A baby’s spoon with an area of 6.25 cm2is plated with silver from AgNO3 using a current of 2.00 A for two hours and 25 minutes. (a) how many grams of silver are plated? (b) What is the thickness of the silver plate formed (d = 10.5 g/cm3)?

Q: What is the electrical current, in Amperes, that must be applied if 6.50 g Ag is deposited at the…

A:

Q: How many seconds are required to deposit 0.189 grams of manganese metal from a solution that…

A: Hey, since there are multiple questions posted, we will answer first question. If you want any…

Q: How long will it take to plate out 3.9 g Ni from aqueous Ni2+ with a current of 108.2 A? HOW DO WE…

A: To plate Ni using the process of electrolysis, the reaction that needs to be employed on the…

Q: During a period of discharge of a lead–acid battery, 402 gof Pb from the anode is converted into…

A: Overall cell reaction is Pb(s) + PbO2(s) + 2H+ (aq) + 2HSO4- → 2 PbSO4 + 2H2O Where, 1 mol of Pb is…

Q: How long will it take for a uniform current of 6.00 A to deposit 78.0 g gold (197.0 g/mol) from a…

A:

Q: What volumes of H2(g) and O2(g) at STP are produced from the electrolysis of water by a current of…

A: Amount of charge (Q) = I . t  where I = current and t = time

Q: Let’s say that you want to plate gold metal on the outside of some heart pendants (to give to all of…

A:

Q: How many grams of chromium metal are plated out when a constant current of 8.00 A is passed through…

A: Faraday's Law: It can be defined as by saying that the amount of substance produced at each…

Q: How long would it take to electroplate all the Zn^ 2+ in 0.280 L of .210 M ZnSO 4 solution with a…

A: The question is based on the concept of electrochemistry. It involves  application of first law of…

Q: How many grams of magnesium metal will be deposited from a solution that contains Mg2+ ions if a…

A:

Q: The passage of a current of 0.750 A for 25.0min deposited 0.369 g of copper from a CuSO4 solution.…

A:

Q: How many seconds are required to deposit 0.268 grams of iron metal from a solution that contains…

A: Given  Mass deposited (m) = 0.268 g Current (i) = 1.22 A Time (t) = ? S The equation is Fe2+ + 2e-…

Q: A current of 11.8 A is applied to 1.25 L of a solution of 0.549 mol L- aqueous HBr converting some…

A:

Q: Copper is electroplated from CuSO4 solution. A constant current of 4.28 A is applied by an external…

A:

Q: What mass of zinc (in grams) is deposited at the cathode when a current of 9.8 amperes passes…

A: According to the electrochemistry Mass of substance deposited,  W = ZCt Where,   t = time in second…

Q: How many seconds are required to produce 8.00g of aluminum metal from the electrolysis of molten…

A: Assume that the required seconds as x. 1 A = 1 C/s. Coulombs generated by 12.0 A in x seconds is 12…

Q: Manganese metal can be produced industrially by electrolysis of MnO2. How many hours would it take…

A: The compound of manganese electrolysed is MnO2 having Mn4+ ion. Hence the electrolysis reaction to…

Q: What mass of chromium could be deposited by electrolysis of an aqueous solution of Cr2(SO4)3 for 143…

A:

Q: A constant current of 0.445 A is passed through an electrolytic cell containing molten BaCl2 for…

A: The reaction is, Ba2+ + 2e- ---> Ba(s) From this reaction, we can conclude that 2 mol of…

Q: 9. A concentrated Pb(NO3)2 (aq) solution is electrolyzed using a current of 10.5 A. a) What mass of…

A: SOLUTION: Step 1: Hello. Since the question contain multiple sub-parts, the first three subparts are…

Q: A lead storage battery delivers a current of 6 A for one hour and 22 minutes at a voltage of 12 V.…

A: The electrical energy which is generated in the lead storage battery will be equivalent to the…

Q: A current of 5.83 A is passed through a Fe(NO3)2 solution for 1.60 h. How much iron is plated out of…

A: According to Faraday's law of electrolysis, the amount of substance deposited on an electrode is…

Q: Brass, an alloy of copper and zinc, can be produced by si-multaneously electroplating the two metals…

A:

Q: A solution containing a 3+ metal ion is electrolyzed by a current of 5.0 A for 10 minutes. What is…

A:

