Carbon is allowed to diffuse through a steel plate 11 mm thick. The concentrations of carbon at the two faces are 0.85 and 0.42 kgC/m³ in Fe, which are maintained constant. If the preexponential and activation energy are 6.2 × 10-7 m²/s and 80,000 J/mol,respectively, compute the temperature (in K) at which the diffusion flux is 6.5 × 10-10 kg/m²-s.i 1170KeTextbook and MediaHintAssistance UsedReview Sections 5.3 and 5.5, in particular Equations 5.2, 5.3, and 5.8.dCJ = -Ddx(5.2)dCACСл — Свconcentration gradient :dx(5.3)AxХА — ХвD = Do exp|(5.8)RT

Given: t=11 mm C1= 0.85 kgC/m3 C2=0.42 kgC/m3 Activation energy =80000 J/mol To determine: The…

Answered: ,compute the temperature (in K)

Engineering

Mechanical Engineering

,compute the temperature (in K)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The activation energy for the diffusion of copper in silver is 193,000 J/mol. Calculate the diffusion coefficient at 1200 K (927C), given that D at 1000 K (727C) is 1.0 x10^-14 m2 /s.
The diffusion coefficient for carbon in BCC iron at 400C and 900C is given as 3.80x10-13 and 1.70x-10m2/s respectively. Determine the temperature (in degrees C) at which a specimen of BCC iron has to be carburized for 150 minutes to produce the same diffusion result as at 900C for one hour.
Calculate the diffusion constant, D, for the process at a diffusion temperature of T=1150 ⁰C given that D0 = 5.5 *10-5 m2/s; Qd = 148,000 J/mol.
The diffusion coefficients for iron in nickel are given at two temperatures: T(K) D(m2/s) 1273 9.4 x 10-16 1473 2.4 x 10-14 (a) Determine the values of D0 and the activation energy Qd. (b) What is the magnitude of D at 1100ºC (1373 K)?
Calculate the value of the diffusion coefficient D (in m^2/s) at 694°C for the diffusion of some species in a metal; assume that the values of D0 and Qd are 5.6 x 10^-5 m^2/s and 177 kJ/mol, respectively. R=8.314 J/(mol*K)
Gaseous hydrogen weakens the mechanical strength of cast iron. this phenomenon often occurs in cast iron pressure vessels containing 100% gas hydrogen. H2 gas dissolves in metallic iron and diffuses into solid non-porous iron by an interstitial diffusion mechanism. H2 gas does not need to penetrate far into the iron to have a negative effect on the mechanical strength of iron. In the present situation, 100% of H2 gas at 1.0 atm and 100°C is contained within a 1.0 m internal diameter and wall thickness of 2.0 cm. The solubility of hydrogen in iron in 100°C is 2.2x10-7 mol of H/g Fe atoms. The diffusion coefficient of atoms of hydrogen in solid iron is 124.0x10-9 cm2 /sec at 100°C. Initially, there are no H atoms in solid iron. How many hours will it take for the hydrogen level inside the iron metal reaches 1.76x10-7 mol H atoms/g Fe at a depth of 0.1 cm from the surface exposed to hydrogen gas?
The diffusion coefficient of nickel in an austenitic stainless steel is 10-22 m2/s at 500°C and 10^-15 m^2/s at 1000°C. Calculate the activation energy for the diffusion of nickel in this alloy over this temperature range.
Diffusion of carbon into the surface of BCC steel at 600oC for 10 hours results in a carbon concentration of 0.2wt% at a depth of 1.5 mm below the surface. At what depth will the same concentration be obtained if the diffusion time is increased to 20 hours, leaving the temperature at 600o
A sheet of steel with 3.5-mm thickness has a nitrogen atmospheres on both sides at 900°C and is permitted to achieve a steady-state diffusion condition. The diffusion flux is found to be (1.0 ×10^-7 )kg/m^2×second.Also it is known that the concentration of nitrogen in steel at the high-pressure surface is 2 kg/m^3.How far into the sheet from this high-pressure side will the concentration be 0.5 kg/m^3?Assume a linear concentration profile.
The diffusivity of aluminum in a commercial aluminum alloy is 10-20 m2/s at 400°C. The activation energy for diffusion of Aluminum in this system is 195 kJ/mol. Calculate the diffusivity at 600°C
[Decarburization] An FCC iron-carbon alloy initially containing carbon with the concentration, C0, is exposed to anoxygen-rich and virtually carbon-free atmosphere. Under the given conditions, the carbon diffuses from the alloy andreacts at the surface with the oxygen in the atmosphere, meaning that the carbon concentration at the surface position is maintained essentially at 0 wt% C. The subproblems are independent.(1) Determine the diffusion coefficient at the temperature T given below. Use T = 1250 °C(2) When the value of D is given below, what position will the carbon concentration be Cx after a treatment for thetime, t? Use D = 1.93 × 10−10m2 /s; C0 = 0.35 wt%; Cx = 0.11 wt%; t = 12 hr
(c) Consider an alloy that is undergoing carburizing process, initially has a uniform carbon concentration of 0.27 wt% and is to be treated at 950oC (1750oF). If the concentration of carbon at the surface is suddenly brought to and maintained at 1.32 wt%, how long will it take to achieve a carbon content of 0.85% at a position 0.7 mm below the surface? The diffusion coefficient for carbon in iron at this temperature is 1.6 x 10-11 m2/s; assume that the steel piece is semi-finite.