10. The following results were obtained in a tensile test on a mild steel specimen of original diameter 20 mm and gauge length 40 mm. Load at limit of proportionality 80 kN Extension at 80 kN load 0.048 mm 85 kN Load at yield point Maximum load 150 kN When the two parts were fitted together after being broken, the length between gauge length was found to be 55.6 mm and the diameter at the neck was 15.8 mm. Calculate Young's modulus, yield stress, ultimate tensile stress, percentage elongation and percentage [Ans. 213 kN/mm²; 270 N/mm²; 478 N/mm²; 39%; 38%] reduction in area.

10. The following results were obtained in a tensile test on a mild steel specimen of original diameter 20 mm and gauge length 40 mm. Load at limit of proportionality 80 kN Extension at 80 kN load 0.048 mm 85 kN Load at yield point Maximum load 150 kN When the two parts were fitted together after being broken, the length between gauge length was found to be 55.6 mm and the diameter at the neck was 15.8 mm. Calculate Young's modulus, yield stress, ultimate tensile stress, percentage elongation and percentage [Ans. 213 kN/mm²; 270 N/mm²; 478 N/mm²; 39%; 38%] reduction in area.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
Calculate the values of Poisson’s ratio of a rod under uniaxial tensile test. Initially it has 15.5 mm diameter and 62 mm gauge length, then it changes to 15.415 mm diameter and 62.102 mm gauge length under a load of 20 kN.a) 0.186 b) 0.242 c) 0.259 d) 0.342
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation. use correct stratgy and correct E 0.55962
40)A tensile test specimen has a gage length=3.0 inches and a diameter= .75 inches. Yielding occurs at a load of 38000lbs. The corresponding gage length=3.0103 inches (neglect the .0.2% yield point). The maximum load of 54000lbs i9s reached at a gage length =3.453 inches. If the specimen necked down to a diameter=.645 inches, determine the percent reduction in area (Round to the nearest whole %)
A) An engineer works for a company that has many gray cast iron rods of different diameters and would like to design an equivalent rod that could handle a force of P= 10.0 kipkip without fracturing. What is the minimum diameter that this new rod must have to support P? B)A tensile test is being conducted on a steel-rod specimen with a gauge length of L0 = 4.0 in and an initial diameter of d0 = 0.75 in. If the final length of the rod at fracture is Lf= 5.53 in , find the percent elongation of the rod at fracture.
38)A tensile test specimen has a gage length=3.0 inches and a diameter= .75 inches. Yielding occurs at a load of 38000lbs. The corresponding gage length=3.0103 inches (neglect the .0.2% yield point). The maximum load of 54000lbs i9s reached at a gage length =3.453 inches. Determine the tensile strength (Round to the nearest whole ksi)
A test rod of rust-resistant steel, with a diam. of 12.8 mm and a measuring length of 50.8 mm is subjected to a tensile test. The data from the test is shown in the table below.
39) A tensile test specimen has a gauge length=2in. and a diameter of 0.875in. Yielding occurs at a load of 35,500lbs. The corresponding gauge length = 2.0113in. (neglect the .2% yield point). The maximum load of 45,000lbs is reached at a gauge length of 2.543in. If fracture occurs at a gauge length of 2.673in, determine the percent elongation at fracture (Round to the nearest whole %)
A routine quality control test is made on a structural steelbar that is 1 in. square and 16 in. long. The data developed during the testshow that the bar elongated 0.0111 in. when subjected to a tensile force of20.5 kips. Compute the modulus of elasticity of the steel.
The following data were obtained from a standard tensile stress test on a mild steel specimen. Graph the result and determine proportional limit stress and Young’s Modulus.