Q: 2+ A current of 3.40 A is passed through a solution containing Cu²+ (aq) for 30.0 minutes, with…

A:

Q: Molten CaCl, can be electrolyzed to form metallic Ca. For what duration should an electrolysis be…

A:

Q: 3. The passage of a current of 0.750 A for 25.0 min deposited 0.369 g of copper from a Cuso,…

A: The Faraday's laws are the main concepts of electrochemistry.  The first law shows  the connection…

Q: How long will it take to plate 2.5 g of copper onto a light fixture using a solution of Cu(NO3)2 and…

A:

Q: What mass of copper could be deposited from a copper(II) sulfate solution using a current of0.50 A…

A: The given problem can be solved by using the formula as; Q=I×t…

Q: Gold can be plated out of a solution containing Au3+ according to the following half-reaction: Au 3+…

A:

Q: = +0.851Vwhat is the spontaneous reaction between these two half-cells and what is the poten

A: For Spontaneous reaction, E°cell is positive.  Electrode with higher standard reduction potential…

Q: One of the half-reactions for the electrolysis of water is: 2H2O (l) -----> O2 (g) + 4H+ (aq) + 4e-…

A: According to the ideal gas equation, PV=nRT where P, V, n, R and T are the pressure, volume, number…

Q: How long will it take to plate out 0.270 g of iron metal from a solution containing Fe3+(aq) in an…

A: Electrochemistry is branch of chemistry in which we deal with oxidation and reduction reaction…

Q: A current of 3.27 A is passed through a Pb(NO3)2 solution. How long, in hours, would this current…

A:

Q: How many hours are required to plate 12.00 g of nickel metal from 1.00 M NİSO4(aq), using a current…

A:

Q: How many minutes would it take to plate 12g of silver from an aqueous Ag(l) solution using a current…

A:

Q: How long would it take to deposit 2.72 g of copper from an aqueous solution of copper II sulfate by…

A: Given that : Mass of copper to be deposited (w) = 2.72 g Current (i) = 2 amps

Q: An aqueous solution of an unknown salt of ruthenium Is electrolyzed by a current of 2.70A passion…

A: Given data contains, Current I = 2.70 A time t =20.0×60 s = 1200 s Mass of Ru deposited = 1.132 g…

Q: Over a period of time, the concentration of sulfuric acid in the lead storage battery of an…

A: Given data,Initial % by mass of H2SO4=38.0 %Final % by mass of H2SO4=26.0%Volume of H2SO4=734…

Q: What period of time (in hours) is required to produce 1.00mol of chlorine using a current of 5.00A?

A: A numerical problem based on Faraday's law, which is to be accomplished.

Q: In an electrolytic cell, how many grams of nickel (MM = 58.69 g/mol) will be deposited on a metal…

A: we have to calculate the mass of Ni deposited

Q: A solution of CuSO4 is electrolysis for 10 minutes with a current of 1.5 amperes. What is the mass…

A:

Q: A pure organic acid sample (0.1516 g) is neutralized with OH- ions produced in a constant current of…

A:

Q: (a) In the electrolysis of aqueous NaNO2, how many liters of O2(g) (at STP) are generated by a…

A: Interpretation -  In the electrolysis of aqueous NaNO2, how many liters of O2(g) (at STP) are…

Q: If a constant current of 7.3 amperes is passed through a cell containing Cu²+ for 1.5 hours, how…

A:

Q: what mass, in g, of copper will be deposited from a solution of Cu^2+ by a current of 2.43 A in 7.52…

A:

Q: The passage of a current of 0.750 A for 25.0 min deposited 0.369 g of copper from a CuSO, solution.…

A:

Q: A current of 5.26 A is passed through a 2Sn(NO3)2 solution. How long, in hours, would this current…

A: In Sn(NO3)2 we have Sn in Sn2+ form  Hence to get tin that is Sn from Sn2+ the reaction will be Sn2+…

Electrolysis

Electrolysis is defined as the process of breaking down ionic compounds into their constituent elements by passing a direct electric current through the compound in a fluid state. The cathode reduces cations, while the anode oxidizes anions. An electrolyte, electrodes, and some form of external power source are the main components required for conducting electrolysis. A partition, such as an ion-exchange membrane or a salt bridge, may also be used, but this is optional. These are primarily used to prevent the products from diffusing near the opposing electrode.