Question 5 Draw eutectic binary system graph for lead-tin alloy (Sn-Pb). Consider a lead–tin alloy of composition 40 wt% Sn-60 wt% Pb is slowly heated from a temperature of 150 C. Answer all questions below and show it in the graph. a. At what temperature does the first liquid phase form? b. What is the composition of this liquid phase? c. At what temperature does complete melting of the alloy occur? d. What is the composition of the last solid remaining prior to complete melting?

Question 5 Draw eutectic binary system graph for lead-tin alloy (Sn-Pb). Consider a lead–tin alloy of composition 40 wt% Sn-60 wt% Pb is slowly heated from a temperature of 150 C. Answer all questions below and show it in the graph. a. At what temperature does the first liquid phase form? b. What is the composition of this liquid phase? c. At what temperature does complete melting of the alloy occur? d. What is the composition of the last solid remaining prior to complete melting?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

For alloys of two hypothetical metals A and B, there exist an α, A-rich phase and a β, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Alloy Composition Fractionα Phase Fractionβ Phase 60 wt% A - 40 wt% B 0.57 0.43 30 wt% A - 70 wt% B 0.12 0.88 (a) α phase ________ wt% A (b) β phase ________ wt% A
A hypothetical A-B alloy of composition 54 wt% B-46 wt% A at some temperature is found to consist of mass fractions of 0.5 for both αand β phases. If the composition of the β phase is 89 wt% B-11 wt% A, what is the composition of the α phase? ________ wt% B
Water's unary phase diagram has a triple point at 0.01 °C and 0.006 atm, and a solid-liquid boundary with a negative slope. Consider water vapor at 110 °C and 1.08 atm. At constant temperature, what will happen if the pressure was increased? a. water vapor will condense into a liquid then freeze into a solid b. water vapor will transition directly to the solid state c. water vapor will condense into a liquid but will never become a solid
A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine (b) the composition of the liquid phase in wt% Ni
10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?
A 50 wt% Ni–50 wt% Cu alloy is heated to a temperature within the a liquid-phase region. If the composition of the alpha phase is 58 wt% Ni, determine the equation of mass fraction of liquid phase ,WL
An alloy of Component A and Component B, which do not react but are miscible in all proportions in molten state, is used to manufacture “Fail Safe” devices for boiler. Narrate the effect of composition on equilibrium: Solid ↔ Liquid with the help of a phase diagram, if the melting point of A (900 ºC), B (350 ºC) and the lowest melting of all compositions is 280 ºC at 12.6% of A and 87.4% of B.
For alloys of two hypothetical metals A and B, there exists an a, A-rich phase and a b, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Alloy composition Fraction a Phase Fraction b Phase 60wt%A-40wt%B 0.60 0.40 30wt%A-70wt%B 0.12 0.88 a) a Phase = ___________ wt%A b) b Phase = ___________ wt%A
Use the phase diagrams for Cu-Ni and Cu-Ag systems below to answer the question: Use the diagrams provided to determine the values of the following: i. Solubility of Ni in Cu at 1050 °F. ii. Solubility of Ag in Cu at 700 °F.iii. Solubility of Cu in Ni at 1300 °F. iv. Solubility of Cu in Ag at 400 °F.
Referring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325C
Question: For 5.7 kg of a magnesium–lead alloy of composition 50 wt% Pb–50 wt% Mg, is it possible, at equilibrium, to have α and Mg2Pb phases with respective masses of 5.13 and 0.57 kg? If so, what will be the approximate temperature of the alloy? If such an alloy is not possible, then explain why.
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…