The metal rubidium has a BCC crystal structure. If the angle of diffraction for the (321) set of planes occurs at 27.00 degrees (first-order reflection) when monochromatic x-radiation having a wavelength of 0.0711 nm is used, compute the interplanar spacing for this set of planes. Final answer in 4 decimal and in nm.

The metal rubidium has a BCC crystal structure. If the angle of diffraction for the (321) set of planes occurs at 27.00 degrees (first-order reflection) when monochromatic x-radiation having a wavelength of 0.0711 nm is used, compute the interplanar spacing for this set of planes. Final answer in 4 decimal and in nm.

University Physics Volume 3

17th Edition

ISBN:9781938168185

Author:William Moebs, Jeff Sanny

Publisher:William Moebs, Jeff Sanny

Chapter4: Diffraction

Section: Chapter Questions

Problem 76P: On a certain crystal, a first-order X-ray diffraction maximum is observed at an angle of 27.1°...

See similar textbooks

Similar questions

The structure of the NaCl crystal forms reflecting planes 0.541 nm apart. What is the smallest angle, measured from these planes, at which X-ray diffraction can be observed, if X-rays of wavelength 0.085 nm are used?
On a certain crystal, a first-order X-ray diffraction maximum is observed at an angle of 27.1° relative to its surface, using an X-ray source of unknown wavelength. Additionally, when illuminated with a different, this time of known wavelength 0.137 nm, a second-order maximum is detected at 37.3°. Determine (a) the spacing between the reflecting planes, and (b) the unknown wavelength.
An electric current through hydrogen gas produces several distinct wavelengths of visible light. What are the wavelengths of the hydrogen spectrum, if they form first-order maxima at angles 24.2°, 25.7°, 29.1°, and 41.0° when projected on a diffraction grating having 10,000 lines per centimeter?
Reflections from the {110} planes of barium titanate, BaTiO3, which has a tetragonal crystalline structure, were observed at glancing angles of 9.13° with Co Ka radiation of wavelength 179 pm. What is the value of the unit cell parameter a?
Monochromatic x-rays (λ = 0.166 nm) from a nickel target are incident on a potassium chloride (KCl) crystal surface. The spacing between planes of atoms in KCl is 0.314 nm. At what angle (relative to the surface) should the beam bedirected for a second-order maximum to be observed?
In the figure, first-order reflection from the reflection planes shown occurs when an x-ray beam of wavelength 0.820 nm makes an angle θ = 62.3˚ with the top face of the crystal. What is the unit cell size a0?
Potassium chloride (KCI) has a set of crystal planes separated by a distance of d= 0.34 nm. At what glancing angle 0 to these planes would the first-order Bragg maximum occur for X-rays of wavelength 0.05 nm?
The interplanar distance of (101) plane of ZnO crystal is 0.45 nm. If the first-order diffraction maximum is observed at an incidence angle of 36.2°, what is the wavelength of the X-ray scattering from this crystal? And estimate the crystallite size of the ZnO nanomaterial if FWHM of (101) plane is 2.51° (degree to radian Degree x T/180) and k = 0.9.
A bubble is formed by a soap film with index of refraction n=1.3 and a thickness of 325nm. When illuminated by white light and viewed directly (perpendicular to the surface), what wavelength in the visible spectrum (375nm to 725nm) will be strongly reflected?
If a light with a wavelength of 391.7 nm is used to illuminate a double grating system with a separation of 4.3 μm, what is the greatest number of maxima that this assembly can produce under these conditions? (remember that sinθ ≤ 1).
an x-ray beam of wavelengths from 95.0 to 140 pm is incident at u = 45.0° to a family of reflecting planes with spacing d= 275 pm.What are the (a) longest wavelength l and (b) associated order number m and the (c) shortest l and (d) associated m of the intensity maxima in the diffraction of the beam?
Prove that it is not possible to determine both wavelength of incident radiation and spacing of reflecting planes in a crystal by measuring the Bragg angles for several orders.