From the shear stress - shear strain diagram shown below, all the following are true except: Shear Stress (MPa) 400 250 200 15e 100 se as 1 12 14 1.6 Shear Strain frad) Shear Stress-Strain Curve for Brass Select one: a. The ultimate Shear stress and Shear strain are 430 MPa and 1.72 rad. b. Shear stress and Shear strain are 250 MPa and 0.05 rad at Yielding. c. Shear stress and Shear strain are 430 MPa and 1.72 rad at fracture. d. The elastic zone ends at a shear stress of 400 MPa and shear strain of 1 rad

From the shear stress - shear strain diagram shown below, all the following are true except: Shear Stress (MPa) 400 250 200 15e 100 se as 1 12 14 1.6 Shear Strain frad) Shear Stress-Strain Curve for Brass Select one: a. The ultimate Shear stress and Shear strain are 430 MPa and 1.72 rad. b. Shear stress and Shear strain are 250 MPa and 0.05 rad at Yielding. c. Shear stress and Shear strain are 430 MPa and 1.72 rad at fracture. d. The elastic zone ends at a shear stress of 400 MPa and shear strain of 1 rad

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Civil engineers often use the straight-line equation, = b 0 + b 1x, to model the relationship between the shear strength y of masonry joints and precompression stress, x. To test this theory, a series of stress tests were performed on solid bricks arranged in triplets and joined with mortar. The precompression stress was varied for each triplet and the ultimate shear load just before failure (called the shear strength) was recorded. The stress results for n = 7 resulted in a Coefficient of Determination of 0.8436. Given that r 2= 0.8436, give a practical interpretation of r 2, the coefficient of determination for the least squares model. a. We expect to predict the shear strength of a triplet test to within about 0.8436 tons of its true value. b. About 84.36% of the total variation in the sample of y-values can be explained by (or attributed to) the linear relationship between shear strength and precompression stress. c. In repeated sampling, approximately 84.36% of…
a . Sketch stress strain curve if the result shown in table represent the force and extension happened in steel, and show Mechanical properties that we get from tensile test on curve? (10p)Note : Lo=80 mm , Do=10 mm , use excel to plot the curve ExtensionLoad(mm) (N)0 0.900.83 4694.341.67 4831.412.50 4781.083.33 4918.834.17 4926.585.00 5257.075.83 5437.016.66 5575.888.33 5775.189.16 5847.5210.83 5965.4111.67 6010.5312.50 6042.5713.33 6072.2614.16 6092.9315.00 6113.2416.67 6140.3617.50 6146.3718.33 6148.1419.16 6149.1725.00 5940.2125.83 5675.3326.67 4725.52b. What is meant by modulus of rigidity? if it increases what does happen to material? (2p)
In a forming process the diameter of the specimen is 1 cm and its length changes from 50 mm to 60 mm. Show the maximum force value on the graph of Force vs. True Strain plotted in Excel Program or any plotting program not by hand using the flow stress equation given below. σ= Kεn and σ=F/A Where the parameters are σ : True Stress in MPa K: Strength Coefficient, K=210 in MPa ε : True Strain, ε=ln (l/l0) n: Strain Hardening Exponent, n=0.27 F: Force in 10 A : Area in mm2 Take at least 3 digits after the decimal point. Specify the units. You can use Excel or any plotting program not by hand then paste your graph into the solution section.
An element of material in plane strain is subjected to strains εxx=480×10–6 , εyy=70×10–6 and τxy=470×10–6 . Determine the strains for an element rotated through an angle θ=80⁰, the principal strains and the maximum shear strains using (a) transformation relations, (b) using Mohr’s circle of strains.
A 316 steel plate sample is under the following loading condition:?(sigma) = 90 40 0 40 −50 0 0 0 0 MPaa. Plot the shear and normal stresses on a given oblique plane (rotated plane) on a graph (stress vs. angle) and show the max. shear plane and the principal planes.b. Draw the Mohr circle for the loading state above to scale (using a proper computer program or using a compass with correct scales on the axes) and show the angles you found in (a).c. If the steel sample has a Young’s modulus of 193 GPa, compute the dimensional changes of the plate under the above loading condition
a. Determine whether the new biomaterial follows a most closely a linear elastic, neo-Hookean, or Mooney-Rivlin relationship.b. Show manipulation of strain energy density functions and include comparative plots of data showing results for linear elastic, neo-Hookean, and Mooney-Rivlin relationships.c. list any assumptions givens: . Shear moduli: 11 = U2 = 10MPa. Relationship between elastic constants: E = 2u(1 + v)
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. Question 1 ;Determine the elastic energy absorption capacity (in N.mm) of that specimen. Question 2; Determine the plastic energy absorption capacity (in N.mm) of that specimen.
The stress-strain diagram of a reinforcement steel having a cross-sectional diameter of 12 mmdiameter and 100 mm gage length is determined after its tensile strength test as follows. Based on the stressstrain diagram determine the followings properties of the material (Poisson’s ratio of the material is 0.32) : a) Modulus of elasticityb) Yield strengthc) Toughnessd) Resiliencee) Shear modulusf) Bulk modulusg) Ductility as described bypercent change in length
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Determine the true stress (in MPa) at yield point. - Determine the true stress (in MPa) at point of ultimate strength. - Determine the true stress (in MPa) at fracture point. - Determine the true strain (in mm/mm) at yield point. (Use at least five decimal units) - Determine the true strain (in mm/mm) at point of ultimate strength. (Use at least five decimal units) - Determine the true strain (in mm/mm) at fracture point. (Use at least five decimal units)
A sheet metal cutting machine cuts the sheet metal via shear force, V as shown in Fig. 1. The crosssection of sheet metal is rectangular with width, b = 3m and thickness, d = 5mm. The sheet metal ishaving yield strength σy = 220 MPa; Young’s modules, E = 200 GPa and Poisson’s ratio, ν = 0.3.Conduct the following analyses at the state of stress when maximum stress reaches σy and beforeshearing commences. (Need answer Question c) & d) c. Sketch the YIELD LOCI for both cases above. d. As a sheet-metal engineer, which failure criterion in (b) will you use to determine the cuttingshear force? Explain the reason for your answer.
A sheet metal cutting machine cuts the sheet metal via shear force, V as shown in Fig. 1. The crosssection of sheet metal is rectangular with width, b = 3m and thickness, d = 5mm. The sheet metal ishaving yield strength σy = 220 MPa; Young’s modules, E = 200 GPa and Poisson’s ratio, ν = 0.3.Conduct the following analyses at the state of stress when maximum stress reaches σy and beforeshearing commences. a. At the MOST CRITICAL POINT of the sheet metal, calculate the stress state and sketch thecorresponding stress element b. If SAFETY FACTOR = 2 is considered, what is the MINIMUM shear force, V required tocut the sheet metal according to following criterions? i. ii. Tresca criterion?von Mises criterion? c. Sketch the YIELD LOCI for both cases above. d. As a sheet-metal engineer, which failure criterion in (b) will you use to determine the cuttingshear force? Explain the reason for your answer.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.