2) Answer the following questions according to the given Ag-Cu system.1200Liquid1000 -800-(Ag)(Cu)2 600-400-200-102030 40 5060708090100AgMass % CuCue) For the 95Cu-5Ag alloy, determine the amount and the composition ofthe each phases and draw the microstructures schematically for the1010°C, 850°C ve 25°C.f) For the Ag-20% Cu and Ag-80% Cu alloy; from 1100°C to roomtemperature,(a) For equilibrium solidification, (b) For nonequilibrium solidification (veryrapid cooling)Show the change in the microstructures schematically for the giventemperatures; i) 1100°C ii) Liquidus temperature iii) 20°C below of eutectictemperature iv) Room temperature

Answered: Image /qna-images/answer/2ef26c3f-3aee-4e6a-8da5-68cbf990ddf8.jpg

Answered: f) For the Ag-20% Cu and Ag-80% Cu…

Engineering

Mechanical Engineering

f) For the Ag-20% Cu and Ag-80% Cu alloy; from 1100°C to room temperature,

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: In white cast iron, the carbon is in combined form as .. O cementit O iron O silicon O cementite

A: White cast iron displays white fractured surfaces due to the presence of an iron carbide…

Q: Consider 2.4 kg of a 99.7 wt% Fe-0.3 wt% C alloy that is cooled to a temperature just below the…

Q: 4. Give the temperature range over which it is possible to austenitize each of the following Fe-C…

A: Full annealing is a softening process in which the metals is heated above the re crystallation…

Q: QUESTION 1 For a 1% steel, the carbon is completely soluble in iron at: 1600 Q 1400°C liquid 910°C…

A: For 1 % steel, single phase will not be possible.

Q: Torricellian vaccum is

A: answer is 2nd option, Barometer.for solution refer below image.

Q: 900 1600 800 (a) A+F 1400 (a) 700 |(c) (c) A + P P 1200 600 (c) A + B 1000 500 (c) A (b) 800 50% 400…

A: we have (a) The final composition will consist of proeutectoid ferrite and martensite.

Q: Determine the tensile strength of a eutectoid Fe-Fe3C alloy that has been subjected to heat…

A: Given : To find : tensile strength

Q: n a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture…

A: Given: Ectetiod Temperature = 723 °CAusentic mixture = 2% C

Q: Hardness of steel greatly improves with

A: Hardness of steel greatly improves with Answer: a) Cyaniding

Q: QUESTION 20 Consider a 60 wt% Sn-40 wt% Pb alloy residing at 100°C, (a) Draw a tie-line and label…

A: Given: The composition of the alloy, C = 60Wt%Sn and 40Wt%Pb The temperature of the alloy, T = 100 C

Q: Q12. Carry out a phase analysis on the Bismuth-Cadmium eutectic composition.

A: Given question: Carry out a phase analysis on the Bismuth-Cadmium eutectic composition. The…

Q: Question 5 Draw eutectic binary system graph for lead-tin alloy (Sn-Pb). Consider a lead–tin alloy…

Q: (c) Two samples of steel contain 93 % pearlite. Estimate the carbon content of each sample if one is…

Q: Define the following terms: a. heat of fusion b. heat of vaporization c. heat capacity d. boiling…

A: note: “Since you have posted a question with multiple sub-parts, we will solve first three sub-parts…

Q: Q2/ * QI/For a 60 wt% Pb -30 wt% Sn alloy as shown in figure below, Determine: (a) The phase(s) is…

Q: For the preceding problem, use the inverse lever rule to determine the proportions of liquid and…

A: Dear Students

Q: Q1/ Draw a thermal equilibrium diagram for the binary alloy system (Si -Au), from the following…

Q: 20. The equilibrium vapor pressure of solid Cu as a function of temperature is given by 45,650 In…

Q: 13. In Steel produced by BOF or electric furnace. The treatment involves adding in elements such as…

Q: Name the microstructural products of a eutectoid iron-carbon alloy (0.76 wt% C ) that is first…

A: Material Science

Q: ) Is it advisable to have austenite in the HAZ (Heat Affected Zone)? Explain?

A: Explanation- Whenever a material (steels) welds with a specific welding process, there will heat…

Q: What is the value of higher heating value if the value of lower heating value is 10 J and the…

A: Option a is correct.

Q: H.W.:- An ore is analyzed for manganese content by converting the manganese to Mn3O4 and weighing…

Q: 9.10 Cite the phases that are present and the phase compositions for the following alloys (please…

Q: Quenching is a process used to preserve at room temperature a phase which exists in equilibrium at…

A: We are authorized to answer one question at a time since you have not mentioned which question you…

Q: Q2 By using the Iron - Carbon diagram that you have. Find 5 of the following. 1- Find the Eutectic,…

Q: Q3: For a 94.5 wt% Fe-5.5 wt% C at a temperature1100 °C, determine the following: a) The Number and…

A: Apply level to find the mixture percentage

Q: Which of the following process is not an example for Case Hardening process? a. Annealing b.…

A: Examples for heat treatment process:- Annealing Normalizing Hardening Tempering

Q: Ans. 4.44 x 10 rapid quenching from 800 K.

Q: Q.1. What is the composition in weight percent, of an alloy that consists of 10 at% Cu and 90 at%…

A: Given: 10% of Cu and 90% of Al

Q: In white cast iron, the carbon is in combined form as .......... O cementite iron O silicon оос…

Q: How do I manually calculate the Final temperature of Aluminum, unknown solid 1, unknown solid 2? How…

A: Specific heat of aluminium = . 89J/gC

Q: For a 1095 steel alloy, what would the percent of each phase be at 730°C and 725°C?

