A carbon steel contains 87.3 % of ferrite room temperature. Calculate the carbon content of the steel and choose the correct answer below. O 2.11% C O 1.15% C O 5.65 % C O 0.85 % C

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Consider 2.4 kg of a 99.7 wt% Fe-0.3 wt% C alloy that is cooled to a temperature just below the…

Q: What are the units of temperature and time for whichthe typical Larson-Miller parameter is equal to…

A: General application of Larsen-Miller parameter to forecast the life cycle of a tool or tool material…

Q: For a 99.64 wt% Fe-0.36 wt% C steel at a temperature right below the eutectoid, a) the phase…

A: The weight % of carbon, The weight % of carbon at the eutectoid point, The weight % of ferrite,…

Q: Maximum solubility in FCC austenite at 1147 °C is 2.04 wt% 2.14 wt% 14.2 wt% O 0.022 wt% O

A: Maximum solubility in FCC austenite at 1147 °C will be ,

Q: The alloy containing 70% Ni and 30% Cu by weight is heated slowly from 1300 C. a) At what…

A: Shown below is the Cu-Ni phase diagram and a vertical line constructed at a composition of 70 wt%…

Q: 5. Given a Cu-Ag alloy with a bulk composition of 40wt% Ag, how much eutectic (the a+ß structure…

A: Given: The composition of the alloy, Co = 40wt% Ag or 60wt%Cu The temperature range of cooling =…

Q: 2: Consider a Cu-80wt% Ni-20% alloy, determine the following: (a) The liquidus and solidus…

A: (a) Liquidus temperature ar 'a' →Tl Tl = 1250 oC Solidus temperature at 'b' →Ts Ts = 1150 oC (b)…

Q: A piece of titanium metal with a mass of 20.8 g is heated in boiling water to 99.5°C and then…

Q: By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- The microstructure of…

A: Given, The iron-carbon phase diagram is given below,

Q: Using the lever rule, calculate the amount of ferrite in a 0.42% C steel at 727 degrees celcius.

A: given data- amount of carbon = 0.42 % at 727 deg C to determine- amount of ferrite

Q: Answer the following questions: 1. An alloy of Fe in y-Fe (FCC) with a uniform Fe concentration of…

A: GivenFe concentrationFeo=0.41wt%CFe concentration is suddenly brought to Fec=1.5wt%C

Q: What are the different types of alloys? Explain their differences. Give one example of each type.

A: ALLOY is a metal made by combining two or more metallic elements, especially to give greater…

Q: The maximum solubility of C in Fe, when a steel is formed, is 2% by weight A) True B) false

A: Steel is an alloy of carbon and iron.

Q: (Q.3) For 30 wt% Cu-70 wt% Ag alloy at 650 "C, (a) what phases are present? (b) What are the…

Q: T (°C) T3 A 10 20 30 40 50 60 85 90 95 100 B →%B

A: In this system, the solid has the same structure for all compositions. Also, when two elements of…

Q: At room temperature, the steel contains 18% cementite and 82% ferrite. Calculate the amount of…

Q: Heating 0.50% C steel to 815 OC with sufficient holding time will lead to all of the carbon atoms…

A: Solution:

Q: What is the atomic % of carbon in a hypo-eutectoid steel of 0.4 wt% carbon?

Q: Which is the iron ore whose chemical component is FeCO3 and whose iron content is 48,2%? A)…

A: Solution:

Q: A certain tool steel consists of the following chemical composition (typical analysis in %): Element…

A: 1.1: Most important properties of Tool Steel: (i) Wear Resistant: Tool material must be highly wear…

Q: Rank the following four iron-carbon alloys from the hardest to the softest. Fe;C- Fe;C- Fe,C- Fe,C…

A: Given : The different iron carbon alloys.

