Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a thidkness of 6 mn The roll radius is 200 mm, and the roll rorates at 200 rev/min; use coefficient of friction at the die-work interface (u)- 0.1. A low carbon steel such as AISI 1020 has K (strength coefficient) - 530 MPa and n( strain hardening exxponent)= 0.26

Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a thidkness of 6 mn The roll radius is 200 mm, and the roll rorates at 200 rev/min; use coefficient of friction at the die-work interface (u)- 0.1. A low carbon steel such as AISI 1020 has K (strength coefficient) - 530 MPa and n( strain hardening exxponent)= 0.26

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A metal strip is to be rolled from an initial wrought thickness of 3.5 mm to a final rolled thickness of 2.5 mm in a single pass rolling mill having rolls of 250 mm diameter. The strip is 450 mm wide. The average coefficient of friction in the roll gap is 0.08. Taking plane strain low stress of 140 MPa, for the metal and assuming negligible spreading, the roll separating force is.....
A 300mm thick slab is being cold rolled using roll of 600mm diameter.If the coefficient of friction is 0.08. Determine the maximum possible reduction.
Estimate the roll force, F, and the torque for an AISI 1020 carbon-steel strip that is 200 mmwide, 10 mm thick, and rolled to a thickness of 7 mm. The roll radius is 200 mm, and itrotates at 200 rpm. Note that K = 530 MPa and n = 0.26.
A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. To do 5.1 If the final width of the sheet is 200 mm, calculate the required roll force. 5.2. Explain what is roll flattening, its effects and how it can be reduced.
A plate that is 260 mm wide and 27 mm thick is to be reduced in a single pass in a two‑high rolling mill to a thickness of 22 mm. The roll has a radius = 510 mm, and its speed = 25 m/min. The work material has a strength coefficient = 235 MPa and a strain hardening exponent = 0.21. Determine (a) roll force, (b) roll torque, and (c) power required to accomplish this operation
In a rolling operation using rolls of diameter 400mm if a 35mm thick plate cannot be reduced to less than 20 mm in one pass coefficient of friction between the roll and the plate is??
Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thlck, rolled to a thickness of 6 mm The roll radius is 200 mm), and the roll rotates at 200 rev/min; use coefficient 0f friction at the die-work interface (p)= 0.1, Alow carbon steel such as AlSI 1020 has K (strength coefficient) = 530 MPaand n (stram hardening exponent) = 0.26
A solid cylindrical slug made of 304 stainless steel is 150 mm in diameter and 100 mm high. It is reduced in height by 50% at room temperature by opendie forging with flat dies. Assuming that the coefficient of friction is 0.2 and the flow stress of this material is 1000 MPa, calculate the forging force at the end of the stroke. Manufacturing processes
A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. 5.1 Calculate the minimum coefficient of friction required, that will make the rolling operation possible. 5.2 Calculate the exit velocity of the plate. 5.3 Calculate the forward slip. 5.4 If the final width of the sheet is 200 mm, calculate the required roll force. 5.5 Explain what is roll flattening, its effects and how it can be reduced.
A cylindrical part is warm upset forged in an open die. The initial diameter is 50 mm and the initial height is 40 mm. The height after forging is 30 mm. The coefficient of friction at the die-work interface is 0.25. The yield strength of the work material is 285 MPa, and its flow curve is defined by a strength coefficient of 600 MPa and a strain-hardening exponent of 0.12. Calculate the strain at yield point.
1. A round wire made from 1020 carbon steel is being drawn from a diameter of 12.5 mm to 9.5 mm in a draw die of 10°. For a coefficient of friction of 0.15, calculate required drawing force. 2. How would the extrusion process be effected if the die angle is increased?
A cold heading operation is performed to produce the head on a steel nail. The strength coefficient for this steel is 600 MPa, and the strain hardening exponent is 0.22. Coefficient of friction at the die‑work interface is 0.14. The wire stock out of which the nail is made is 5.00 mm in diameter. The head is to have a diameter of 9.5 mm and a thickness of 1.6 mm. The final length of the nail is 120 mm. (a) What length of stock must project out of the die in order to provide sufficient volume of material for this upsetting operation? (b) Compute the maximum force that the punch must apply to form the head in this open‑die operation.