i need the answer quickly Q1: A tensile test uses a circular test specimen that has a gage length of50 mm and diameter = 20 mm. During the test the specimen yieldsunder a load of 100,000 N. The corresponding gage length = 50.5 mm.%3DThis is the 0.2% yield point. The maximum load of 180,000 N is reachedat a gage length = 65 mm. Determine%3D(a) yield strength,(b) modulus of elasticity, and(c) tensile strength.(d) If fracture occurs at a gage length of 73 mm, determine theductility..

Given that, gage length = 50 mm diameter = 20 mm loat at 0.2% yield point = 100,000 N gage length…

Q1: A tensile test uses a circular test specimen that has a gage length of 50 mm and diameter = 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility..

Q1: A tensile test uses a circular test specimen that has a gage length of 50 mm and diameter = 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility..

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.6P: The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular...

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
Consider a bar with a rectangular cross-section area with a thickness of t = 0.5 in. and height of h = 3.5 in. When force P = 19 kips is applied to the bar, the strain gages attached to the surface of the bar reads εx = 740 µε along the direction of the force and εy = -170 µε in the perpendicular direction. Determine Poisson's ratio for this specimen? Determine the modulus of elasticity for this specimen?in Ksi
In a simple tensile test using a cylindrical test specimen (Dia.=10mm), the applied force was 120 kN and the extension was 2%. Find the modulus of elasticity of that specimen. If the standard modulus of elasticity is 200 GPa, is this material accepted or not? and why?
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 74.0 ksi, e = 104.0 ksi , g = 85.0 ksi , and h = 0.15 in/in. Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.7 in . Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 11.0 kips, find the nominal stress experienced by the rod. Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It is then noted that the distance between the gage marks became 50.122mm. a,) What is the modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axial stress of the specimen?Note: Please show detailed solutions with illustrations.
Tension specimens (diameter d0 0.500 in., gage length L0 2.00 in.) made of structural materials A and B are tested to failure in tension. (a) At failure the distances between the gage marks are LAf 2.90 in. and LBf 2.22 in.; the corresponding diameters at the failure cross sections are dAf 0.263 in. and dBf 0.471 in., respectively. Determine the percent elongation in 2 in. and the percent reduction in area for these two materials, and classify each material as either brittle or ductile. (b) From these tensile tests the following data are also obtained: EA 10.0 103 ksi, (Y)A 5 ksi, (U)A 13 ksi; EB 10.4 103 ksi, (Y)B 73 ksi, (U)B 83 ksi. From the data given here, make rough sketches (to scale) of the stress-strain diagrams of materials A and B.
A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It isthen noted that the distance between the gage marks became 50.122mm. a,) What isthe modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axialstress of the specimen? Solution must have Free Body Diagram/drawing.
A metal specimen with 20 mm diameter and 100 mm gauge length is loadedelastically with 5 kN and elongates 0.8 mm. Its diameter under this load is 19.95 mm. Calculate:a) the Bulk Modulus, Kb) the Shear Modulus, G
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=50mm and initial diameter of d0=13mm. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 510 MPa , e = 693 MPa , g = 565 MPa , and ℎ = 0.15 mm/mm Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 65.0 mm.
a) A tension test was carried out for a specimen having 610 mm in length and an average diameter of 12.80 mm. The test was conducted until the specimen failed. The data record from a tensile test for the specimen is given in Table 1. A 50 mm gauge length was marked on the specimen before load applied.Referring to the data in Table 1;i) Plot a stress-strain diagram by using a scale of 1:0.02 mm/mm for the x-axis and 1:40 MPa for the y-axis. Redraw the elastic region by using a strain scale of 1:0.004 min/mm.ii) Determine the approximate modulus of elasticity, ultimate stress, and the yield strength of this material at 0.20% offset.iii) Calculate the modulus of toughness.iv) Calculate the final length of the specimen, if the specimen elongated about 26.78%.v) Calculate the percentage of reduction of area and the final diameter at breakage, if the cross-section area decreases to 105.13 mm2
a. Assuming the computer and the printer are turned on, what will be the next step to do when trying to perform a test?b. What part of the UTM will you use to remove the tensile test specimen from the grips?c. In what direction does the lower crosshead move during a tensile test?d. In what direction does the lower crosshead move during a compression test?e. In what direction does the lower crosshead move during a bending test?