7. The following figure shows the continue cycling transformation diagram for a 0.35wt.%C iron-carbon alloy superimposed by 5 continuous cooling curves marked as (a), (b), (c), (d) and (e), respectively. What is the final microstructure for each of the five continue cooling conditions?

7. The following figure shows the continue cycling transformation diagram for a 0.35wt.%C iron-carbon alloy superimposed by 5 continuous cooling curves marked as (a), (b), (c), (d) and (e), respectively. What is the final microstructure for each of the five continue cooling conditions?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Identify the composition of the eutectic mixture. What is its relevance?

Q: Torricellian vaccum is

A: answer is 2nd option, Barometer.for solution refer below image.

Q: Carbon nitrating is a case hardening process in which a steel is heated in a gaseous atmosphere of…

A: It is a modified nitriding process in which a gas containing carbon is added to the ammonia…

Q: For a 99.65 wt% Fe-0.35 wt% C alloy at a temperature just up the eutectoid teamperature, determine…

A: Given DataC0=0.35%C2=0.76% C1=0.02% (From Fe-Fe3C phase Diagram)

Q: .17 Determine the relative amounts (in terms of mass fractions) of the phases for the alloys and…

Q: n a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture…

A: Given: Ectetiod Temperature = 723 °CAusentic mixture = 2% C

Q: Question 3 Using the binary phase diagram below, explain what happens as the Pb-Sn compound with 70%…

Q: T° C) 1600 L 1400 1200 1148°C (austenite) 1000 800 a 727°C =T 600 0.008 400 6.67 (Fe) C, wt% C 1.…

A: (1) In this, we have to level two phase regions with the name of phases in the given diagram.

Q: Using the continuous-cooling transformation diagram for a eutectoid Fe-C alloy shown below, perform…

A: Given:

Q: Your friend in the lab has been working with a 90% Dc, 10% Vr alloy and developed the…

A: T-T-T (Time Temperature Transformation) diagram: The basis of heat treatment is the…

Q: a binary phase diagram ( pressure omitted) what is the maximum number of phases that can coexist for…

A: The two components system are called binary system. The restriction on constant temperature and…

Q: What type of grain structure in terms of chemical composition does non equlibrium cooling produces…

A: To choose: The correct answer.

Q: b) sketch corresponding heat treatment profile with To, T1, T2 shown c) and corresponding…

Q: b) At a temperature just above the isotherm at 1830C, for the 30 wt% Sn Alloy, calculate the…

A: Given data: The temperature of the composition at 183°C. The composition weight% of Sn alloy is,…

Q: Using the isothermal transformation diagram for an iron-carbon alloy of eutectoid composition,…

A: Assume the given specimen of iron-carbon alloy is having homogeneous Austenitic structure initially.…

Q: Composition (at % Cu) 10 20 30 1200 600 a+ L Consiuer the given Al-Cu phase 1000 diagram. How much…

Q: What are the equilibrium phases, compositions, and phase fractions in a sample with overall…

A: Given data To determine the phase, Compositions and phase fractions in a sample of 40%wtCu at 6000C

Q: 2. The microstructural design of Fe –C alloys has led to the development of a vast range of steels…

A: Given: Fe-C phase diagram:

Q: 6. Match the proper description of the microstructure depicted below. Put the corresponding…

A: Alloy metals can exist in different phases. Phases are substantially homogeneous states of an alloy.…

Q: 20. The equilibrium vapor pressure of solid Cu as a function of temperature is given by 45,650 In…

Q: Problem 1 A 30 wt% Sn-70 wt% Pb alloy is heated to a temperature within the aliquid phase region. If…

A: Problem 1: The unknown temperature with unknown phase composition marked on Pb-Sn diagram is given…

Q: 12) If you have an alloy with a composition of 50 wt% Ag at a temperature of 778.9° C, identify: a)…

A: Given for a Cu-Ag phase wt% of Ag is 50% Temperature = 778.9 degree C Eutectoid Temperature = 779…

Q: ) Is it advisable to have austenite in the HAZ (Heat Affected Zone)? Explain?

A: Explanation- Whenever a material (steels) welds with a specific welding process, there will heat…

Q: C/ Bismuth (Bi) was melted at 2710C and tin (Sn) was melted at 2320C. Bismuth and ten are formed a…

A: The bismuth - tin phase diagram is given below -

Q: To produce martensite, do you need to use a very slow cooling rate? Why or why not ?

A: Heat treatment is the process in which metal heat without reaching its molten point and then cool it…

Q: 1-Pointed all the phases for this type of phase equilibrium diagram. 2-Draw the cooling carves for…

Q: Quenching is a process used to preserve at room temperature a phase which exists in equilibrium at…

A: We are authorized to answer one question at a time since you have not mentioned which question you…

Q: What is the mass flow rate of zinc in the scrap brass stream (ṁZn,3) in kg/h to 0 decimal place?…

Q: 3. For the regions and points on the Fe-C phase diagram given bellow, write the corresponding phases…

A: The reaction and corresponding composition phases are written from diagram as,

Q: The lead and tin are partially dissolved in each other in solid state although they completely…

Q: Q4: For a 98 wt% Fe-2 wt% C at a temperature 700 °C, determine the following: a) The Number and…

A: Find those answers using the iron iron carbide diagram, First draw the iron iron carbide diagram…

Q: Using the time-temperature-transformation diagram, what steel phases would you generate by cooling…

A: Givan under:

