The figure below shows a hypothetical binary eutectic phase diagram on which we indicate an alloy composition of 27% B. Calculate the following quantities: a. Fraction of primary solid that forms under equilibrium cooling at eutectic temperature b. Fraction of liquid with the eutectic composition that will transform to two solid phases below the eutectic isotherm c. The amount of a and ß that will form from the liquid just below the eutectic isotherm. L+B L+a B a 20 37 73 27 a +B

The figure below shows a hypothetical binary eutectic phase diagram on which we indicate an alloy composition of 27% B. Calculate the following quantities: a. Fraction of primary solid that forms under equilibrium cooling at eutectic temperature b. Fraction of liquid with the eutectic composition that will transform to two solid phases below the eutectic isotherm c. The amount of a and ß that will form from the liquid just below the eutectic isotherm. L+B L+a B a 20 37 73 27 a +B

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a binary phase diagram ( pressure omitted) what is the maximum number of phases that can coexist for at least one degree of freedom?
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…
Given a blank phase diagram, label the solid, liquid, and gas phases for a pure substance. Give the approximate temp. and pressure of the triple point, and determine what the substance's phase would be at a given temperature and pressure. Can you provide an example?
For the metals A and B, which are given below, create the hypothetical phase diagram between 500 ° C and 900 ° C temperatures.Ø A metal has a melting temperature of 840 ° C.The solubility of Ø B in A can be ignored at all temperatures.Ø Melting temperature of Metal B is 730 ° C.The maximum solubility of A in Ø B is 10% A by weight, which occurs at 600 ° C.At 500 ° C, the solubility of A in B is 6% A by weight.Ø An eutectic 600 ° C and 74% B by weight - 26% by weight A are formed.Ø The second eutectic occurs at 630 ° C and 59% B - 41% A by weight.Ø A third eutectic occurs at 655 ° C and 39% B - 61% A by weight.Ø A congress melting point is formed at 680 ° C and 52% B - 48% A by weight.Ø A second congress melting point is formed at 655 ° C and 66% B - 34% A by weight.Ø Intermetallic compound AB is present at 52 wt% B - 48 wt% A.Ø Intermetallic compound AB2 is present at 66 wt% B to 34 wt% A.
Question: Construct the hypothetical phase diagram for metals A and B between room temperature (20°C) and 700°C given the following information: The melting temperature of metal A is 480°C. The maximum solubility of B in A is 4 wt% B, which occurs at 420°C. The solubility of B in A at room temperature is 0 wt% B. One eutectic occurs at 420°C and 18 wt% B–82 wt% A. A second eutectic occurs at 475°C and 42 wt% B–58 wt% A. The intermetallic compound AB exists at a composition of 30 wt% B–70 wt% A, and melts congruently at 525°C. The melting temperature of metal B is 600°C. The maximum solubility of A in B is 13 wt% A, which occurs at 475°C. ● The solubility of A in B at room temperature is 3 wt% A.
Use the phase diagrams for Cu-Ni and Cu-Ag systems below to answer the question: Based on the mechanism, would you expect a solution containing 80 wt% Cu to be stronger if the remaining 20% of the alloy was Ni or Ag? Briefly explain
Describe the phases present at the eutectic temperature when the overall composition is x(Cu)= 0.5
Using the Ti-Cu phase diagram, if you start with 100 kg of a Ti-Cu mixture at 3000C and 10 wt. % Cu and cool down very slowly to point D (500 C), determine what phases are present at each letter, determine the compositions for each phase, and determine theweight in each phase. Point D): Phase(s) present Weight % of Cu in each phaseWeight of each phase
For the Pb-Sn phase diagram showing incomplete solid solution, which of the Hume-Rothery rules are violated.
Using the Mg-Pb phase diagram below, if you start at point A and cool down very slowly to room temperature (point D), sketch the microstructure associated with each letter, determine what phases are present at each letter, determine the compositions for each phase, and determine the weight in each phase. The Mg-Pb mixture has 20 wt. % Pb in it. You start with 100 kg.
10.27 A hypothetical A-B alloy of composition 55 wt% B-45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both a and 8 phases. If the composition of the B phase is 90 wt B-10 wt% A, what is the composition of the a phase?
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)