The engineering stress-engineering strain tensile curve for a stainless steel type 304 alloy is shown. Calculate the constants K and n for the true stress and true strain curve before necking (o= K (&)"). 1000- 900- 800- 700- Engineering Stress (MPa) 8888 600 500 400 300- 200- 100- 0.0 02 0.4 Enginering Strain (mm/mm) 0.8 10

The engineering stress-engineering strain tensile curve for a stainless steel type 304 alloy is shown. Calculate the constants K and n for the true stress and true strain curve before necking (o= K (&)"). 1000- 900- 800- 700- Engineering Stress (MPa) 8888 600 500 400 300- 200- 100- 0.0 02 0.4 Enginering Strain (mm/mm) 0.8 10

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Bronze alloy, the following true stresses produce the corresponding plastic true strains, before to necking: On the basis of this information, compute the true stress necessary to produce a true strain of 0.25 and then find the engineering stress and strain at this point. True stresses (MPa) True strain 354 0121 70 018
2) Use the engineering stress strain diagram provided below to answer parts (A) to (H) below (the stress-strain diagram has already been drawn for you): stress strain diagram 400 350 0 300 0 250 0 200 0 150.0 100.0 50.0 00 0 05 01 0. 15 strain A. Determine the tensile strength of this alloy. B. show the clastic, plastic and total strain on the diagram stress (Mpa)
1. Plot the engineering stress & strain diagram of an alloy having a tensile test result found in Table 1. The tensile test specimen has a diameter of 12.5mm and a gage length of 50.0mm. The given alloy is used to make a 30.0mm diameter cylinder, which is placed inside a hardened circular steel casement with a 30.01mm inner diameter. Table 1: Tensile test results of an alloy Change In Length (mm) Change In Diameter (mm) Load (kN) 0.000 0.0000 0.0000 4.364 0.0254 0.0019 -0.0057 13.092 0.0762 21.819 0.1270 0.0095 30.547 32.729 0.1778 0.7620 34.911 3.0480 30.01 mm O F Rigid Plate Cylindrical Alloy -Steel casement Figure k Section view of the steel casement encapsulating the cylindrical alloy 2. Determine the required minimum value of F such that the cylindrical alloy would touch the walls of the steel casement.
Question A cylindrical specimen of metal having a diameter of 12.88 mm and a gauge length of 63.50 mm is tested using a tensile testing machine. The elongation measurement are recorded in Table 3. nPlot the stress-strain curve on the graph paper provided based on data in Table 3 Based on the stress-strain curved plotted in (i): Compute the modulus of elasticity Determine the yield strength at a strain offset of 0.002. Determine the tensile strength Determine the ductility in percent elongation and percent area reduction Table 3: Load-elongation readings for a metal specimen Jadual 3: Bacaan beban pemanjangan untuk statu spesimen logam) Load (N) Elongation (mm) 1380 0.03 2780 0.06 5630 0.12 7430 0.2 8140 0.25 9870 0.64 12850 1.91 14100 3.18 14340 4.45 13830 5.72 12500 6.99 Fracture
? (sigma) = 90 40 0 40 −50 0 0 0 0 MPaa. Plot the shear and normal stresses on a given oblique plane (rotated plane) on a graph (stress vs. angle) and show the max. shear plane and the principal planes. (like in the image, using excel) b.If the steel sample has a Young’s modulus of 193 GPa, compute the dimensional changes of the plate under the above loading condition. Shear moduli is 70Gpa.
a . Sketch stress strain curve if the result shown in table represent the force and extension happened in steel, and show Mechanical properties that we get from tensile test on curve? (10p)Note : Lo=80 mm , Do=10 mm , use excel to plot the curve ExtensionLoad(mm) (N)0 0.900.83 4694.341.67 4831.412.50 4781.083.33 4918.834.17 4926.585.00 5257.075.83 5437.016.66 5575.888.33 5775.189.16 5847.5210.83 5965.4111.67 6010.5312.50 6042.5713.33 6072.2614.16 6092.9315.00 6113.2416.67 6140.3617.50 6146.3718.33 6148.1419.16 6149.1725.00 5940.2125.83 5675.3326.67 4725.52b. What is meant by modulus of rigidity? if it increases what does happen to material? (2p)
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. 600 500 400 500 300 400 300E 200 3200 100 100E 0.000 0.002 0.004 0.006 Strain ol 0.00 0.16 0.20 0.08 Strain 0.04 0.12 Select one: O The tensile yield strength Sy = 290 Mpa and the maximum strength Smax = 500 Mpa. O The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 400 Mca. G The tensile yield strength Sy = 200 Mpa and the maximum strength Smax = 500 Moa. O Tne tensile yield strength Sy = 390 Mpa and the maximum strength Smax= 500 Mpa. The tensile yed strength Sy = 150 Mpa and the maximum strength Smax = 250 Mpa. Stress (MPa) Stress (MPa)
Example: Convert the change in length data in Table 3-2 to engineering stress and strain and plot a stress-strain curve Homework- help Table 3-2 The results of a tensile test of a 0.505 in. diameter aluminum alloy test bar, initial length (1o) = 2 in. Calculated LTO Load (Ib) Change in Length (in.) Stress (psi) Strain (in./in.) 0.000 1000 0.001 0.0005 4,993 14,978 24,963 34,948 37,445 39,442 39,941 39,691 37,944 3000 0.003 0.0015 5000 0.005 0.0025 7000 0.007 0.0035 7500 0.030 0.0150 7900 0.080 0.0400 8000 (maximum load) 0.120 0.0600 7950 0.160 0.0800 7600 (fracture) 0.205 0.1025
From the shear stress - shear strain diagram shown below, all the following are true except: Shear Stress (MPa) 500 450 400 350 300 250 200 150 100 50 0. 0.2 0.4 0.6 0.8 1.2 1.4 1.6 1.8 Shear Strain (rad) Shear Stress-Strain Curve for Brass Select one: O a. Shear stress and Shear strain are 430 MPa and 1.72 rad at fracture. O b. Shear stress and Shear strain are 250 MPa and 0.05 rad at Yielding. Oc. The elastic zone ends at a shear stress of 400 MPa and shear strain of 1 rad Od. The ultimate Shear stress and Shear strain are 430 MPa and 1.72 rad.
Use the engineering stress strain diagram provided below to answer parts (A) to (H) below (the stress-strain diagram bas already been drawn for you): stress strain diagram 400 350 0 300 0 250 0 200 0 150.0 100.0 50.0 O 05 0 1 0.15 strain A. Determine the tensile strength of this alloy. B. show the elastic, plastic and total strain on the diagram stress (Mpa)
For a steel sample under tensile testing, if the first principal strain was equal to 0.005 and all other principal strain components are zero. If steel has a Lame's constant of 100 MPa and Shear Modulus of 10 MPa. If we plotted the stress-strain curve of this test. What is the area under this curve? Select one: O a. 1500 MPa O b. 1500 kPa 3. O C. 1500 Joule/m O d. 1500 Joule/m O e. NONE