A combined section of steel and copper is subjected to a compressive load. Refer to the table below for the properties of each Steel Copper Area, A 900 mm2 1,200 mm2 Modulus of elasticity, E 200 GPa 120 GPa Allowable compressive stress 140 MPa 70 MPa Which of the following most nearly gives the load, in percent, carried by the copper? Select the correct response: 44.44% 55.56% O66.67% 33.33%

A combined section of steel and copper is subjected to a compressive load. Refer to the table below for the properties of each Steel Copper Area, A 900 mm2 1,200 mm2 Modulus of elasticity, E 200 GPa 120 GPa Allowable compressive stress 140 MPa 70 MPa Which of the following most nearly gives the load, in percent, carried by the copper? Select the correct response: 44.44% 55.56% O66.67% 33.33%

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.3P: A tensile test was performed on a metal specimen having a circular cross section with a diameter 0....

See similar textbooks

Similar questions

A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
1. Titanium alloy with an elastic modulus of 107 GPa (15.5 x 106 psi) and an initial diameter of 3.8 mm (0.15 in. ), only elastic deformation occurs. If the maximum permissible elongation is 0.42 mm, find the specimen's maximum length before deformation (0.0165 in.) 2.) With a load of 89,000 N (20,000 lbf), a steel bar 100 mm (4.0 in.) long with a square cross section 20 mm (0.8 in.) on one edge is pulled in tension and undergoes an elongation of 0.10 mm (4.0 103 in.). Calculate the steel's elastic modulus, assuming the deformation is fully elastic. Please indicate the given sir. Thanks alot…
A steel rod of 30 mm diameter is inserted in a copper tube of external diameter 45 mm and an internal diameter of 37 mm carries a load of W =1750kN. The length of this compound bar is 180 mm. If, ES= 2 × 105 N/mm2and ECu= 1 × 105 N/mm2, calculate the stresses developed in copper and steel.
A rectangular steel bar 0.5 inch thickness by 1.5 inches width and 220 ft long is subjectedto a 6000 lbs tensile load acting along its width. Find the deformation along its length andthickness if poison’s ratio is 0.27.
An aluminum tube is fastened between a steel rod and a bronze rod as shown. Axial loads are applied at the positions indicated. For Bronze: Allowable stress = 120 MPa, EB = 83,000 MPa For Aluminum: Allowable stress = 120 Mpa, EA = 70,000 MPa For Steel: Allowable stress = 120 MPa, Es = 200,000 MPa Assume that the assembly is suitably braced to prevent buckling. Maximum overall deformation should not exceed 2mm. a) Give the value of the force acting on the bronze so as not to exceed allowable stresses and deformation. b) Give the value of the force acting on the aluminum so as not to exceed its allowable stresses and deformation. c) Give the value of the force acting on the steel so as not to exceed its allowable stresses and deformation.
A compound bar is subjected to a compressive force of P=556 kN by means of a rigid endplate at the top. If the length of the bar is 876mm, determine the stress in the alurninum core. Answer in MPa. Round off your final answer to 2 decimal places. 25 mm Brass core E = 105 GPa a = 20.9 x 10-6/°C Aluminum shell E = 70 GPa Q = 23.6 x 10-6/°C 60 mm
Calculate the total deformation of steelbars shown in Figure. (d1=15 mm, d2=25 mm and E=210 GPa) A= 5, B=3, C=8
A circular steel rod AB (diameter d1=15 mm, length L1=1100 mm) has a bronze sleeve (outer diameter d2 21 mm, length L2=800 mm) shrunk onto it so that the two parts are securely bonded (see figure). Calculate the total elongation δ (mm) of the steel bar due to a temperature rise ΔT=200oC. (Material properties are as follows: for steel, Es=210 GPa and αs=12x10-6/C; for bronze, Eb=110 GPa and αb=20x10-6/C.)
NEED IN 1 HOUR PLS, THANK U A copper bar is of uniform cross-section and is rigidly attached to the walls as shown. The rod is 5ft long and has a cross-sectional area of 2.5 in². At a temperature of 20°F the rod is stress-free in the configuration shown. Determine the stress in the rod when the temperature has dropped to 50°F. Assume that the supports do not yield. For copper, E = 16x10⁶ lb/in² and α = 9.3 x 10^-6/°F.
A steel rod Is stretched two rigid walls and carries a tensile load of 6000 N to 20 degrees Centigrade. Coefficient of thermal expansion is 11.7 x l0^-6 /deg.C and modulus of elasticity 200000 MPa.1. Which of the following gives the minimum diameter of the rod if the allowable stress is not to exceed 140 MPa at -25°C. a. 15 mmb. 17 mmc. 16 mmd. 18 mm2. Which of the following gives the total elongation of the steel rod if it has a length of 1.5m. a. 1.00 mmb. 1.04 mmc. 1.02 mmd. 1.06 mm