A 1.250 g sample of bauxite (the primary ore of aluminum) was analyzed for aluminum. The sample waspowderized and treated in concentrated nitric acid. The nitric acid was removed and solids were treated inhot water with added nitric acid. Insoluble solids were removed by gravity filtration. The solution wasmade basic by the slow addition of dilute ammonia forming the gelatinous precipitate (Al(OH), andAl,O,.x H2O). The precipitate was heated to coagulate it then filtered over filter paper. The paper andsolids were placed in a porcelain crucible and the paper was ashed while the precipitate was ignited at600°C to convert the precipitate to pure Al,O,. The mass of Al,O, recovered was 0.2890 g. The averagemass of ash after charring 10 sheets of the identical filter paper was 0.0007 g. Calculate the percentaluminum in the bauxite ore sample.

Given: Weight of sample of bauxite = 1.250 g Mass of Al2O3 recovered =0.2890 g Mass of Ash = 0.0007…

A 1.250 g sample of bauxite (the primary ore of aluminum) was analyzed for aluminum. The sample was powderized and treated in concentrated nitric acid. The nitric acid was removed and solids were treated in hot water with added nitric acid. Insoluble solids were removed by gravity filtration. The solution was made basic by the slow addition of dilute ammonia forming the gelatinous precipitate (Al(OH), and AIĻO.x H2O). The precipitate was heated to coagulate it then filtered over filter paper. The paper and solids were placed in a porcelain crucible and the paper was ashed while the precipitate was ignited at 600°C te convet the precinitote to nure ALO The moss of ALO recOvered wos 0 2800 c The ovee

A 1.250 g sample of bauxite (the primary ore of aluminum) was analyzed for aluminum. The sample was powderized and treated in concentrated nitric acid. The nitric acid was removed and solids were treated in hot water with added nitric acid. Insoluble solids were removed by gravity filtration. The solution was made basic by the slow addition of dilute ammonia forming the gelatinous precipitate (Al(OH), and AIĻO.x H2O). The precipitate was heated to coagulate it then filtered over filter paper. The paper and solids were placed in a porcelain crucible and the paper was ashed while the precipitate was ignited at 600°C te convet the precinitote to nure ALO The moss of ALO recOvered wos 0 2800 c The ovee

