Calculate the fiber volume fraction required in a certain unidirectional E-glass fiber reinforced epoxy composite, where the fibers are expected to carry 92% of load along the fiber direction. If the modulus of elasticity and tensile strength of the glass fiber is 72.8 GPa and 3200 MPa and that for epoxy is 3.4 GPa and 86 MPa respectively, also calculate the tensile strength of the composite

Calculate the fiber volume fraction required in a certain unidirectional E-glass fiber reinforced epoxy composite, where the fibers are expected to carry 92% of load along the fiber direction. If the modulus of elasticity and tensile strength of the glass fiber is 72.8 GPa and 3200 MPa and that for epoxy is 3.4 GPa and 86 MPa respectively, also calculate the tensile strength of the composite

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Boron coated with SiC reinforced aluminum containing 40 vol.% fibers is animportant high temperature, light weight composite material. Estimate the density, modulus of elasticity, and tensile strength of composite parallel to the fiber axis. Also estimate the modulus of elasticity of composite perpendicular to the fibres.
An epoxy matrix is reinforced with 40 vol% E-glass fibers to produce a 2-cm diametercomposite that is to withstand a load of 25,000 N. Calculate the stress acting oneach fiber.
Boron coated with SiC reinforced aluminium containing 40 vol.% fibers is animportant high temperature, light weight composite material. Estimate the density,modulus of elasticity and tensile strength of composite parallel to the fiber axis. Alsoestimate the modulus of elasticity of composite perpendicular to the fibres.
A tensile load of 120N is applied to an aluminum boron composite with 1mm^2 cross sectional area.the volume of parallel fibers is 20%.what is the stress in the fibers when the load Axis is (a)parallel to the fibers (b)perpendicular to the fibers
Calculate the density of a composite made with 35% Kevlar-49 fibers in an epoxy resin (ρ = 1.1 kg/m3, E = 2.5 GPa). For Kevlar-49, Ef = 131 GPa; density = 1440 kg/m3
Question 1 A composite material consists of 40% parallel carbon fibres with a Young’s modulus of 405 GPa in a matrix of epoxy resin with a Young’s modulus of 2.5 GPa. Calculate the Young’s modulus of the composite in the parallel and in the perpendicular directions of the fibres. Use the graphical method seen in class to show the possible value of the overall young modulus of your composite material.
Glass fibres provide longitudinal reinforcement for a nylon material subject to tensile load. The fibre diameter is 20 μm and the volume fraction is 0.45. (Take Young’s modulus of glass fibres as 70 000 MPa and nylon as 2800 MPa)(i)Calculate the Young’s modulus of composite(ii)Determine the tensile strength in the glass fibre if the tensile strength of the composites and matrix is 14 MPa and 11.8 MPa, respectively
a) Determine the modulus of elasticity of the fibers. b) Estimate their modulus of toughness. c) Estimate their modulus of resilience.
The compressive strength of aramid fiber is about one-eighth of its tensile stress. Estimate the smallest diameter of a rod on which the aramid fiber can be wound without causing kinks, etc. on its compression side. How to find the diameter based on bending moment and formula, MR = EI?
i. Calculate the tensile modulus of elasticity of a unidirectional Kevlar-49 fibers epoxy composite material that contains 63% by volume of Kevlar 49 fibers and is stressed under isostrain conditions. The Kevlar 49 fibers have a tensile modulus of elasticity of 189.8 GPa and the epoxy matrix a tensile modulus of elasticity of 3.8 GPa. ii. If the tensile strength of the Kevlar 49 fibers is 3.8 GPa and that of the epoxy resin is 75.9 MPa, calculate the tensile strength of the composite material in Q3b(i). Calculate the fraction of load carried by the Kevlar 49.
I need the solution of this question,please. Prove that the area fraction equal to volume fraction when using aligned fibers in composite materials.
Explain what the following terms mean:decomposition temperature, heat distortion temperature, glass-transition temperature, and melting temperature. Why is itthat thermoplastics do not have a fixedmelting or glass-transition temperature?