5. For which set of crystallographic planes will a first-order diffraction peak occur at a diffraction angle of 46.21° for BCC iron when monochromatic radiation having a wavelength of 0.0711 nm is used?

5. For which set of crystallographic planes will a first-order diffraction peak occur at a diffraction angle of 46.21° for BCC iron when monochromatic radiation having a wavelength of 0.0711 nm is used?

Chemistry: The Molecular Science

5th Edition

ISBN:9781285199047

Author:John W. Moore, Conrad L. Stanitski

Publisher:John W. Moore, Conrad L. Stanitski

Chapter9: Liquids, Solids, And Materials

Section: Chapter Questions

Problem 74QRT

See similar textbooks

Related questions

Q: An Echellette grating has 2336 lines/mm. What diffraction line (in nm) would be observed at an angle…

A: Given the angle of incidence is 430 and the angle of reflection is 50

Q: Figure below shows the first four peaks of the x - ray diffraction pattern for copper, which has a…

Q: 25) X-ray diffraction (XRD) is an analytical method of studying solids. Find the identity of an…

Q: A crystal is known to have a face-centered (F-centering) cubic unit cell. The fractional coordinate…

A: There are four possible coordinator --- 1) (-0.5,0.5,1.5) 2) (-0.5,1,-0.5) 3) 0.5,0.5,0.5) 4) (1/2,…

Q: Calcium carbonate crystals in the form of aragonite have orthorhombic unit cells of dimensions…

Q: (a) Mark the sites in the unit cell. b (b) List the Miller indices of all the octahedral…

A: In case of FCC, there are 4 atoms. Therefore, there are 4 octahedral voids.

Q: A solid sample Niobium is composed of 1.24x10^21 BCC unit cells. What is the volume of the solid…

A: Atomic radius of Nb = 143 pm Conversion of pm into cm: 1 pm =10-10 cm143 pm =143×10-10cm

Q: 20. A unit cell has the dimensions a = 4 A, b= 6 A, c = 8 A, x = ß = 90°, y = 120°. Determine: a)…

Q: a) A solid substance is considered to be orthorhombic in nature. Since the edges of the unit cell…

A: The d is the interplanar spacing and it is defined by the spacing between the adjacent planes which…

Q: (e) Platinum has an FCC crystal structure. The atomic radius of platinum is 0.1387 nm. An X-ray…

A: The diffraction of X-rays from crystal surface follow Bragg's equation, nλ=2dsinθn=order of…

Q: The cell parameters and lattice angles for the tetragonal a = 3.785 Å a = 90* %3D b = 3.785 Å B =…

A: Solution -

Q: Q4: In the calcium fluorite. CaF2 structure, atoms occupy the position of % % %, which is not filled…

Q: The angle of a Bragg reflection from a set of crystal planes separated by 99.3 pm is 20.85°.…

Q: 3.47 Determine the Miller indices for the planes shown in the following unit cell: +z 1 2 В A >+y 2…

Q: 3.36 (a) What are the direction indices for a vector ● that passes from point 11 to point 01; in a…

Q: Potassium nitrate crystals have orthorhombic unit cells of dimensions a = 542 pm, b = 917 pm, and c…

A: From the question, we obtain that- Potassium nitrate crystals have orthorhombic unit cells a = 542…

Q: 0.58 oA x-ray wavelength is used to calculate the d200 distance of nickel. The diffraction angle ɵ…

A: This question is given from solid state, so as given data given Wavelength , interplanar distance ,…

Q: In an x-ray diffraction measurement of BCC Nb, the observed angle (2Θ) for the (211) set of planes…

Q: A solid is thought to have an orthorhombic structure. Calculate the positions D and 2θ for the plane…

A: Interpretation- To calculate the position D and 2θ for the plane 111 expected in the diffraction…

Q: Based on the volumes calculated in the previous question and the picture below, calculate the edge…

A: 1 pm = 1x10-10 cm = 1x10-12 m since, 1 m =100 cm1m3 = 106 cm3For a body centered cubic unit…

Q: is thought that a solid substance has an orthorhombic structure. Since the edges of the unit cell…

A: Welcome to bartleby !

Q: What is the main factor in not observing the glass transition behavior in highly cross-linked and…

A: Glass transition behavior in highly cross-linked and highly crystalline polymers.

Q: A. Determine the Fhkl Factor of the ionic crystal NaCl, assuming the scattering factors for Na and…

Q: (a) What kind of packing arrangement is seen in the accompanyingphoto? (b) What is the coordination…

A: (a) In the given photo, each ball in the first layer touches six neighboring balls. The balls in the…

Q: 1. For FCC (face-centered cubic) platinum (Pt, having an atomic radius of 0.1387 nm), determine the…

A: Given Type of Structure = FCC Atomic Radius ( R )= 0.1387 nm Plane = ( 3 1 1 ) Wavelength =…

Q: The ratio of first nearest neighbor distance of .4 the body-centered (bcc) to that of face-…

Q: b) Calculate the atomic packing factor for a metal that has a cubic unit cell with a lattice…

A: A unit cell is the regular repeated three-dimensional arrangement that makes up he entire lattice.…

Q: Explain and discuss the difference between the 2-Dimensional and 3-Dimensional structure of…

A: We have to Explain and discuss the difference between the 2-Dimensional and 3-Dimensional structure…

Q: A crystalline sample has a diffraction peak at 17.2°. What is the corresponding d space in pm?…

A: Using Bragg's Law we Can solve this problem and calculate the value of 'd'

Q: 5. a. Would you expect Frenkel defects for anions to exist in ionic ceramics in relatively large…

Q: a) It is considered that a solid substance has an orthorhombic structure, Since the edges of the…

Q: The unit cell for tin has tetragonal symmetry, with a and blattice parameters of 0.5 and 0.318 nm,…

