Tests conducted to find the ultimate tensilestrength of alloy steel gave the following results63.3, 61.8, 67.4, 65.3, 59.7, 64.2, 60.9, 66.1, 62.6, 63.9.Assuming that the ultimate tensile strength followsa two-parameter Weibull distribution, plot the data,and determine the parameters of that distribution.

Answered: Assuming that the ultimate tensile…

Assuming that the ultimate tensile strength follows a two-parameter Weibull distribution, plot the data, and determine the parameters of that distribution.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: It is known that a brass alloy has a yield strength of 275 MPa, a tensile strength of 380 MPa and a…

Q: For a 10-mm-diameter Brinell hardness indenter, what will be the diameter of an indentation in mm to…

Q: One piece is made of a metal alloy with a yield limit of 180 MPa. At a certain point in the part…

Q: A metal sample on a tension in the test, , a tensile true strain 0.08, and true stress when the…

A: Given, ε1=0.08σ1=265 MPaε2=0.27σ2=325 MPa

Q: Which material is considered as ductile and which one is considered as brittle? Explain. What is the…

A: Given: To determine: which material is brittle and which one brittle material

Q: A gauge # 10 HSLA steel for an automotive application has a Young’s modulus of 200 GPa, a yield…

A: Find the punch force required

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 12 mm2…

A: Data given- F = 15 kN = 15 × 101.972 = 1529.57 kgf A = 12 mm2 BHN = ?

Q: Determine the indentation diameter of a mild steel material subjected to a Brinell hardness test…

Q: Describe the experimental process from the preparation of the metal tensile specimen to the tensile…

A: Composition is the mixture of two ingredients or elements. For different cast irons mostly silicon…

Q: Determine the indentation diameter of a mild steel material subjected to a Brinell hardness test…

A: 1. Indentation Diameter 10.48mm 2.Surface area of indentation 184.577 mm square

Q: Please elaborate the following: Typical stress-strain characteristics of steel in simple tension and…

A: Characteristics of Stress Strain Mechanical Properties

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 12 mm2…

A: Surface area of indentation (A)= 12 mm2 Applied force = 15 kN = 15000 N Applied load…

Q: For a 10-mm-diameter Brinell hardness indenter, what will be the diameter of an indentation in mm to…

A: Given data: D=10 mmHB=300 HBP=500 kg Need to determine the diameter of an indentation.

Q: 3. For steels, the endurance limit is approximately half of the tensile strength, and the fatigue…

Q: Determine Brinell Hardness Number for a specimen that has a surface area of indentation as 10 mm?…

Q: cylindrical specimen of steel having an original diameter of 0.505 in. is tensile tested to fracture…

A: Write the given information.

Q: A part made from AISI 1212 steel undergoes a 20 percent cold-work operation. (a) Obtain the yield…

A: Data given- AISI 1212 steel with 20% cold work

Q: the stress versus strain diagram, naming axes and units 2) Define modulus of elasticity and…

A: Given L0 = 35 cm = 350 mm Required 1. Stress -strain graph 2. Modulus of elasticity 3. Yield…

Q: Determine the surface area of indentation for a specimen that has Brinell hardness number as 851 and…

A: We have to find surface area

Q: For a tensile test it can be shown that the percent cold work (%CW) is related to strain according…

Q: Two previously undeformed cylindrical specimens of an alloy are to be strain hardened by reducing…

Q: 1- Discuss the relationship between the main parameters which are the torque, torsional stress,…

A: Given question Discuss the relationship between main parameters such as torque, torsional stress,…

Q: 2) a) Draw a stress-strain curve for a low carbon steel and an aluminum after tensile test. Show…

A: The stress strain curve of low carbon steel and aluminium can be drawn as below, Here, x-axis and…

Q: Calculate the Vickers hardness when a 700-g load yields an indentation diagonal length of 0.050 mm.

A: Given data: P=700 gd=0.05 mm Need to determine the Vickers hardness.

Q: During a high cycle fatigue test, a metallic specimen is subjected to cyclic loading with a mean…

A: Given:σmin=-70 MPaσmean=+140 MPa

Q: A tensile test is performed to determine the strength constant C and strain-rate sensitivity…

Q: The magnitude of the shear stress to cause yielding in a torsion test and the magnitude of the…

A: It is False

Q: Q5) material given the data from a tension test ? How would you determine the strain- hardening…

Q: Sketch the expected tensile stress versus strain curves for the following:

A: all the three curves are shown in the same stress train diagram so that comparison can be done.

Q: Is the maximum normal stress theory useful to predict the accurate failure of brittle material?

A: Yes, the maximum normal stress theory useful to predict the accurate failure of brittle material.

