(6) The weldment shown in the figure is subjected to an alternating force F. The hot-rolled steel bar is 10 mm thick and is of AISI 1010 steel. The vertical support is likewise of 1010 steel. The electrode is 6010. Estimate the fatigue load F the bar will carry if three 6-mm fillet welds are used. (As 22.1 kN) 50 |--60-→- D

(6) The weldment shown in the figure is subjected to an alternating force F. The hot-rolled steel bar is 10 mm thick and is of AISI 1010 steel. The vertical support is likewise of 1010 steel. The electrode is 6010. Estimate the fatigue load F the bar will carry if three 6-mm fillet welds are used. (As 22.1 kN) 50 |--60-→- D

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter8: Applications Of Plane Stress (pressure Vessels, Beams, And Combined Loadings)

Section: Chapter Questions

Problem 8.2.9P: A spherical tank of diameter 48 in. and wall thickness 1.75 in. contains compressed air at a...

See similar textbooks

Similar questions

A plate 100 mm wide and 12.5 mm thick is to be welded to another plate by means of parallel fillet welds. The plates are subjected to a load of 50 kN. Find the length of the weld so that the maximum stress does not exceed 56 MPa. Consider the joint first under static loading and then under fatigue loading.
A welded joint, as shown in figure below, is subjected to an eccentric load of 2500 N. Find thesize of the weld, if the maximum shear stress in the weld is not to exceed 50 N/mm2
appropriate length of the weld joint shown in the figure if the force is equal to (60000lb) and the operating stress value is (60ksi) and the size of the weld is (1/4in).
(1) What are the methods used to obtain a good weld when welding steel when the carbon content is high? b) Find the appropriate size and length for the weld joint shown in the figure if the strength is equal to (70000Ib) and the allowable shear stress value is 40ksi and the weld rib dimension is (1/4in)
The carrier plate material St52 (S355) given in the figure below is welded to the body. combined. F1 = 4 kN and F2 = 40 kN static forces act on the plate. Source I. Quality (v2 = 1), no impact (v3 = 1), weld thickness a = 5 mm, safety coefficient s = 2 and weld seam coefficient v1 = 0.8 will be taken. Find out whether a = 5 mm weld seam thickness is sufficient or not, according to the data in the figure and above.
I need right solution with clear calculations. Two steel plates having yield point stress of 350 N/mm2 are joined together by double fillet welds of 10 mm thick as shown in figure. The weldment is from the same parent plate material. If the weld has to be replaced by 3 bolts of the same material, one each at A and B and one at mid-way between C and D, design the bolts. Take factor of safety as 2 for the bolts
A bracket is as shown in figure 2. Determine the uniform weld size for the arrangement. The permissible shear stress of weld material is 80 MPa. Consider the loading condition as shown in figure.
A beam is supported and loaded as shown in the figure. Data: L = 1000 mm, c = 300 mm, f = 100 mm, D = 100 mm, d = 80 mm. The beam consists of different parts that are welded, and the fillet weld size a is 4 mm. The load q is 2 kN/m, and P = 10 kN. Calculate the maximum stress in the welds.
A rectangular steel plate is welded as a cantilever to a vertical column and supports a single concentrated load P. Determine the weld size if shear stress in the same is not to exceed 140 MPa
All-round fillet weld with a steel beam weld thickness a=6 mm and weld seam length shown in the figure welded to the steel column. Forces of 2 kN and 3 kN from the beam end in the horizontal and vertical directions, respectively has been applied. The smallest yield strength of the weld material so that the steel structure has a safety of 2.5. Calculate according to von Mises static damage theory ?
Question: a) A plate 100 mm wide and 10 mm thick is to be welded to another plate by means of double parallel fillets. The plates are subjected to a static load of 80 kN. Find the length of weld if the permissible shear stress in the weld does not exceed 55MPa. Determine the increase in load carrying capacity if a combination of single transverse double parallel fillet is used the permissible tensile strength of material is 80MPa. b) Draw a neat sketch of double riveted double cover but joint. If 8mm plates with 20 mm diameter rivets having a pitch of 50 mm are joint using double riveted lap joint. The permissible stresses are permissible tensile stress = 120 MPa;Permissible crushing stress= 100 MPa; Permissble shear stess= 150 MPa. Find the strengths and efficiency of joint, taking the strength of the rivet in double shear acoording to the indian boiler standards.
a. figure 1 shows a large pressure vessel fabricated by welding together steel plates of 12 mm thickness as shown. If the stress acting normal to the welds must be less than 80 MPa, what is the largest allowable internal pressure? b. determine the state of strain in the tank when the internal pressure is 0.3 MPa. The elastic modulus (?) of the steel is 200 GPa, and the Poisson’s ratio (?) is 0.3. c. The welded joints are to be replaced with equally spaced rivets (loaded in single shear), each with a diameter of 10 mm and maximum allowable stress of 80 MPa. For an internal pressure of 0.3 MPa inside the tank, determine: (i) The minimum rivet spacing (?) along the circumference of the tank. (ii) The minimum rivet spacing (?) along the height of the tank. d. If the pressure vessel is subjected to a temperature change of 50°C determine the change in height. The co-efficient of thermal expansion for steel can be taken as ? = 11.2 × 10−6 °C−1.