Q: A crystal was analyzed using X-ray diffraction with radiation Element a (pm) from an iron source.…

Q: Since the edges of the unit cell are a = 3.50Å, b = 4.0 Å, c = 5.5 Å, calculate the d and 2θ…

A: Answer Calculate miller index from plane intersecting the crystal…

Q: Which of the following statements are true? a) all polymers have a crystalline melting point b)…

A: given find true statements

Q: Calculate a value for the atomic radius of a chromium atom with a coordination number of 12 given…

A: Given that the crystal lattice is a bcc-centered cubic. The volume of a unit cell in bcc can be…

Q: Cinnabar (HgS) was utilized as a pigment known as vermillion.It has a band gap of 2.20 eV near room…

A: Given , Band gap = 2.20 eV If E is the corresponding photon energy then,…

Q: (a) What kind of packing arrangement is seen in the accompanyingphoto? (b) What is the coordination…

A: Coordination number is the number of ions, atoms or molecules that a central atom or ions holds…

Q: Elemental silver reflects X-rays of wavelength 154.18 pm at angles of 19.076°, 22.171°, and 32.256°.…

Q: A crystalline sample has a diffraction peak at 15.6°. What is the corresponding d space in pm?…

A: n = 1 wavelength = 90.1 pm theta = 15.6 degree d =? pm

Q: A crystal of FeO was found to have a unit cell dimension of 4.501Å, a measured density of 5.828…

A: Solution : We can determine the defect in the sample of non-stoichiometric compounds. This can…

Q: A crystal is known to have a body-centered (I-centering) cubic unit cell. The fractional coordinate…

Q: Three-dimensional hexagonal boron nitride is made up of sheets of the two- dimensional material…

A: B2H6 + NH3 (excess) → (BN)x boron nitride

Q: Q1- Choose the correct answer for the following (Justify your answer): 1-The direction indices for…

A: A). the Direction indices for the cryptographic direction indicated by the vectors [1,1,1]. OPTION…

Q: Which type of magnetic material cannot be used to makepermanent magnets, a ferromagnetic substance,…

A: Permanent Magnets A magnet that retains its magnetic properties in the absence of an inducing field…

Q: Calculate the packing efficiencies of sodium chloride and zinc blende. (Radii of ions: four…

Q: Sketch the Miller plane in a unit cell (0-1-3)

A: The miller indices can be evaluate through the reciprocal of unit cell.

Question

100%

5. For which set of crystallographic planes will a first-order diffraction peak occur at a
diffraction angle of 46.21° for BCC iron when monochromatic radiation having a
wavelength of 0.0711 nm is used?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, chemistry and related others by exploring similar questions and additional content below.

Similar questions

What is the first-order scintillation angle of the shimmering x-rays of a crystal surface with a distance between planes of 0.204 nm and a wavelength of 0.154 nm.
I) Diamond crystallises in a face-centred cubic structure with a = 3.5625 Å. Calculate the d-spacing and peak position of the first allowed peak (i.e. the peak with the lowest hkl value that meets the selection rules) using a wavelength of 0.71073 Å. II) A solvothermal synthesis gave rise to a mixture of two crystalline phases: one phase consists of 50-65 μm octahedral crystallites while the other phase consists of 150-180 μm hexagonal plates. Identify a separation technique that would likely be effective in separating these materials.
13. Explain the relationship between chain symmetry and density of polymers.
Given caesium has a body-centred cube with density of 1.93 g/cm3. i. Determine the lattice constant of caesium if the molar mass of caesium is 132.9 g mol-1. (NA = 6.022 x 1023 atom mol-1) ii. Assuming the body-centred caesium is replaced by an anion, X, suggest the type of structure of this derivative. iii. Determine coordination environment for both ions.
Knowing that the crystal spacing of the monochromator [Topaz crystal (303) ] has an interplanar distance of 0.1356 nm, calculate the limits of the wavelengths within which it is possible to record the spectrum if the angle of incidence is (2q =10º and 2q =160º )
What are the main advantages and limitations of the Valencia Linkage Theory?
State the Miller indices of the planes that intersect the crystallographic axes at the distances (−a, 2b, −c) and (a, 4b, −4c).
Which type of magnetic material cannot be used to makepermanent magnets, a ferromagnetic substance, an antiferromagneticsubstance, or a ferrimagnetic substance?
show that the atomic packing factor for BCC is 0.68 and forHCP is 0.74.
Using a simple infinite barrier approximation, calculate the “effective bandgap” of a 10 nm GaAs/AlGaAs quantum well grown along [001] direction. If there is a one-monolayer fluctuation in the well size, how much will the effective bandgap change? This example gives an idea of how stringent the control has to be in order to exploit heterostructures.
Suppose you have collected the X-ray powder diffraction pattern of tetragonal BaTiO3 at roomtemperature using copper radiation (λ=1.54 Å) and identified the lattice planes corresponding to thepeaks at each 2θ positions, as shown in the table below. 2θ (°) (hkl) Intensity (%)22.05 (001) 12.022.28 (100) 25.031.45 (101) 100.031.65 (110) 100.038.82 (111) 46.044.86 (002) 12.045.39 (200) 37.050.60 (102) 6.050.98 (201) 8.051.3 (210) 7.056.01 (112) 15.056.3 (211) 12.065.75 (202) 35.0 Determine:a) the d-spacing of the four most intense reflections; b) the lattice parameters a, b and c of the unit cell.
1) For a crystalline substance with a hexagonal unit cell, the distance interplanar d is given by the expression. Consider graphite, for which a = 0.247 nm and c = 0.679 nm. On a standardized diffractogram with Cu Kα radiation ((λ = 1.5418 Å)), where angle 2θ will be observed the Bragg 002 peak of graphite?