QUESTION The following data were obtained during a tension test of a low carbon steel specimen having a gauge length of 100 mm. At the point where the stress strain curve deviated from linearity, the load was 35KN, the gauge length was 102.5 mm and the diameter of the specimen was 1.6 mm. Before necking began, loads of 45 KN and 55 KN produced gauge lengths of 103.4 mm and 107.7 mm respectively. Calculate (a) The Modulus of elasticity (b) The Strainhardening exponent

QUESTION The following data were obtained during a tension test of a low carbon steel specimen having a gauge length of 100 mm. At the point where the stress strain curve deviated from linearity, the load was 35KN, the gauge length was 102.5 mm and the diameter of the specimen was 1.6 mm. Before necking began, loads of 45 KN and 55 KN produced gauge lengths of 103.4 mm and 107.7 mm respectively. Calculate (a) The Modulus of elasticity (b) The Strainhardening exponent

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 146 kN. - Length of the specimen is 25 mm. - The yield strength is 83 kN/mm2. - The percentage of elongation is 40 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.1 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm) Answer for part 7
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 142 kN. - Length of the specimen is 23 mm. - The yield strength is 82 kN/mm2. - The percentage of elongation is 48 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 15 kN, iv) Young's Modulus if the elongation is 1.6 mm at 15 kN and (v) Final diameter if the percentage of reduction in area is 20 %. Solution Initial Cross-sectional Area (in mm2) Answer for part 1 The Diameter of the Specimen (in mm) Answer for part 2 Final Length of the Specimen (in mm) Answer for part 3 Stress at the elastic load (in N/mm2) Answer for part 4 Young's Modulus of the Specimen (in N/mm2) Answer for part 5 Final Area of the Specimen at Fracture (in mm) Answer for part 6 Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. Find: 1)Stress at the elastic load (in N/mm2) 2)Young's Modulus of the Specimen (in N/mm2) 3)Final Area of the Specimen at Fracture (in mm) 4)Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 151 kN. - Length of the specimen is 23 mm. - The yield strength is 79 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 17 kN, iv) Young's Modulus if the elongation is 2.4 mm at 17 kN and (v) Final diameter if the percentage of reduction in area is 24 %. THE QUESTION IS : FIND THE Final Diameter of the Specimen after Fracture (in mm)????
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 18 kN, iv) Young's Modulus if the elongation is 1.3 mm at 18 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution: Initial Cross-sectional Area (in mm2) The Diameter of the Specimen (in mm) Final Length of the Specimen (in mm) Stress at the elastic load (in N/mm2) Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 147 kN. - Length of the specimen is 28 mm. - The yield strength is 75 kN/mm2. - The percentage of elongation is 49 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 16 kN, iv) Young's Modulus if the elongation is 1 mm at 16 kN and (v) Final diameter if the percentage of reduction in area is 22 Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm) Initial Cross-sectional Area (in mm2)
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1.3 mm at 18 kN and Final diameter if the percentage of reduction in area is 25 %. Fine this ans 1-Initial Cross-sectional Area (in mm2) 2-The Diameter of the Specimen (in mm) 3-Final Length of the Specimen (in mm) 4-Stress at the elastic load (in N/mm2) 5-Young's Modulus of the Specimen (in N/mm2) 6-Final Area of the Specimen at Fracture (in mm) 7-Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. Initial Cross-sectional Area 2.01 mm2. The Diameter of the Specimen 1.59 mm. Final Length of the Specimen 42.92 mm. Stress at the elastic load 8955.22 N/mm2. Find: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 143 kN. - Length of the specimen is 29 mm. - The yield strength is 71 kN/mm2. - The percentage of elongation is 48 %. Determine the following Diameter of the specimen, Final length of the specimen, Stress under an elastic load of 18 kN, Young's Modulus if the elongation is 1 mm at 18 kN and Final diameter if the percentage of reduction in area is 29 %. FIND: Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
A tension test specimen had a gauge length of 2.5 in. After the test, the gauge length had increased to 6.5203 in. What is the uncertainty in the percentage elongation calculation of the specimen, if a caliper having an uncertainty of 0.001 in was used for measuring the length?