of the dislocation line present in the sample of 1 cm3? If the sample is made of Cu, calculate the total stored elastic energy in [J/m] within the sample for [110] slip direction.
Calculate the dislocation density in tungsten if the stress is controlled by the stress necessary to operate a Frank-Read source. The stress in the plane is 31 Mpa. Take G = 275 Gpa
Please show how the value of b was calculated Calculate the dislocation density in tungsten if the stress is controlled by the stress necessary to operate a Frank-Read source. The stress in the plane is 31 Mpa. Take G = 275 Gpa
In Fig. 3.2, must it be true that the dislocation segments at points C and C' are screw dislocations? And must it be true that they are of opposite sign?
Calculate the dislocation spacing of a low-angle tilt boundary in aluminumfor θ = 0.5◦. Take G = 26.1 GPa, v = 0.345, and rAl = 0.143 nm.
To put lattice defects in perspective, consider a metal blank that has a dislocation density of 10^3 mm^-2 suppose all the dislocations in 1000 mm^3 are linked together as a chain.How long will this chain be in km? Now suppose that dislocation density increases to (10^10) mm^-2 with cold deformation. How long will the chain be now?
Consider dislocations blocked with an average spacing of in a coppercrystal. If the flow stress is controlled by the stress necessary to operate aFrank--Read source, compute the dislocation density ρ in this crystal when itis deformed to a point where the resolved shear stress in the slip plane is 42MPa. Take G = 50 GPa.
You may look up any parameters you need. Calculate the energy per unit length of edge and screw dislocations in Copper. What can you say that is definite about which must be bigger in general? PLEASE SHOW ALL WORK!!
Consider an aluminum polycrystal with a grain size of 10 μm. If a dislocationsource at the center of a grain emits dislocations under an appliedshear stress of 50 MPa that pile up at the grain boundaries, what is the stressexperienced by a grain boundary? Take G = 26 GPa and b = 0.3 nm.
Cite the relative Burgers vector–dislocation line orientations for edge, screw,and mixed dislocations.
If a series of dislocations produced by a single FrankRead source encounter an impassible barrier, a back stress is created. What is the reason for this back stress, and why is it very effective for dislocations produced by a single F-R source?
The flow stress for an alloy is 115 Mpa when its dislocation density is 10^6 cm^-2 and 207 Mpa when its dislocation density is 10^8 cm^-2. When the flow stress is 359 Mpa, Find the dislocation density.

SEE MORE QUESTIONS

Recommended textbooks for you

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Control Systems Engineering

Mechanical Engineering

ISBN:

9781118170519

Author:

Norman S. Nise

Publisher:

WILEY

Mechanics of Materials (MindTap Course List)

Mechanical Engineering

ISBN:

9781337093347

Author:

Barry J. Goodno, James M. Gere

Publisher:

Cengage Learning

Engineering Mechanics: Statics

Mechanical Engineering

ISBN:

9781118807330

Author:

James L. Meriam, L. G. Kraige, J. N. Bolton

Publisher:

WILEY

SEE MORE TEXTBOOKS

10. Calculate the store energy in 1 cm³ of iron crystal due to presence of 10* cm/cm³ of screw dislocations. The shear modulus of iron is 8.6x101ºPa and Burgers vector equals 2.48x10-1º m. Assume that radius of dislocation core is equal to b.