Image shows a part of the phase diagram typical of a simple steel. Describe what would be observed as the melt at a is allowed to cool to room temperature. 1600aoLiquid1200austenite800Y + cementite400ferritea + cementite123457Mass percentage of carbonFig. 4 A part of the phase diagram typical of a simple steel.Temperature, orcFe,C cementite

Answered: Image /qna-images/answer/6fdc3830-6a68-4089-a61b-d2ec867b42af.jpg

1600 ao Liquid 1200 austenite 800 Y + cementite 400 ferrite a + cementite 1 2 3 4 5 7 Mass percentage of carbon Fig. 4 A part of the phase diagram typical of a simple steel. Temperature, orc Fe,C cementite

1600 ao Liquid 1200 austenite 800 Y + cementite 400 ferrite a + cementite 1 2 3 4 5 7 Mass percentage of carbon Fig. 4 A part of the phase diagram typical of a simple steel. Temperature, orc Fe,C cementite

Principles of Instrumental Analysis

7th Edition

ISBN:9781305577213

Author:Douglas A. Skoog, F. James Holler, Stanley R. Crouch

Publisher:Douglas A. Skoog, F. James Holler, Stanley R. Crouch

Chapter2: Electrical Components And Circuits

Section: Chapter Questions

Problem 2.10QAP

See similar textbooks

Related questions

Q: 6 The graphite anodes have to be replaced regularly. Why is this? 7 Why is it so much more…

A: Bauxite is a sedimentary rock and it is the ore of Aluminum. The chemical composition of bauxite is…

Q: What is the composition, in atom percent, of an alloy that consists of 30 wt% Zn and 70 wt% Cu? What…

Q: define phase chaneg and calculate the amount of each phase present in 15 kg of 60 wt% Pb-40 wt% Sn…

A: Phase change is defined as the change in the physical state of the component or the change in the…

Q: 6-Soluble in ferrite and increases yield strength, tensile strength, toughness and hardness It is…

A: Steel is made up of Fe, C, V, Si, Ni, Mn, Cu, Cr.

Q: Qualitatively predict the trends in melting point, boiling point, and hardness of metals?

A: Melting Point : If we compare two closely associated elements (one metal and other non metal) then…

Q: Calculate the composition, in weight percent, of an alloy that contains 218.0 kg titanium, 14.6 kg…

A: Given: Mass of titanium = 218.0 Kg Mass of aluminium = 14.6 Kg And mass of vanadium = 9.7 Kg.

Q: >The elements Mn and Si are added to steel to improve its properties in electric motors, and some…

A: Small sized non metals occupy the metallic lattice sites in interstitial alloys.

Q: B. What are the effects of adding elements (Ni. Cr, Si and S) on steel?

Q: A type of cast iron containing 3.1-4 wt% C and 1.7-3 wt% Si. * a. Compact graphite b. Malleable…

Q: Indicate the coordination number of the metal for [Pt(en)3](ClO4)4

A: According to the wener theory the coordination number is secondary valancy of metal ion.

Q: A sample of pig iron contains 3.4 % C, 2% Si, 2% P. The remainder being iron. Discuss briefly how…

A: Steel has high tensile strength. It is one of the most important construction materials. It is used…

Q: When found in nature, which of the following metal ions would prefer to bind to sulfide rather than…

A: The general chemical formula of sulfide minerals is : AmSn. Where, A is metal S is sulfur m,n are…

Q: Sterling silver (silver 925) is a substitutional solid solution alloy consisting of 92.5 wt% Ag and…

Q: >Name three advantages of making metal components from the powder metallurgical process.

A: The important three advantages of Powder metallurgy are given below.

Q: Find melting points of the materials: Aluminum…

Q: How is the steel used for the manufacture of metal structures and pipes for the transfer of…

A: Production of ingots1. Molten steel is manufactured by melting iron ore and coke (a carbon-rich…

Q: TABLE 22.2 General Characteristics of Cutting-tool Materials (These Materials Have a Wide Range of…

A: The given table shows the trend observed in the properties of High-speed steels, cast-cobalt alloys,…

Q: 5. Calculate the conductance and the conductivity of a metal if the resistivity of the metal is…

Q: 1. Write a short description about the physical and chemical properties of a copper at standard…

Q: Given the formula of some materials, identify the principal metal than can be extracted from each…

A: Alloy is the mixture of two or more elements combined together.

