The stress-strain curves of materials A, B and C are given in Figure. Answer the questions according to curves.a.Stress (MPa)C.140012001000Stress (MPa)80060040020000.po12001000800600400200O0.0000.002 0.0040.006 0.0080.10Strain0.010StrainRank the materials from most ductile to most brittle.0.150.012 0.014Calculate the modulus of elasticity in GPa of each material0.20сb. Determine the tensile strength of each material. Show your work on the stress-strain curve.0.016 0.018 0.020

The material C has highest yield stress. Hence, it is the strongest material but most brittle one.…

a. Rank the materials from most ductile to most brittle. b. Determine the tensile strength of each material. Show your work on the stress-strain curve. C. Calculate the modulus of elasticity in GPa of each material

a. Rank the materials from most ductile to most brittle. b. Determine the tensile strength of each material. Show your work on the stress-strain curve. C. Calculate the modulus of elasticity in GPa of each material

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The stress-strain diagram of a reinforcement steel having a cross-sectional diameter of 12 mmdiameter and 100 mm gage length is determined after its tensile strength test as follows. Based on the stressstrain diagram determine the followings properties of the material (Poisson’s ratio of the material is 0.32) : a) Modulus of elasticityb) Yield strengthc) Toughnessd) Resiliencee) Shear modulusf) Bulk modulusg) Ductility as described bypercent change in length
Determine the percentage of ductility of a metal alloy having the following tensile stress-strain diagram. 600 500E 400 500 300 400 300 200 100 100 0.000 0.002 0.004 0.006 Strain 0.00 0.04 0.08 0.12 0.16 0.20 Strain Select one: O 0.6% O 19% O 4% 300% O 10% Stress (MPa) O O O O Stress (MPa)
Draw the tensile curves of the following materials, taking into account the appropriate elongation at break, modulus of elasticity and tensile stress, on the side stress-strain graph. a)Low carbon steel (Ecelik=200Gpa),(Syield=300MPa),(Stensile=400MPa) b)High carbon steel (Esteel=200GPa),(Stensile=700MPa) c)Aluminum (Ealuminum=70GPa), (Syield=200MPa),(Stensile=300MPa) d)Cast iron (Ecast iron=120GPa),(Stensile=200MPa)
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
The state of in-plane stress at a point on an element of material is shown. Let |σx| = 370 MPa, |σy| = 130 MPa, and |τxy| = 85.0 MPa. Use this information to represent the state of stress of the same point that is rotated through an angle of θ = 25.0.
Choose the correct answer Stress divided by Rate of strain is: d. Velocity a. Surface tension f. Kinematic viscosity b. Density e. Dynamic Viscosity c. Unit less
a . Sketch stress strain curve if the result shown in table represent the force and extension happened in steel, and show Mechanical properties that we get from tensile test on curve? (10p)Note : Lo=80 mm , Do=10 mm , use excel to plot the curve ExtensionLoad(mm) (N)0 0.900.83 4694.341.67 4831.412.50 4781.083.33 4918.834.17 4926.585.00 5257.075.83 5437.016.66 5575.888.33 5775.189.16 5847.5210.83 5965.4111.67 6010.5312.50 6042.5713.33 6072.2614.16 6092.9315.00 6113.2416.67 6140.3617.50 6146.3718.33 6148.1419.16 6149.1725.00 5940.2125.83 5675.3326.67 4725.52b. What is meant by modulus of rigidity? if it increases what does happen to material? (2p)
Define the given terms related to mechanical properties of materials. 1. elastic material 2. Apparent Viscosity 3. Bend test 4. Bingham Plastic 5. Dilatant
Given the following stress-strain graph:a. is the modulus of elasticity of "A-514" greater, less or equal to the one of "A-572"?b. from the previous question, make an estimatio for both of them, check that the graphic comes in %c. If we were to test these materials in a universal tension equipment, which one would withstand more load?d. If we were to test these materials in a universal tension machine, which one would elongate the most before fracturing? would elongate the most before fracturing? e. Of the 6 materials shown, do any behave as brittle materials? f.
In a forming process the diameter of the specimen is 1 cm and its length changes from 50 mm to 60 mm. Show the maximum force value on the graph of Force vs. True Strain plotted in Excel Program or any plotting program not by hand using the flow stress equation given below. σ= Kεn and σ=F/A Where the parameters are σ : True Stress in MPa K: Strength Coefficient, K=210 in MPa ε : True Strain, ε=ln (l/l0) n: Strain Hardening Exponent, n=0.27 F: Force in 10 A : Area in mm2 Take at least 3 digits after the decimal point. Specify the units. You can use Excel or any plotting program not by hand then paste your graph into the solution section.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 157 kN. - Length of the specimen is 23 mm. - The yield strength is 89 kN/mm2. - The percentage of elongation is 45 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 18 kN, iv) Young's Modulus if the elongation is 1.3 mm at 18 kN and (v) Final diameter if the percentage of reduction in area is 25 %. Solution: Initial Cross-sectional Area (in mm2) The Diameter of the Specimen (in mm) Final Length of the Specimen (in mm) Stress at the elastic load (in N/mm2) Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
The following data (in given figure) were obtained from the tensile test of Aluminum alloy. The initial diameter of test specimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.