By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- The microstructure of Cast iron with 3% C. 2- The Liquid and Austinite percent with chemical composition for cast iron with 2% C at 1300°C 3- Find the melting point and microstructure of steel with 0.83% C 4- Define the temperature range for Acm temperature. 5- Find the Ac3, Acl temperature and microstructure of steel with 0.4% C 6- Find the Eutectic , Eutectoid temperature and microstructure of cast iron with 4.3% C

By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- The microstructure of Cast iron with 3% C. 2- The Liquid and Austinite percent with chemical composition for cast iron with 2% C at 1300°C 3- Find the melting point and microstructure of steel with 0.83% C 4- Define the temperature range for Acm temperature. 5- Find the Ac3, Acl temperature and microstructure of steel with 0.4% C 6- Find the Eutectic , Eutectoid temperature and microstructure of cast iron with 4.3% C

Precision Machining Technology (MindTap Course List)

2nd Edition

ISBN:9781285444543

Author:Peter J. Hoffman, Eric S. Hopewell, Brian Janes

Publisher:Peter J. Hoffman, Eric S. Hopewell, Brian Janes

Chapter2: Measurement, Materials, And Safety

Section2.7: Heat Treatment Of Metals

Problem 2RQ: Direct hardening can be performed on steel containing at least________ carbon.

See similar textbooks

Similar questions

For the preceding problem, use the inverse lever rule to determine the proportions of liquid and solid phases present in the alloy.
Referring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325C
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite
Given a blank phase diagram, label the solid, liquid, and gas phases for a pure substance. Give the approximate temp. and pressure of the triple point, and determine what the substance's phase would be at a given temperature and pressure. Can you provide an example?
Using the TTT diagram for eutectoid steel, draw the specified cooling path on the diagram. Indicate what phases you expect in the final product with percentage of each phase. Assume the material has been fully austenitized before cooling. a. Water cool to room temperature b. Hot quench in molten salt to 690°C and then cooled isothermally for 2 hours: c. Hot quench to 610°C hold 3 minutes and water quench
1. Given the time-temperature transformation diagram, what would be the phases present for a 1.13 wt. % C steel with no alloying elements. calculate the amount of pro eutectoid product, where applicable (at the bottom) A.) quenched in cold water to 380 C in 0.1 seconds, then held at 380 C for 30 seconds, then quenched to room temperature B.) cooled in air at 2 C/minute to 600oC, then quenched to room temperature C. quenched in cold water to 550 C in 0.1 seconds, then held at 550 C for 2 seconds, then quenched to room temperature D. Necessary Steel Phase Diagram Calculations to determine the amount of pro eutectoid product:
The following questions are based on a high carbon steel with a composition of 1,5% C and 98,5% Fe. Please refer to the Fe-Fe3C binary phase diagram in Callister and Rethwhich 1) a Name the phases present and calculate the amounts of these phases just above the eutectoid temperature b, Give the amount of austenite present at 1100°C. c. Give the amount of pro-eutectoid ferrite just above the eutectoid temperature. d. With equilibrium cooling just below the eutectoid temperature calculate the total ferrite. e. Why must the samples be quenched rapidly to obtain high hardness?
What is the chemical composition upper limit of carbon for steel?A) 5%B) 0.022%C) 2.11%D) 4.3%E) 0.8% 2- Is it in liquid or semi-liquid state consisting of data and solidifies in a vacuum?A) tattooB) machiningC) pre-cookingD) castingE) turning 4- Which element has the lowest density and lowest atomic weight?A) magnesiumB) hydrogenC) heliumD) aluminumE) argon
11.15) Make a copy of the isothermal transforma- tion diagram for an iron-carbon alloy of eutectoid composition (Figure 11.14) and then sketch and label on this diagram time- temperature paths to produce the following microstructures: (a) 100% coarse pearlite. (b) 100% tempered martensite. (c) 50% coarse pearlite, 25% bainite, and pearl- 25% martensite.
Using the TTT diagram, explain how you can get the following: (explain by mentioning detailed heat treatment by showing each heat treatment alone in order shown)1. Fine pearlite2. Coarse pearlite3. Martensite
Choose the corect answer -A vertical line in the phase diagram represents a.an intermetallic compound b.a eutectic phase c.a eutectoid phase Match each statement with a letter -In the peritectoid reaction -In the Peritectic reaction: -In the Monotectic reaction: -In the Eutectoid reaction: -In the Eutectic reaction: a. a liquid phase transforms into two solids when it is cooled down b. a solid phase transforms into two different solids when it is cooled down c. a liquid phase transforms into a new liquid phase and a solid phase d. Two solid phases transform into a new single solid phase e. A solid phase and a liquid phase transforms into a solid phase