Refer to the composition-temperature phase diagram of solder, that is composed of lead (Pb) a tin (Sn). At the following temperature and composition, determine the mass of states a (solid sta of Pb) and B (solid state of Sn) for the solder alloy. Assuming the total mass of solder (m) to 100 g. a. Temperature = 100°C; alloy of 30% Sn and 70% Pb. b. Temperature = 200°C; alloy of 30% Sn and 70% Pb. c. Temperature = 200°C; alloy of 90% Sn and 10% Pb. What is the eutectic temperature and determine the composition where such a reaction m occur? 400 300 Liquidus Solidus Liquidus B+L a+L Solidı 200 α 19 183 61.9 97.5 Solvus Solvus- 100 a+B Pb 20 40 60 80 Sn Weight percent tin Temperature ("C)

Refer to the composition-temperature phase diagram of solder, that is composed of lead (Pb) a tin (Sn). At the following temperature and composition, determine the mass of states a (solid sta of Pb) and B (solid state of Sn) for the solder alloy. Assuming the total mass of solder (m) to 100 g. a. Temperature = 100°C; alloy of 30% Sn and 70% Pb. b. Temperature = 200°C; alloy of 30% Sn and 70% Pb. c. Temperature = 200°C; alloy of 90% Sn and 10% Pb. What is the eutectic temperature and determine the composition where such a reaction m occur? 400 300 Liquidus Solidus Liquidus B+L a+L Solidı 200 α 19 183 61.9 97.5 Solvus Solvus- 100 a+B Pb 20 40 60 80 Sn Weight percent tin Temperature ("C)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

5 During decommissioning work, in order to determine the number of radionuclides deposited in a section of iron pipe, you grind up a small section of the pipe into a fine powder to carry out a reaction at 400 0C. Preliminary analysis shows that the predominant iron species are FeO and Fe2O3 Is it safe to use an aluminum crucible for heating your sample? What about a graphite crucible? Provide a short but detailed explanation referencing Ellingham diagrams, calculating Gibbs Free Energy, as well as provide any relevant reactions.
From the phase diagram of the Fe-0.25wt%C alloy below, determine the phase fraction and elemental composition of the resulting phase immediately after solidification across the eutectoid line (725 C). a.alpha_eutectoid = 96.6 wt% and cementite = 29.85 wt% b.alpha_eutectoid = 96.6 wt% and cementite = 3.4 wt% c.alpha_eutectoid = 1.05 wt% and cementite = 29.85 wt% d.alpha_eutectoid = 29.85 wt% and cementite = 1.05 wt%
For two hypotetical materials which have limitless solubility for both in the “liquid” and “solid” states in each other, the following data are listed. Melting Temperatures of material A and B are Tm,A and Tm,B respectively, Liquidus and Solidus curves are circular arcs. a- Draw the related “Phase Diagram” of Material A and Material B showing the data given and calculated. b- Calculate/Determine the compositions of phases at T2 , explain the procedure. c- Calculate/Determine the “percentages” of “phases” of Alloy,2 at T2 , explain the procedure. Given: -Tm,A, Celcius =530 -Tm,B, Celcius =830 -T1, Celcius =630 -B percentage of Liquid phase at T1 =35 -B percentage of Solid phase at T1 =80 -B percentage of Alloy 2. =60 -T2, Celcius =680 -B percentage of Liquid phase of Alloy 2 at T2 = to be calculated -B percentage of Solid phase of Alloy 2 at T2 = to be calculated
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.
Consider a Pb-35% Sn alloy. Determine: a) if the alloy is hypoeutectic or hypereutectic b) the composition of the first solid to form during solidification c) the amounts and compositions of each phase at 184 degrees C d) the amounts and compositions of each phase at 182 degrees C e) the amounts and compositions of each microconstituent at 182 degrees C f) the amounts and compositions of phase at 25 degrees C
Draw a PVT surface and indicate the regions where two phases coexist and label the axes
Assume that the following three phases are at equilibrium at the eutectic point. Which phase will have the highest solubility of Sn? Group of answer choices Beta Phase Alpha Phase Liquid Phase
Lead-Tin (Pb-Sn) alloys are used in soldering applications. Draw phase diagram and Distinguish between the micro-structure at composition of “Pb40%Sn” and “Pb80%Sn”.
Silicon having a melting point of 1412ºC forms an alloy with aluminum having a melting point of 660°C. The solidification temperature of the alloy is observed to be at 580°C at which the mass fraction of silicon is 0.125. Represent the liquid-solid diagram from the given data. Determine the phases present in the following conditions:
Referring to Figure 1, answer the following: What are the liquidus and solidus temperatures for an 80%Pb20%Tl alloy? What is the composition of the solid solution phase for the aforementioned alloy once we hit the liquidus temperature upon cooling? For the same alloy above, use the inverse lever rule to calculate the %solid and %liquid at 325C
Question: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.