A part made from AISI 1212 steel undergoes a 20 percent cold-work operation. (a) Obtain the yield strength and ultimate strength before and after the cold-work operation. Determine the percent increase in each strength. (b) Determine the ratios of ultimate strength to yield strength before and after the cold work operation. What does the result indicate about the change of ductility of the part?

A part made from AISI 1212 steel undergoes a 20 percent cold-work operation. (a) Obtain the yield strength and ultimate strength before and after the cold-work operation. Determine the percent increase in each strength. (b) Determine the ratios of ultimate strength to yield strength before and after the cold work operation. What does the result indicate about the change of ductility of the part?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Using various tables, determine the specific strength (yield strength-to-density ratio) in unit of kN⋅m/kg for AISI 1015 hot-rolled steel, 7075-T6 aluminum alloy, Ti-0.2 Pd titanium alloy, and ASTM No. 60 gray cast iron.
A hardness of 45 Rc is required for a plain carbon steel containing 0.6% carbon. Can you explain step by step the work to be done?
The annealed low carbon steel behavior is approximated by σ = 10000ε 0.25 MPa. Evaluate (a) The yield strength after the bar is cold worked for __%. (b) If the same annealed low carbon steel bar is initially cold worked __%, followed by additional cold work of __%, determine the probable yield strength of the final bar. (c If the same annealed low carbon steel bar was cold worked for an unknown amount and then cold worked 20% more and found to have a yield strength of __ MPa. What was the unknown amount of cold work. (d) Discuss the variation of yield stress in question a & b. (e) Discuss the effect of mechanical working on variation of properties with respect to grain size. Also draw a clear graph of properties versus grain size for ductility and strength. σ = 10000ε 0.24 (a) 30% (b) initially 15% followed by 20% (c) yield strength of 7500 MPa
An application requires ultimate tensile strength and yield strength ofa steel at 110 ksi and 91 ksi, respectively. Answer the following 4 questions: Can SAE 1040 steel be selected for this application? If “no” is the answer in Part I, the following Part II, III, and IV can beignored. If “yes” is the answer in Part I, which condition of SAE 1040 shouldbe selected? Why is that steel with the condition in part II selected? Is the selected steel brittle or ductile? and Why?
A batch of casted mild steel has a modulus of elasticity of 200 GPa and a yield strength of 250MPa. Calculate for its modulus of resilience. After cold working the steel, the yield strength increases to 310 MPa. Calculate for the percent reduction in the average grain diameter given σo =70 MPa and k = 0.74.
In the flow curve for pure aluminum, the strength coefficient = 175 MPa and strain-hardening exponent = 0.20. In a forming operation, the final true strain = 0.75. Determine a) the flow stress and b) average flow stress that the metal experienced.
A cylindrical brass rod with a minimum tensile strength of 450 MPa, a ductility of at least 13% EL (elongation), and a final diameter of 12.7mm is required. You have in your inventory some 19.0mm diameter brass stock that has been cold worked to 35%. Assuming that the cross section of the rod is still circular after being cold worked, and that brass experiences cracking at 65% CW, describe the necessary working steps in order to achieve the final product. Take the expression for % cold work to be = (Ao - Af)/ Ao x 100%, where Ao and Af are the original and final circular cross-sectional areas of the rod.
How does the carbon content in plane carbon steels affect the fracture toughness? Show this influence by A7 curves.
A material has a Yield Strength of 424.8 MPa and a UTS of 567.5 MPa. If a medium hard condition for this material is required, what would be the target Stress at which the material has to be cold work to meet this requirement?
What type of behaviour is observed from these stress-strain curves?
An application requires ultimate tensile strength and yield strength ofa steel at 110 ksi and 91 ksi, respectively. Answer the following 4 questions:4.1. Can SAE 1040 steel be selected for this application?4.2. If “no” is the answer in Part I, the following Part II, III, and IV can beignored. If “yes” is the answer in Part I, which condition of SAE 1040 shouldbe selected?4.3. Why is that steel with the condition in part II selected?4.4. Is the selected steel brittle or ductile? and Why?
A low-carbon steel alloy was loaded in tension until just after yielding took place. A few Luders bands were visible on the surface. The bar can either be reloaded (a) immediately, (b) after a brief and moderate temperature aging treatment, or (c) after several weeks without any exposure to elevated temperature. In each of the three cases, how is the yield strength of the reloaded bar likely to compare to that of the original test?