Consider a cylindrical specimen of a steel alloy with 8.5 mm diameter and 80 mm long that is pulled in tension. Estimate the following mechanical properties using Fig. 1: a. Modulus of Elasticity and Resilience in MPa and psi b. Ultimate Tensile Strength in MPa and psi c. Fracture Strength in MPa and psi d. Ductility or % elongation at fracture in MPa and psil

Consider a cylindrical specimen of a steel alloy with 8.5 mm diameter and 80 mm long that is pulled in tension. Estimate the following mechanical properties using Fig. 1: a. Modulus of Elasticity and Resilience in MPa and psi b. Ultimate Tensile Strength in MPa and psi c. Fracture Strength in MPa and psi d. Ductility or % elongation at fracture in MPa and psil

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

You are given a 10-cm-diameter cylindrically shaped extruded bar (length = 50 cm) of an aluminum alloy. a. What specimen configurations would you use to characterize the degree of anisotropy of the material’s fracture toughness? b. If the lowest fracture toughness of the bar was found to be 20 MPa √m , what would be the load level needed to achieve this stress intensity level? c. Confirm the presence of plane-strain conditions, given that σys = 500 MPa. (Assume specimen thickness = 1 cm, a/W = 0.5, and bar diameter = 1.2 W.)
You are called as an expert witness to analyze the fracture of a sintered silicon carbide plate that was fractured in bending when a blunt load was applied to the plate center. Measurement of the distance between the fracture origin and the mirror/mist boundary on the fracture surface gives a radius of 0.796 mm. You are given three pieces of the same SiC to test, and you determine that the mirror radius is 0.603, 0.203, and 0.162 mm for bending failure stress levels of 225, 368, and 442 MPa, respectively. What is your estimate of the stress present at the time of fracture for the original plate?
A specimen of a 4340 steel alloy having a plane strain fracture toughness of 45MPa√m is exposed to a stress of 1000 MPa. The largest surface crack is 0.75mm and the parameter Y has a value of 1.0. Show that the specimen will fracture under this amount of applied stress.
An 820 MPa (145,000 psi) stress is applied to a specimen of 4341 steel alloy, which has a plane strain fracture toughness of 45MPa squareroot (m). If the greatest surface crack is 0.95 mm (0.03 in) long, will this specimen fracture as a result? Assume that the parameter Y is 1.22.
Estimate the theoretical fracture strength of a brittle material if it is known that fracture occurs by the propagation of an elliptically shaped surface crack of length 0.20 mm and that has a tip radius of curvature of 0.001 mm when a stress of 1450 MPa is applied. The question is attached. The answer is not 29000. WileyPlus marks it as incorrect.
A Copper specimen of circular cross-section is subjected to a tensile test. The data obtained are: Length of Specimen = 329 mm; Diameter of Specimen = 39 mm; Load at Yield Point = 130 kN; Maximum Load = 219 kN; Load at fracture = 118kN Determine the following: 1) Find initial area of the test specimen 2) Yield Stress 3) Ultimate Stress 4) Fracture stress 5) Find the strain for 0.058mm elongation.
To manufacture a piston with a circular cross section, an alloy steel bar is required whose length is fixed and has a value of 35 cm and must withstand a compression load of 5.2 tons. For its design, a safety factor of 4/5 is suggested with respect to the yield stress. The shear modulus for that alloy is 80 GPa.To know the resistance of this steel alloy, a compression test was carried out on a specimen of the same material, from this test the data table of stress against engineering deformation shown was obtained. Image 1 1) Calculate the increase in the diameter of the bar when the load is applied2) Define the Poisson's ratio and calculate its value
Experiments were conducted in a tension testing machine to evaluate the material properties of two metallic rods both having diameter equal to 10 mm. First rod having modulus of rigidity of the material equal to 400 tonnes/cm2 when subjected to an axial tensile force of 6 kN, the change in its diameter was observed to be 0.0018 cm. The value for the bulk modulus of the second metallic rod is same as that of the first one but modulus of elasticity 18% more. Based on the material properties calculate and compare the values of different moduli as well as Poisson’s ratio for both metallic rods. Justify your answer with reasons.
A structural beam is built from steel with a yield strength of 345 MPa. The structure has a minimum service temperature of 5 oC, where the fracture toughness of the steel KIC = 60 MPam. What is the minimum surface crack lengths that must be detected by quality control to ensure that the full yield strength of the steel is available in the beam? Assume geometric parameter Y = 1 and plain strain conditions. Answer in millimeters.
cylindrical specimen of steel having an original diameter of 0.505 in. is tensile tested to fracture and found to have an engineering fracture strength of 67,000 psi. If its cross-sectional diameter at fracture is 0.422 in, determine:(a) The ductility in terms of percent reduction in area(b) The true stress at fracture
For a piece of copper alloy, a standard stress test was applied to it, the following data was collected, from which a stress-strain diagram must be generated, where as data it is known that the initial diameter of the element is 0.505in. The analysis must include the following: 1.Modulus of Elasticity and modulus of resilience. 2.Percentage of elongation. 3.Percentage of area reduction. 4.Real and engineering stress at fracture. It is known that after the specimen fractures, its dimensions in terms of length and diameter are 3.014 and 0.374in, respectively.
A 50 mmm long circular rod of the AISI 1015 hot rolled steel with a diameter of 12.5 mm is loaded in tension to failure. From the test it is learnt that the yield strength = 315 MPa, the tensile strength = 420 MPa, the elongation at fracture = 39% and the reduction in area = 51%. It is also observed that 45% of the total elongation was uniform in nature prior to the onset of necking. a) What is the true strain at fracture? b) Calculate the true stress at the point of onset of plastic instability c) What is the the strength coefficient K for this steel?