EBK A SMALL SCALE APPROACH TO ORGANIC L

4th Edition

ISBN:9781305446021

Author:Lampman

Publisher:Lampman

Chapter13: Isolation Of Eugenol From Clov

Section: Chapter Questions

Problem 9Q

See similar textbooks

Similar questions

A 25.00mL wastewater sample was analyzed for its Mg2+ content using a standard gravimetric method. the sample was diluted to 3.00L and an 11.00mL aliquot was treated to precipitate magnesium as MgNH4PO4.6H2O using (NH4)2HPO4 as the precipitating agent. the precipitate was then filtered, washed, dried, and ignited resulting in a 0.1325mg Mg2P2O7 residue. How much Mg (in ppm) is present in the original sample
A pipet is used to transfer 5.00 mL of a 1.25 M stock solution in flask “S” to a 25.00-mL volumetric flask “A,” which is then diluted with DI H2O to the calibration mark. The solution is thoroughly mixed. Next, 2.00 mL of the solution in volumetric flask “A” is transferred by pipet to a 50.00-mL volumetric flask “B” and then diluted with DI H2O to the calibration mark. Calculate the molarity of the solution in volumetric flask “B.”
A concentration of toxic metals in plant tissue is often found by combusting the material in a furnace and then dissolving the ash in concentrated acid. A 0.5124-gram sample of leaves was combusted to ash and transferred to a 150-mL beaker. A 25-mL portion of concentrated HCl was added and the mixture was heated on a hot plate. Three 5-mL portions of concentration HCl were added over approximately 10 minutes with continued heating in between additions. The resulting mixture was cooled to room temperature and filtered into a 50-mL volumetric flask, which was brought to volume using distilled water and mixed well. From this stock solution, a 10-mL portion was pipetted into a clean 50-mL volumetric flask, brought to volume with distilled water, and mixed. This final solution was analyzed and found to contain 12.1 ppm lead. What are the mass percent of lead in the original plant tissue?
A pipet is used to transfer 6.00 mLmL of a 3.75 MM stock solution in flask “S” to a 25.00-mL volumetric flask “A,” which is then diluted with DI H2OH2O to the calibration mark. The solution is thoroughly mixed. Next, 10.00 mLmL of the solution in volumetric flask “A” is transferred by pipet to a 50.00-mL volumetric flask “B” and then diluted with DI H2OH2O to the calibration mark. Calculate the molarity of the solution in volumetric flask “B.”
An sample of eggshell that weighs 1.0014g and is 51μm thick is titrated with disodium EDTA. A solution of the 1.0014g sample and 30 mL of HCl is vacuum filtered after being mixed. The product of the filtration is added to a 250mL volumetric flask and is diluted by being filled to the 250 mL mark with deionized water. 10 mL of this diluted mixture is mixed with EBT indicator and titrated with 0.05 M disodium EDTA. It takes 12.3 mL of disodium EDTA to notice a change in color. What percent mass of calcium is in the eggshell?
To each digestion flask 200 mL aliquots of 10 different drinking water samples were added. Silver was extracted by a co-precipitation procedure and collected by filtration. The precipitate was digested in 200 μl hot concentrated nitric acid and diluted to 5 mL in a dilute phosphate solution. Standards were prepared according to the following table. The samples were analyzed by graphite furnace AAS. Calculate the concentration of silver in each sample. Are there any problems? How will you address each of the identified problems?
A scientist was tasked to extract Fe from an aqueous suspension that contains 106 g of Fe2O3. The following steps detail the transformation of Fe2O3 (aq) to elemental iron: I. Enough sulfur trioxide gas was bubbled to Fe2O3 aqueous suspension to completely yield ferric sulfate. II. Then, 5.00 M nitric acid was added to ferric sulfate yielding an aqueous solution of ferric nitrate. III. Excess magnesium powder was added to the aqueous solution of ferric nitrate precipitating the solid iron ----- a. Write the balanced chemical reaction and the type of chemical reaction for [I], [II], [III]. Do not forget to indicate the states of the reactants and products (s, l, g).(CHOICES: COMBINATION, SINGLE DISPLACEMENT, DOUBLE DISPLACEMENT) b. What is the final mass of iron? Express final answers in 3 significant figures. c. High-concentration HCl is supposed to be added at the last part of the procedure. Briefly state its purpose.
An impure sample of calcium carbonate with a mass of 7.95 g was reacted with 50.00 cm3 of 1.00 mol dm hydrochloric acid (an excess). The resulling solution was transferred to a volumetric flask and titrated with 11.10cm3 of 0.300 mol dm-3 sodium hydroxide solution. Determine the percentage purity by mass of the calcium carbonate sample.CaCO3 + HCl -> CaCl2 + H2O + CO2 HCl + NaOH -> NaCl +H2O a. Determine how many moles of hydrochloric acid were used.b. Determine how many moles of excess HCI was titratedc. Determine how much in moles calcium carbonate present in the sample.d. Calculate the mass of calcium carbonate presente. Determine the percentwge calcium carbonate is in the sample.
An impure sample of Na3PO3 weighing 0.1392 g was dissolved in 25 mL of water. A solution containing 50 mL of 3% w/v mercury(II) chloride, 20 mL of 10% w/v sodium acetate, and 5 mL of glacial acetic acid was then prepared. The solution containing the phosphite was added dropwise to the second solution, oxidizing PO3^3– to PO4^3– and precipitating Hg2Cl2. After digesting, filtering, and rinsing, the precipitated Hg2Cl2 was found to weigh 0.4320 g. Report the purity of the original sample as %w/w Na3PO3. Moles Na3PO3 = moles Hg2Cl2
Method of separation/chemical reaction (with the brief process) of 3 KG's OF SODIUM BORATE AND 1.5 KG's HYDROCHLORIC ACID
A 1.1324 g sample of magnetite ore was dissolved in concentrated HCl to give a solution that contained a mixture of Fe2+ and Fe3+. Nitric acid was added and the solution was boiled for a few minutes, which converted all of the iron to Fe3+. The Fe3+ was then precipitated as Fe2O3*xH2O by addition of NH3. After filtration and washing, the residue was ignited at a high temp to give 0.5394 g of pure Fe2O3. What is the percent Fe and the percent Fe3O4 in the sample?
The % purity of a powdered crude sample of Na^2CO^3 containing only inert impurities is to be determined by reacting 225.0 mg of the crude sample to 10.0 mL of 3.00 M HCl solution, and bubbling the resulting CO2(g) product in water that is at exactly 29 °C. After the reaction has completed, the level of the liquid inside the eudiometer rests 4.30 cm above the water level in the beaker. The graduation on the eudiometer indicates that the trapped gas is 44.37 mL. The experiment was done under a barometric pressure of 755.2 torr. Write the balanced chemical equation of the reaction in your solutions sheet. What is the sum of all the coefficients of the balanced chemical equation? Determine the pressure of the trapped gas inside the eudiometer in mmHg. Determine the partial pressure of the collected CO^2 in mm Hg. How many millimoles of CO^2 was collected? What is the % purity of the sample to the nearest whole number?