A graphene sheet with thickness t= 150 nm and u= 0.185 is subjected to ananoindentation test. Based on the result shown in the figure2000 (9)150020g 1000500ExperimentFitting0420406080100Indentation depth (nm)A. Calculate the E if the indenter with square cross-section has a poison'sratio v= 0.25 and Young's Modulus E;= 100 GPa.B. Calculate the Hardness H.(NU) peon

thcikness (t) =150 nm and poison's ratio (ν) = 0.185 poison' ratio (ν)= 0.25 young's modulus (Ei )=…

A graphene sheet with thickness t= 150 nm and u= 0.185 is subjected to a nanoindentation test. Based on the result shown in the figure 2000 (9) 1500 20 1000 500 O Experiment Fitting 20 40 60 80 100 Indentation depth (nm) (Nu) peon

A graphene sheet with thickness t= 150 nm and u= 0.185 is subjected to a nanoindentation test. Based on the result shown in the figure 2000 (9) 1500 20 1000 500 O Experiment Fitting 20 40 60 80 100 Indentation depth (nm) (Nu) peon

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Assume the following elastic loading exists on ablock of copper:σX = 325 MPa; σY = 80 MPa; and τXY = 40 MPaCalculate eX and eZ for this block, assuminga. that it is a random polycrystalline material.b. that it is a single crystal with the tensile and shearaxes lining up along unit cell axes.c. Explain why the relative strain values you calculated along the X axis make sense for the two cases,based on the elastic anisotropy of copper.
What is the maximum value of KIc as per LEFM that can be determined from experiments on a 20 mm thick plate? yield strength= 500 MPa, E= 210 GPa, poission ratio=0.3.
Question 2: A GFRP product is made from: 7.0 mm long by 0.002 mm diameter aligned fibres with Ef =72.5GPa and a tensile strength of 3.5GPa, and a matrix material with Em=1.6GPa and a tensile strength of 41.4MPa. The stress in the matrix at the fibre fracture strain is 20MPa. a) If the shear strength of the fibre-matrix bond is τc=10MPa then determine the longitudinal composite strength (σ∗) when the GFRP is made with ϕf=0.4. b) Determine the stiffness of this GFRP product in the longitudinal and transverse directions. c) If it were possible to modify the design of this GFRP product, determine the volume fraction of fibre that would be needed to achieve a strength (σ∗) of 2000MPa
Two vertical wires are suspended at 450 mm apart. Their lower ends support a rigid horizontal bar that carries a load F. The left-hand wire is made of copper and has a diameter of 3 mm. The right-hand wire is made of steel and has a diameter of 2 mm. Calculate: (a) The position of F if the elongation in both wires is the same. (b) The load carried by each wire and the total elongation if F = 350 N and both wires are initially 3,5 m long. (Esteel = 200 GPa and Ecopper = 100 GPa).
3. Molybdenum has a BCC crystal structure, an atomic radius of 0.1363 nm, and an atomic weight of 95.94 g/mol. Compute its theoretical density.4. For a brass alloy, the stress at which plastic deformation begins is 345 MPa and the modulus of elasticity is 103 GPa.a. What is the maximum load that may be applied to a specimen with a cross-sectionalarea of 130 mm2 without plastic deformation?b. If the original specimen length is 76 mm, what is the maximum length to which itmay be stretched without causing plastic deformation?
For safe and reliable operation, a certain polypropylene pipe must withstand an internal pressure of 0.5 MPa for a minimum of three years. If the pipe diameter is 100 mm, what is the minimum necessary wall thickness to ensure that the pipe will not experience a strain greater than 1.3%? To solve this problem, use the accompanying graph that reveals the room temperature creep response for polypropylene.
The compressive strength of alumina quartz (Al2O3) is 2.1 GPa. A quartz tube is being used for a vacuum furnace. Both ends of the tube are constrained and cannot move. To what temperature can the tube be heated up from room temperature such that the tube won’t fracture due to the thermal stress?
A 200-mm-long polypropylene rod, with a rectangular cross-section that is 20 mm by 4 mm, is subjected to a tensile load of 300 N, directed along its length. If the rod extends by 0.5 mm after being under load for 100 s, determine the creep modulus. How does this value compare with the typical static modulus for polypropylene, and what does the comparison imply about the amount of creep that has probably taken place in 100 s?
Consider a 1 m-long bar of 2024-T81 aluminum alloy with a 20mm-diameter and the following property data: E=70 GPa Y.S = 410 MPa T.S. = 480 MPa % Elongation at failure = 8 % What is the maximum tensile load that can be permitted without producing extensive plastic deformation of the bar? Your answer should be in units of Newtons (N).
A ceramic with KIc = 4 MPa m1/2 contains pores with radius a = 5 µm due to incomplete sintering. These pores lead to a decrease in the failure stress of the material in both tension and compression. One in every ten grainboundary junctions contains a void; the grain size of the ceramic is 50 µm. The ceramic fails in compression when the length ℓ of each crack generated at the voids equals one-half of the spacing between the voids. (a) Determine the compression strength of the ceramic, using the equation from Sammis and Ashby. (b) Determine the tensile strength of the ceramic, assuming flaws with size a.
The theoretical failure strength is significantly higher than the empirical failure strength of polycrystalline materials, even when they are highly polished because: a) Polycrystalline materials have little or no capacity for plastic deformation, so they have lower failure stresses b) Plastic deformation in polycrystalline materials adsorbs energy which reduces their failure strength c)The energy needed to break the atomic bonds in crystal lattices is lower in polycrystalline materials as compared to in single crystals d)Polycrystalline materials contain internal discontinuities
The stress-strain curve of cellulose acetate at 25°C is shown below. Draw the curves at 0°C and 60°C