Q: The stress element corresponds to a point under a flat stress state, on the surface of a part made…

A: For the given stress element if yield strength (Sy) is 700 MPa To determine (a) f.o.s according…

Q: Tensile and fully reversed loading fatigue tests were conducted for a certain steel alloy and…

A: σy = 1200 MPa (tensile) σe = 550 MPa (comp) static stress = 600 MPa σtensile = 350 MPa σcomp = 350…

Q: Draw a Stress/Strain graph of a mild tensile steel and identify the limit of proportionality and the…

A: stress strain graph of a mild steel which is tensile in nature shows several strength like…

Q: A metal wire of diameter 1.2 mm is used to carry a load of 1100 N. If the material of which the wire…

Q: To manufacture a piston with a circular cross section, an alloy steel bar is required whose length…

A: Given: Length of piston bar = 35 cm Compression load = 5.2 tons = 5200 kg Factor of safety(FOS) =…

Q: Can we determine the relationship between the average normal stress and average normal strain by…

A: The relation between the average normal stress and average normal stress can be determined by…

Q: Calculate the stress of the cylindrical rod. Compare with data given in Table Q1 which are the…

A: we have to calculate the stress

Q: Describe the nature of the load and strength distributions in four practical engineering situations…

Q: Determine the tensile and yield strengths for the following materials: (a) UNS G10200 hot-rolled…

A: The tensile strength of a material is the maximum force required to break the material. or we can…

Q: Table 4 shows the fatigue data of a ductile cast iron to be used for an automobile axle that rotates…

A: a)

Q: When a 3000 kg load is applied to a 10-mm-diameter ball in a Brinell test of a steel,an indentation…

A: Given Data⇒ Load applied(F)= 3000 kgf Diameter of ball(d)=10 mm=0.01 m After indentation, change in…

Q: Describe the behavior of tested materials (mild steel and aluminium) as it responds to increasing…

A: following is the answer to the above problem-

Q: 2. A tensile test is performed on a bar of Dural (an aluminium alloy) of diameter 15 mm. The bar…

A: Given Data: Diameter of the bar, d=15 mm

Q: Describe ductile fracture and brittle one. what is the difference between them in tensile test…

A: Given: Tensile test specimen To explain: Brittle and Ductile fracture

Q: For a specimen with reported Rockwell B hardness number of RHB=93.8, the approximate value of…

A: Rockwell B hardness number=93.8

Q: For a certain metal the strength coefficient K = 600 MPa and the strain hardening exponent n = 0.20.…

A: Given The strength coefficient K = 600 MPa The strain hardening exponent n = 0.2…

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

Tests conducted to find the ultimate tensile
strength of alloy steel gave the following results
63.3, 61.8, 67.4, 65.3, 59.7, 64.2, 60.9, 66.1, 62.6, 63.9.
Assuming that the ultimate tensile strength follows
a two-parameter Weibull distribution, plot the data,
and determine the parameters of that distribution.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

(SI Units) In a tensile test on a steel specimen, true strain = 0.11 at a stress of 245 MPa. When true stress = 340 MPa, true strain = 0.31. Determine the strength coefficient and the strain-hardening exponent in the flow curve equation.
Was there a discrepancy between the values of Young's Modulus found in the tensile test and the bending test? If so, why does this occur?
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation.
A sheet of aluminium alloy is reduced in thickness by 25% following a rolling operation. Tensile test specimens were cut from the sheet before and after rolling. Sketch the tensile test curves for both specimens, making reference to the differences if any, in Young’s modulus, the elastic limit and the level of ductility
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region
Using the graphs in Figures for Q2 (b) & (c), select a metal alloy for an application that requires a tensile strength of at least 370 MPa while maintaining a minimum ductility of 27%. If the metal may be cold worked, decide which of the following is a suitable material; copper, brass or 1040 steel. You need to explain your selection process.
Draw a typical stress vs strain tensile test curve for the following material and label the axis. A typical brittle material subjected to a tensile stress that has been applied to the material till the sample breaks. 1- label the axis and draw the curve for a brittle material. 2- indicate the maximum strength of the material. 3- show on the portion of the curve where young's modulus can be calculated.
A Japanese steel manufacturer is considering expanding operations. From experience, it estimates that new capacity additions obey the law f(y) = .00345y.51,where the cost f(y) is measured in millions of dollars and y is measured in tons of steel produced. If the demand for steel is assumed to grow at the constant rate of 8,000 tons per year and future costs are discounted using a 10 percent discount rate, what is the optimal number of years between new plant openings?
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
(SI/USCS Units) In a Brinell hardness test, a 1500-kg load is pressed into a specimen using a 10-mm-diameter hardened steel ball. The resulting indentation has a diameter = 3.2 mm. (a) Determine the Brinell hardness number for the metal. (b) If the specimen is steel, estimate the tensile strength of the steel.
A metal sample on a tension in the test, , a tensile true strain 0.08, and true stress when the strain is 0.27. Determine the strength coefficient and strain hardening exponent in the flow curve equation.
Explain about these graphs and discuss how they are helpful in engineering. (TENSILE TEST)