Q: describe the important features of the microstructure for low carbon steel, medium carbon steel…

A: We need to discuss about different types of iron and steel.

Q: blast furnace makes pig iron containing 3.6% C, 1.4% Si and 95% Fe. The ore used contains 80% FE2O3,…

Q: Describe how Zn is used to protect the surface of steel products. What is the name of this process?

A: Zinc metal has a number of characteristics that make it a well-suited corrosion protective coating…

Q: A basic lining is given to a furnace by using:(a) Calcined dolomite(b) Copper sulphate(c)…

A: The metallic compounds which are found in nature, called as minerals whereas the minerals which can…

Q: 1. Which of the following is not an essential constituent of potter's clay? a. Feldspar. b. Glass.…

A: Hi! Thank you for the question, As per the honor code, we are allowed to answer one question at a…

Q: Provide a general description of how hydrometallurgy is used to extract metals from ores.

A: Extractive metallurgy is the practice of removing valuable metals from an ore and refining the…

Q: How can evacuated the hot gases formed by reactions of the molten metal in die casting?

A: When metal parts of certain geometry are to be produced at a faster rate, die casting process is…

Q: Give some detail on how new ceramics are used in manufacturing and illustrate the processing method.

A: Please find your solution below : In manufacturing, particularly in the chemical and petrochemical…

Q: 1. Explain the magnetic properties of Mno Zno 2Fe;O, based ferrite on its structure.

A: Magnetic properties: The Magnetic properties (introductory penetrability and relative misfortune…

Q: Some options Choose Correct option for the main hardening those in cement s. a) Trucall ciam…

A: The hardening of cement is basically due to the hydration of the compounds present in the cement…

Q: How much heat is released or absorbed in the reaction of 10.0 grams of SiO2 (quartz) with excess…

Q: type of cast iron containing 3-4 wt% C and 1-3 wt% Si. a. Compact graphite b. Malleable cast iron…

Q: How is steel manufactured by acid bessemer process? What are the advantages and disadvantages of…

A: The acid Bessemer process consists essentially of blowing air through molten pig iron to oxidize the…

Q: PART B Q1 (a) Figure 5 shows the type of point defects that may presence in a metal. Compare the…

A: There are 5 types of point defects, named as, 1. Vacancy defect 2. Interstitial impurity 3.…

Q: Type of Steel % Carbon Characteristics Uses Low-carbon steel < 0.2 % Malleable and ductile Chains…

A: The size of iron atoms is larger than the carbon atoms.

Q: Arrange in decreasing order of thermal expansion co-efficient: steel, polyethylene, silver, Teflon,…

Q: Which of the following could be useful as an elemental semiconductor? Cu O F O K As Xe

A: Materials whose conductivity is lies between the conductors and insulators are known as…

Q: Which TWO of the following properties are generally HIGHER for steel when compared with aluminium?…

A: Note: According to our guidelines we are supposed to answer only one question. Kindly repost other…

Q: What is the basic principle of zone refining of metals?

A: In nature,metals are not found in pure form . They exist in the form of compounds called ores.Metals…

Q: Plaster of Paris is made from(a) Lime stone(b) Slaked Lime (c) Quick lime(d) Gypsum

A: Plaster of Paris is used in hospitals for setting fractured bones in right position for healing.

Q: 4.14 What is the composition, in atom percent, of an O alloy that consists of 5.5 wt% Pb and 94.5…

A: 4.14 Weight % of Pb = 5.5 %Weight % of Sn = 94.5 %The atomic weight of Pb is 207.2 a.m.uThe atomic…

Q: Estimate the coordination number for the cation in each of these ceramic materials; FeO, on the…

A: Radius of Fe2+ = 0.088 nm Radius of O2- = 0.120 nm

Q: What is added to molten iron to make steel? * O A small amounts of carbon B limestone and coke C…

A: Blast furnace is a large cylindrical object made up of the heated bricks which is used for the steel…

Q: Define An alloy

A: ANSWER

Q: Which row describes the uses of aluminium, copper and mild steel? aluminium copper mild steel A…

Question

Image shows a part of the phase diagram typical of a simple steel. Describe what would be observed as the melt at a is allowed to cool to room temperature.