Q: Based on the 2.0 kg of austenite including 0.60 wt% C, cooled to below 727°C. How many kilograms…

A: Since 0.60 wt% C is less than 0.76 wt% C, the ferrite will be in the proeutectoid phase. Referring…

Q: The form of pure iron at room temperature called: O Ferrite with a BCC crystal structure O 8-ferrite…

A: The iron below 910°C has BCC crystal structure. The structure of iron from iron-carbon equilibrium…

Q: 99.6 wt% Fe-0.40 wt% C steel at a temperature just below the eutectoid, determine the following. a)…

A: Given data: Material=99.6 wt% Fe-0.4 wt%C steel Need to determine the composition of Fe3C, ferrite α…

Q: The Molybdenum content in Molybdenum - Steel (4430) according to SAE/AISI classification system is O…

A: The Molybdenum content in Molybdenum - Steel (4430) according to SAE/AISI classification system is..…

Q: Name the phases present and calculate the amounts of these phases just above the eutectoid…

A: Name the phases present

Q: How would I... Determine the composition of aluminum and silicon (%Al/%Si) to melt the Al-Si…

A: what you are looking for is the eutectic point in a eutectic reaction a liquid phase transforms into…

Q: Refer to the Fe-C Diagram below to answer the following questions T( C) 1600 8. L 1400 (Fe-C y +L…

Q: Give the temperature range over which it is possible to austenitize each of the following Fe-C…

A: Given Iron carbon steel in austenitize To find Temperature range

Q: Prove that more than 8% volume change took place when ferritic iron changes its structure to…

A: For solution refer below images.

Q: Determine the specific strength of the strongest Al, Mg, Cu, Ti, and Ni alloys.Use the densities of…

A: Specific strength of any material states that the ratio of yield strength of material to the density…

Q: 1- Edeg dislocations and screw dislocations. 2- Eutectic reaction and Eutectoid reaction. 3-Ferritic…

Q: How many kilograms of nickel must be added to 5.66 kg of copper to yield a liquidus temperature of…

Q: Engineering Material Lecture: The microstructure of a steel consists of 100% coarse perlite.…

A: Given:' The microstructure of a steel consists of 100% coarse perlite. According to this…

Q: Consider de-oxidation by the addition of ferromanganese (60 percent Mn) to molten steel at…

A: When the steel is partially deoxidized with magnese,then the iron also participates in the reactions…

Q: For a 99.0 wt% Fe- 1.0 wt% C steel at a temperature just below the eutectoid, answer Question 27 -…

A: According to the guidelines of our company, we are supposed to answer only first 3 sub-parts. Kindly…

Q: Calculate the amounts of solid phases of ferrite and cementite present in pearlite. + Fe;C a + Fe;C…

A: Pearlite forms at 0.76% carbon so we need to draw line and solve the question

Q: Determine the quenching and normalizing process temperatures of 2 different steels containing 0.6% C…

A: Temperature at AC3 and ACM of Quenching and Normalizing

Q: Inside pearlite structure, the ratio between the thickness of O-ferrite layer to the thickness of…

A: Inside pearlite structure, the ratio between the thickness of -ferrite layer to the thickness of the…

Q: It has been determined that the microstructure of a steel consists of 80% pearlite and 20% ferrite.…

A: microstructure contains 20% ferrite and 80% pearlite. find the concentration of carbon, C =?

Q: For a 9 wt % Fe-l wt% C steel at a temperature 1600 1538"C Composition (ark C) 10 15 20 25 just…

A: A) Iron, ferrite => (C<0.008wt%) Stainless steel, α+Fe3C => (0.008 - 2.14wt%) B)…

Q: By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- The microstructure of…

A: Solution is attached below:

Q: Which of the following alloys would form a complete substitutional solid solution? O Metal 1 is HCP,…

A: For substitutional solid solution, Home-Ruthery rules are given as follows- 1. The atomic radius of…

Q: answer choices 327 °C

A: From above digram it is clear that Sn is 100 ℅ ar the right corner. So from graph value of melting…

Q: During thermal tempering, a glass piece is heated to a temperature: A = Above the glass transition…

A: We know that, During thermal tempering, a glass piece is heated to the a temperature above…

Q: Some of the metals possess a body-centered crystal structure. Which of the following statements is…

A: Its answer is d. It has packing efficiency(74%) greater than SSC(52%) and BCC(68%).

Q: 5. The table below lists the yield strength, tensile strength, and ductility of pure copper and of a…

A: Consider first the properties of brass. Calculate the percentage increase in the yield strength of…

Q: Calculate the number of vacancies/cm³ are expected in copper at 831 °C. The energy for vacancy…

Concept explainers

The Space Lattice and Unit Cells

Every matter consists of atoms, molecules, and ions. If these atoms, molecules, and ions (micro-particles) are represented in a three-dimensional space-occupying certain specific points in space, then these arrangements are termed as space lattices and the specific points which are being occupied by atoms, molecules and ions are termed as lattice points. The atoms, molecules, and ions at the lattice points are generally grouped in a regular fashion and repeat periodically at the three-dimensional space.

