A tension test was conducted for a material called MatX and the following stress-strain curve was obtained. Determine the change in the diameter of the bar made of MatX under the loading shown below. Assume Poisson's ratio is 0.2. Please clearly state if the diameter contracts or elongates. Write your final answer in the textbox below. Stress SAN 200 Stress-strain values of MatX &-0.001 mm/mm G-0.010 mm/mm & -0.100 mm/mm 6- 50 MPa A- 80 MPa 20 mm AN Strain

A tension test was conducted for a material called MatX and the following stress-strain curve was obtained. Determine the change in the diameter of the bar made of MatX under the loading shown below. Assume Poisson's ratio is 0.2. Please clearly state if the diameter contracts or elongates. Write your final answer in the textbox below. Stress SAN 200 Stress-strain values of MatX &-0.001 mm/mm G-0.010 mm/mm & -0.100 mm/mm 6- 50 MPa A- 80 MPa 20 mm AN Strain

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.6P: The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular...

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 74.0 ksi, e = 104.0 ksi , g = 85.0 ksi , and h = 0.15 in/in. Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.7 in . Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 11.0 kips, find the nominal stress experienced by the rod. Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
Consider a bar with a rectangular cross-section area with a thickness of t = 0.5 in. and height of h = 3.5 in. When force P = 19 kips is applied to the bar, the strain gages attached to the surface of the bar reads εx = 740 µε along the direction of the force and εy = -170 µε in the perpendicular direction. Determine Poisson's ratio for this specimen? Determine the modulus of elasticity for this specimen?in Ksi
DURING THE STRESS-STRAIN TEST, THE UNIT DEFORMATION AT A STRESSOF 30 MPa WAS OBSERVED TO BE 110 x 10-6 mm/mm AND AT A STRESS0F 130 MPa IT WAS 520 X 10-6 mm/mm. IF THE PROPORTIONAL LIMITWAS 250 MPa, WHAT IS THE MODULUS OF ELASTICITY? WHAT IS THESTRAIN CORRESPONDING TO A STRESS OF 150 MPa?
A steel wire with a diameter of d = 1/16” is bent around a cylindrical drum with a radius ofR = 36”.(a) Determine the maximum normal strain in the wire.(b) What is the minimum acceptable radius of the drum if the maximum normal strain mustremain below yield? Consider an elastic modulus of 30000 ksi and yield stress of 100ksi.(c) If R = 36”, what is the maximum acceptable diameter of the wire if the maximum normalstrain must remain below yield?
The tensile test was conducted on a specimen with a diameter of 0.5 inch. A strain gage was bonded to the specimen so that the strain could be obtained directly. The following data were obtained. a) create a table of stress and strain values. Plot this data points and draw the best fit straight line through them. b) what is the slope of this line? What does this value represent?
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3⁄8 inch and the gage length (the length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress–strain data and draw a best-fit curve. c. Compute the modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=50mm and initial diameter of d0=13mm. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 510 MPa , e = 693 MPa , g = 565 MPa , and ℎ = 0.15 mm/mm Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 65.0 mm.
STRENGTH OF MATERIALS. Please show the complete solutions. NO LONG EXPLANATION NEEDED! Rate will be given. Answer ASAP! Please answer all. MULTIPLE CHOICE: CHOOSE THE CORRECT ANSWER 1. Using MOHR CIRCLE from the given stresses on two perpendicular planes what is the normal stress on plane a-a? a. 75 MPa b. 150 MPa c. 125 MPa d. 100 MPa
A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It is then noted that the distance between the gage marks became 50.122mm. a,) What is the modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axial stress of the specimen?Note: Please show detailed solutions with illustrations.
Bars (1) are made of a polyimide plastic that has an elastic modulus of 3.8 GPa. Bar (2) is a nylon material that has an elastic modulus of 1.9 GPa. Each bar has a cross-sectional area of 900 mm2. Using L = 395 mm and Δ = 4.6 mm, what magnitude of load P will cause the normal stress in each bar to be the same value?
A hollow cylinder with an OD of 100mm and an ID of 30mm, supports a load of 100kN. What is the compressive stress in MPa?.............I know stress=p/a , but I am not sure how to find the height in order to calculate the area or if there would be another way of doing it ?