1600
ao
Liquid
1200
austenite
800
Y + cementite
400
ferrite
a + cementite
1
2
3
4
5
7
Mass percentage of carbon
Fig. 4 A part of the phase diagram typical of a simple steel.
Temperature, orc
Fe,C cementite

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Thermodynamic Aspects of Phase Transitions

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, chemistry and related others by exploring similar questions and additional content below.

Similar questions

Q. What are the advantages of pyrolytic graphite coatings for furnaces? Q. Why is argon preferred to nitrogen as the purge gas? Q. Why are fast response electronics and background correction essential when using furnace atomization?
A thin film of zinc is to be deposited on one side of a steel sheet. Determine the zinc film thickness per 1cm2 of steel sheet if 2 A current was used and the electrolytic deposition process was done for exactly 30 minutes at 25oC. The zinc solution has a concentration of 1 M and can be assumed to be constant throughout the process. pls explain the solution shown in the figure thoroughly or you can come up with your own thank you
6.1) At the composition of 0.77% by weight C, identify the phase(s) presentat 950 degrees C 6.2) When the specimen is at 950 degrees C, what is the maximum C composition at which a single phase Austenite is stable?6.3) If we slowly cool a Fe-C alloy with 0.77% by weight C, austenitized at950 degrees C, to just below the eutectoid temperature of 727 degrees C, give the weight percentage and composition of the phases present based on the phase diagram given above6.4) If we cool very quickly a Fe-C alloy with 0.77% by weight C,austenitized at 950 degrees C, to room temperature, give the weight percentage and composition of the phase(s) present
A thin film of zinc is to be deposited on one side of a steel sheet. Determine the zinc film thickness per 1cm2 of steel sheet if 2 A current was used and the electrolytic deposition process was done for exactly 30 minutes at 25oC. The zinc solution has a concentration of 1 M and can be assumed to be constant throughout the process.
A 90 wt% Ag-10 wt% Cu alloy is heated to a temperature within the β + liquid phase region. If the composition of the liquid phase is 85 wt% Ag, determine:(i) The temperature of the alloy(ii) The composition of the β phase(iii) The mass fractions of both phases
Microstructure of a steel contain 100% coarse pearlite it carbon content is reported to be 0.65% is it possible? And why ?
Knowing that an electroplating industry wants to coat a steel sheet with a layer of metallic Cu by an electrodeposition process, what is the time to deposit a 50 μm layer on a 10 cm2 plate applying a current density of 30 mA /cm2 if process efficiency is 75%.
how the liquid junction potential can be eliminated ?
JUST PART B PLEASE! 11) JJ Techie calcined some ceramic powders at 1600℃ for 12 hrs, when removed from the furnace, JJ was upset to find a big hard lump. Explain to JJ what happened. b) After grinding up to the lump, someone told JJ to add a sintering aid and deflocculant to the ceramic before trying to press it into cylinders 10 inch by 0.25 inch in diameter. Do you have any suggestions for JJ? JJ needs this size ceramic rod for experiments.
10.11/ A 1.5-kg specimen of a 90 wt% Pb-10 wt% Sn alloy is heated to 250°C (480°F), at which temperature it is entirely an a-phase solid solution . The alloy is to be melted to the extent that 50% of the speci- men is liquid, the remainder being the a phase. This may be accomplished either by heating the alloy or changing its composi- tion while holding the temperature con- stant. (a) To what temperature must the speci- men be heated? (b) How much tin must be added to the 1.5-kg specimen at 250°C to achieve this state? 10.15) A magnesium-lead alloy of mass 5.5 ka consists of a solid a phase that has a compo- sition that is just slightly below the solubility limit at 200°C (390°F). (a) What mass of lead is in the alloy? (b) If the alloy is heated to 350°C (660°F). how much more lead may be dissolved in the a phase without exceeding the solubility limit of this phase? 10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass…
2. (d) Describe three of the functions of the matrix in fibrereinforced composites. (e) With the aid of sketches compare and contrast the fatigue fracture appearance between an alloy that failed at a low fatigue load and one that failed at a high fatigue load. (f) Propose and briefly describe one non-destructive method that can be used to detect small cracks on the surface of a metallic alloy .
The layer thicknesses are L1, L2 = 0.6L1, and L3 = 0.5L1. The thermal conductivities are k1, k2=0.6k1 and k3= 0.9k1. The temperatures at the left side and right side of the wall are TH=30OC and TC= -15OC, respectively. Thermal conduction is steady.What is the temperature difference ΔT2 across layer 2(between the left and right sides of the layer)?