Question

A carbon steel contains 87.3 % of ferrite room temperature. Calculate the carbon content of the steel and choose the correct answer below.
O 2.11% C
O 1.15%C
O 5.65 % C
O 0.85 % C

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Principal Metallic Crystal Structures and Crystal Structure Analysis

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

(0.4 + () × (-1)**) wt% C alloy at a temperature just below the eutectoid, 100 For a determine the fraction of eutectoid ferrite x* = 10 Temperature (°C) 1600 1400 1200 1000 600 1538 C 800 a 400 S 0 (Fe) 912°C -1493 C 1394°C 7. Austenite 0.76 0.022 , Ferrite 2.14 Composition (at%C) 15 10 1147 C a+FeyC L 4.30 y+FejC 4 Composition (wt% C) 727°C 20 Cementite (FeyC) 6 2500 2000 1500 1000 6.70 Temperature (F
At room temperature, the steel contains 18% cementite and 82% ferrite. Calculate the amount of carbon in the steel and determine whether it is hypo-eutectoid or hyper-eutectoid.
Determine the modulus of resilience for each of the following alloys using modulus of elasticity given in the below table
A 200g hypoeutectoid plain carbon steel contains 5.1wt% eutectoid ferrite. 1) What is its average carbon content in weight? 2) What is the weight of total ferrite? 1600 8+7 Liquid 1400 L+ Fe;C L+y 1200 1148°C y austenite 1000 2.0 4.3 y + Fe,C 800 e 723°C 600 0.8 0.02 400 a + Fe,C Fe;C 200 0% C 100% Fe 6 6.67 Fe,C 3 4 Weight percent carbon Temperature ("C)
Q3: Analyze the following figure and answer the following question (Fe-C Diagram) ? 1639 Liquid 1400 +y 7+L L-Fec 1146 C Fe.C- 910 7- Fesc 727 C o.025 a- Fesc 6.67 of Hypo ectd- Hyper ectd 0810 Steel Cast Iron I- What are the % solubility and temperature of exist of a-ferrite? b- 0.025% and 273°c to 910 c. d- 0.05% and 910°c to 1124°c. a-0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. 2- What are the % solubility and temperature of exist of Austenite (Y)? a- 0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. b- 0.025% and 273°c to 910°c. d- 0.09% and 1394°c to 1539°c. 3- What are the % solubility and temperature of exist of 8-ferrite? a- 0.05% and 273°c to 910°c. b-0.025% and 273 e to 910°e. c- 2.1% and 910°c to 1394°c. d- 0.09% and 1394°c to 1539°c. 4- What is the % C content in Cementite Fe3C? AB a- 6.67%. b- 0.025%. c- 2.1%. d- 0.09%. (aradu
1. What temperature does a Fe-C metal with less than 4 weight percent C melt at? 2. What temperature does a Fe-C metal with less than two weight percent C melt at? 3. What climate causes delta-Fe to change into gamma-Fe? 4. What percentage of proeutectoid Fe 3C is present in a steel with 1.15 wt% carbon at 727.1 o C?
Based on the 2.0 kg of austenite including 0.60 wt% C, cooled to below 727°C. How many kilograms each of total ferrite forms? Composition (at% C) 5. 10 1600 1538 C 15 20 25 1493°C L. 1400 2500 1394°C y+L 1200 1175°C 1145°C 1147°C 2.14 4.30 7. Austenite 2000 1000 912 C y+ FegC 1500 800 727°C 700°C 0.76 0.022 600 a+ Fe;C a, Ferrite Cementite (FegC). 1000 6. 6.70 400 0. 1. 2. 3 4 Composition (wt% C) (Fe) Temperature (°C) Temperature (°F)
Analyze the development of microstructure in Iron-Carbon alloys.
What kinds of dispersion hardened alloys can retain their strength up to 1000 ° C?
The engineering yield strength of an alloy is 80 ksi.
The microstructure of eutectic alloys is always heterogeneous.true or false.
1. Using the lever rule, calculate the amount of ferrite in a 0.42% C steel at 727 degrees celcius.