Q: For hypoeutoctoid plain carbon steel(select %C content yourself), determine the phasesthat are…

A: Steels with a carbon weight percentage of 0.8 are called eutectoids. Steels with a carbon weight…

Q: The Fe – Au solid – liquid T – xB phase diagram can be viewed as the intersection of a solid – phase…

A: Let's first understand the mole fraction to discuss the concept of the problem. The mole fraction of…

Q: i) For a 68 wt% Zn-32 wt% Cu alloy, make schematic sketches of the microstructure that would be…

A: given Diagram consists of 4-temperature composition

Q: The solubility of tin in lead matches that required for precipitation hardening. Yet tin does not…

A: In the case of Solid solution hardening of lead alloys, rate of improvement in hardness generally…

Q: In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic…

A: Given: The carbon percentage = 2% The temperature of austenite mixture, T = 1100 C The eutectoid…

Q: A mixture of 1.0 mol of hexane and 1.0 mol of nitrobenzene was prepared at 290 K. Calculate the…

A: At T=290K xN=0.17, xN=0.65 By using formula (lever rule) nαIα=nβIβ nαnβ=IβIα =0.650.17=3.82 or 3…

Q: 3. (a) What is hot shortness? How does it affect the temperature at which eutectic alloys can be…

A: Note: Since you have posted a question with multiple sub-parts, we will solve the first three…

Q: Q.1. For hypereutectoid plain carbon steel (select %C content yourself), determine the phases that…

Q: For a 99.65 wt% Fe-0.35 wt% C alloy at a temperature just up the eutectoid teamperature, determine…

A: Given At 99.65% Fc -0.35 wt%

Q: An alloy of Component A and Component B, which do not react but are miscible in all proportions in…

A: Phase Diagrams: It is an equilibrium diagram which represents the composition of constituent…

Q: 1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13…

A: 1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13…

Q: A/ The lead and tin are partially dissolved in each other in solid state although they completely…

A: Given: The lead melting point, TPb = 329°C The tin melting point, TSn = 232°C The mass of α at…

Q: Quenching a hypereutectoid steel from a two-phase region of austenite and cementite; the phases…

A: Given: Quenching a hypereutectoid steel from a two-phase region of austenite and cementite; the…

Q: A/ The lead and tin are partially dissolved in each other in solid state although they completely…

A: The lead melting point, TPb = 329°C The tin melting point, TSn = 232°C The mass of α at eutectic…

Q: An intermetallic compound is represented by what on a phase diagram? a) Horizontal line b) Vertical…

A: Correct option is (b) by vertical line .

Q: Explain shortly what you know about the following terms as applied in heat treatment.…

Question

1000
800
A→F
600
400
A M
200
(b) (с)
(e)
(a)
(d)
0.1
10
103
105
107
Time (s)
Temperature (°C)

7. The following figure shows the continue cycling transformation diagram for a
0.35wt.%C iron-carbon alloy superimposed by 5 continuous cooling curves marked as
(a), (b), (c), (d) and (e), respectively. What is the final microstructure for each of the five
continue cooling conditions?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Phase Diagrams and Its Applications in Metallurgy

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Consider the temperature-composition phase diagram shown below, which represents a solid-liquid equilibrium based on a (liquid) mixture of A and B at high temperatures. A mixture with overall B composition of 0.57. What is the ratio of the amount of solid containing 0.67 B and 0.33 A to the amount of the eutectic mixture at the eutectic temperature?
Q1/ The figure below shows the phase equilibrium diagram for copper and silver Answer the following paragraphs? Conpostin a% 39 o = « & o Tepertue (F) @ Composttan (w5 ) 0 1- define pointe E? 2- define pointe B? 3- define the line AE? 4- define the line BG? 5- define the line FG?
What is the mass flow rate of zinc in the scrap brass stream (ṁZn,3) in kg/h to 0 decimal place? What is the mass fraction of copper in the mixed scrap stream (xCu,4) to 2 decimal places?
(a) Sketch a Pressure-Temperature phase diagram for a pure substance X where liquid X is less dense than solid X. Insert an isobar at 1 atm and an isotherm at 300 K. Clearly label all physical states, triple point, critical temperature and any normal transition temperatures.
Define the natural tendency of water to evaporate in order to achieve phase equilibrium with the water vapor in the surrounding air forms the basis for the operation of evaporative coolers
In a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.
Carbon nitrating is a case hardening process in which a steel is heated in a gaseous atmosphere of such composition that carbon and nitrogen are absorbed simultaneously. Carbon nitridinf is a modification of the nitriding process.
Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to point D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine theweight in each phase. Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phase
10.15) A magnesium-lead alloy of mass 5.5 ka consists of a solid a phase that has a compo- sition that is just slightly below the solubility limit at 200°C (390°F). (a) What mass of lead is in the alloy? (b) If the alloy is heated to 350°C (660°F). how much more lead may be dissolved in the a phase without exceeding the solubility limit of this phase?
In a binary phase diagram ( pressure omitted) what is the maximum number of phases that can coexist for at least one degree of freedom?
10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?
An alloy of Component A and Component B, which do not react but are miscible in all proportions in molten state, is used to manufacture “Fail Safe” devices for boiler. Narrate the effect of composition on equilibrium: Solid ↔ Liquid with the help of a phase diagram, if the melting point of A (900 ºC), B (350 ºC) and the lowest melting of all compositions is 280 ºC at 12.6% of A and 87.4% of B.