A steel alloy is known to contain 93.8 wt% Fe, 6.0 wt% Ni, and 0.2 wt% C. Assume that there are no alterations in the positions ofother phase boundaries with the addition of Ni.(a) What is the approximate eutectoid temperature of this alloy?i°C(b) What is the proeutectoid phase when this alloy is cooled to a temperature just below the eutectoid?(c) Compute the relative amounts of the proeutectoid phase and pearlite.WaWp :i

The change in the alloy steel with the eutectoid temperature, position of phase boundary, and…

A steel alloy is known to contain 93.8 wt% Fe, 6.0 wt% Ni, and 0.2 wt% C. Assume that there are no alterations in the positions of other phase boundaries with the addition of Ni. (a) What is the approximate eutectoid temperature of this alloy? °C (b) What is the proeutectoid phase when this alloy is cooled to a temperature just below the eutectoid? (c) Compute the relative amounts of the proeutectoid phase and pearlite.

A steel alloy is known to contain 93.8 wt% Fe, 6.0 wt% Ni, and 0.2 wt% C. Assume that there are no alterations in the positions of other phase boundaries with the addition of Ni. (a) What is the approximate eutectoid temperature of this alloy? °C (b) What is the proeutectoid phase when this alloy is cooled to a temperature just below the eutectoid? (c) Compute the relative amounts of the proeutectoid phase and pearlite.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Calculate the amounts and compositions of phases at 726oC in a Fe-0.6% C alloy cooled under equilibrium conditions. Disregard the amounts of proeutectoid phases. A. 77.3% α, 22.7% Fe3C; C in α = 6.7% and C in Fe3C = 0.02% B. 91.3% α, 8.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% C. 77.3% α, 22.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% D. 91.3% α, 8.7% Fe3C; C in α = 0.05% and C in Fe3C = 8.4% E. None of the mentioned
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: a) Is this alloy hypoeutectic or hypereutectic? b) What is the composition of the first solid to form? c) What are the amounts and compositions of each phase that is present at 183°C + ∆T ? d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
Phase Diagrams: You are given the lead tin (Pb-Sn) phase diagram. Below the eutectic isotherm is identified as the two phase region a + B. a) At 30wt % Sn, in the circles below draw the microscopic observations evolving at 3000C, 2250C, and 1000C for this hypoeutectic alloy. b) At a temperature just above the isotherm at 1830C, for the 30 wt% Sn Alloy, calculate the fractions of each phase present at equilibrium and the corresponding composition of each phase.
A lead-tin (Pb-Sn) alloy of composition 30 wt % Sn and 70 wt % Pb is slowly heated from a temperature of 140 OC. Refer to the phase diagram provided in Figure 1 and answer the following. (i) At what temperature does the first liquid phase form? (ii) What is the composition of this liquid phase? (iii) At what temperature does complete melting of the alloy occur? (iv) What is the composition of the last solid remaining prior to complete melting?
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
A 80%Sn-20%Pb alloy is melted fully at 300°C and then slowly cooled down to 182°C. Sketch the microstructures at 300°C, 200°C, and 182°C, respectively. Label all phases and indicate their approximate compositions. Also, determine the follows for this alloy at 182°C. (1) The weight fractions of α and β phases.(2) The weight fractions of primary β and eutectic structure.(3) The weight fraction of eutectic β .
Consider the binary eutectic copper-silver phase diagram shown below. Make phase analysis of a 80 wt % Ag–20 wt% Cu alloy at the temperatures (a) 900°C, and (b) 780°C-ΔT. In the phase analysis include: (I) phases present, (ii) chemical compositions of phases, (iii) mass fractions of phases, and (iv) sketch of microstructure.
Q.1.For hypoeutoctoid plain carbon steel(select %C content yourself), determine the phasesthat are present, the compositionsof these phases, and the percentages or fractionsof the phases.Make schematic sketches of the microstructurethat would be observed for conditions of very slow cooling at the following temperatures: a)Just above the austenite transformation temperature b)The austenite transformation temperature -10C c)The eutectoid transformation temperature +10C d)The eutectoid transformation temperature -10C
BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…
For a 60-40 Pb-Sn alloy, what would the percent of each phase be at 185°C and 180°C?
For a 76 wt% Pb–24 wt% Mg alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 575°C, 500°C, 450°C, and 300°C. Label all phases and indicate their approximate compositions.
Draw the iron-Fe3C phase diagram. Consider 0.4 and 1.1 wt% C steel alloy. It is cooled slowly from a temperature within austenite phase to room temperature. Show a) microstructure at 1000 °C b) microstructure at 730°C c) microstructure at 715°C and d) microstructure at room temperature e) determine the phase present, the phase compositions at 715 and 730 °C f) What do you say about mechanical properties of these alloys, depending on their microstructure at room temperature?