A: Given alloy is steel 1095, for this steel percentage of the carbon present inside the steel is…

Q: Q3/ Draw thermal equilibrium diagram for the binary alloy (Pb- Sn) from the following data :- Lead…

Q: Explain briefly How rock (iron ore) converted to iron using the blast furnace.

A: The most commonly obtained rock (iron ore) from beneath the earth is either Fe2O3 Haemaetite or…

Q: For a 99.65 wt% Fe-0.35 wt% C alloy at a temperature just up the eutectoid teamperature, determine…

A: Given At 99.65% Fc -0.35 wt%

Q: Q1/ Draw a thermal equilibrium diagram for the binary alloy system (Si –Au), from the following…

A: Given: The melting temperature of Si, TSi = 1414oC The melting temperature of Au, TAu = 1064oC The…

Q: - The microstructure for AISI 1080 carbon steel after heat 760°C then For AISI 1080 carbon steel,…

A: Hello. Since your question has multiple sub-parts, we will solve first three sub-parts for you. If…

Q: Using the TTT diagram, explain how you can get the following: (explain by mentioning detailed heat…

Q: During a quenching process on a TTT diagram, we can transform pearlite into bainite. True or false?

A: In a quenching process represented on the TTT diagram, transformation is shown from austenite to…

Q: Q2)) Answer the following briefly: A) Why the primary iron product (pig iron) that resulted from the…

A: Dear student as per the policy i can solve only 3 subparts for you so request to post the remaining…

Q: An alloy of Component A and Component B, which do not react but are miscible in all proportions in…

A: Phase Diagrams: It is an equilibrium diagram which represents the composition of constituent…

Q: The cementite phase in the Iron-Carbon system is metastable. True/False

A: The given statement is true.

Q: answer choices 327 °C

A: From above digram it is clear that Sn is 100 ℅ ar the right corner. So from graph value of melting…

Q: -General Form of Designation. A. Carbon Content in Points or hundredths of percent AISI x x xx B.…

Q: Calculate the standard heat of formation of PbO from Pb and 02 at 227°C from the following data:…

A: Dear student, According to the guidelines I am allowed to answer only one…

Q: Example 3.6 يخلط معدن النحاس والفضة جيدا في شكل مسحوق ، بنسب 80 وزن / س نحاس و 20 ث / س Ag ويتم…

A: Lever Rule in phase diagram: A1 = amount of α phase present in mixture A3 = amount of β phase…

Q: 10/. In _________ process, heating is carried out 20°C above the lower critical temperature and then…

Q: Q1. Fill the blanks 1- The formation of metal alloys system consist of ,1..,2..,3...,4..,5...,6...…

Q: Explain shortly what you know about the following terms as applied in heat treatment.…

Concept explainers

Strengthening of Alloys

Strengthening of the alloys is required as metals become weak due to various lattice defects, metal bonding phenomena. The strength of the metals is not enough for any mechanical work. The internal dislocations of any metals arise due to forming processes. Due to the movement of these dislocations, the metals are plastically deformed.

Question

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?
Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to points A (1400 C), B (950 C), C (800 C), and D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine the weight in each phase. Point A): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point B): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point C): Phase(s) present Weight % of Cu in each phaseWeight of each phase Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phase
Choose the corect answer -A vertical line in the phase diagram represents a.an intermetallic compound b.a eutectic phase c.a eutectoid phase Match each statement with a letter -In the peritectoid reaction -In the Peritectic reaction: -In the Monotectic reaction: -In the Eutectoid reaction: -In the Eutectic reaction: a. a liquid phase transforms into two solids when it is cooled down b. a solid phase transforms into two different solids when it is cooled down c. a liquid phase transforms into a new liquid phase and a solid phase d. Two solid phases transform into a new single solid phase e. A solid phase and a liquid phase transforms into a solid phase
In a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.
Presume that we have 100 grams of an alloy with overall chemical composition of90 wt. pct. tin and 10 wt. pct. lead. The alloy (in the liquid state) is cooled atnear-equilibrium conditions.Determine the following:At slightly below 183oC, what are the following: (parts a-h at a temperature below 183C please!)
Q1/ The figure below shows the phase equilibrium diagram for copper and silver Answer the following paragraphs? Conpostin a% 39 o = « & o Tepertue (F) @ Composttan (w5 ) 0 1- define pointe E? 2- define pointe B? 3- define the line AE? 4- define the line BG? 5- define the line FG?
In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: a) Is this alloy hypoeutectic or hypereutectic? b) What is the composition of the first solid to form? c) What are the amounts and compositions of each phase that is present at 183°C + ∆T ? d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite
An alloy of 30 wt % Pb and 70 wt % Sn is slowly cooled from 250°C to 27°C: d) What is the amount and composition of each phase that is present at 183°C - ∆T ? e) What are the amounts of each phase present at room temperature? f) Draw the microstructure 183°C + ∆T and 183°C - ∆T in 2 cm diameter circle.
For the system KNO3-NaNO3-H2O, a ternary point exists at 5°C at which the twoanhydrous salts are in equilibrium with a saturated solution containing 9.04% KNO3 and41.01% NaNO. Determine analytically the maximum weight of KNO3 which can berecovered pure from a salt mixture containing 70 g of KNO3 and 30 g NaNO3 bycrystallization from an aqueous solution at 5°C. Draw the phase diagram and show your solution.
Calculate the amounts and compositions of phases at 726oC in a Fe-0.6% C alloy cooled under equilibrium conditions. Disregard the amounts of proeutectoid phases. A. 77.3% α, 22.7% Fe3C; C in α = 6.7% and C in Fe3C = 0.02% B. 91.3% α, 8.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% C. 77.3% α, 22.7% Fe3C; C in α = 0.02% and C in Fe3C = 6.7% D. 91.3% α, 8.7% Fe3C; C in α = 0.05% and C in Fe3C = 8.4% E. None of the mentioned