7.32 (a) What is the approximate ductility (%EL)e of a brass that has a yield strength of 345 MPa(50,000 psi)?(b) What is the approximate Brinell hardness ofa 1040 steel having a yield strength of 620 MPa(90,000 psi)?

(a) A yield strength of 345 MPa (50,000 psi) for brass corresponds to 20 %CW. A brass that has been…

Answered: 7.32 (a) What is the approximate…

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

How does the carbon content in plane carbon steels affect the fracture toughness? Show this influence by A7 curves.
An application requires ultimate tensile strength and yield strength ofa steel at 110 ksi and 91 ksi, respectively. Answer the following 4 questions:4.1. Can SAE 1040 steel be selected for this application?4.2. If “no” is the answer in Part I, the following Part II, III, and IV can beignored. If “yes” is the answer in Part I, which condition of SAE 1040 shouldbe selected?4.3. Why is that steel with the condition in part II selected?4.4. Is the selected steel brittle or ductile? and Why?
In the flow curve for pure aluminum, the strength coefficient = 175 MPa and strain-hardening exponent = 0.20. In a forming operation, the final true strain = 0.75. Determine a) the flow stress and b) average flow stress that the metal experienced.
A cylindrical specimen of a cold-worked brass has a ductility (%EL) of 21%. If its cold-worked radius is 14 mm, what was its radius before deformation?
Explain the connection between notch strengthening and material ductility; which is more likely to notch strengthen––pure Al or martensitic steel?
The annealed low carbon steel behavior is approximated by σ = 10000ε 0.25 MPa. Evaluate (a) The yield strength after the bar is cold worked for __%. (b) If the same annealed low carbon steel bar is initially cold worked __%, followed by additional cold work of __%, determine the probable yield strength of the final bar. (c If the same annealed low carbon steel bar was cold worked for an unknown amount and then cold worked 20% more and found to have a yield strength of __ MPa. What was the unknown amount of cold work. (d) Discuss the variation of yield stress in question a & b. (e) Discuss the effect of mechanical working on variation of properties with respect to grain size. Also draw a clear graph of properties versus grain size for ductility and strength. σ = 10000ε 0.24 (a) 30% (b) initially 15% followed by 20% (c) yield strength of 7500 MPa
3000 kg, 10mm Steel Ball Brinell Hardness Reading of 421 is equal to what Rockwell C Reading?
Draw with neat sketch the stress–strain behavior of steel, and identify different levels of strength. Explain with typical graph about the effect of increasing the carbon content in steel?
Draw a stress-strain curve for a low carbon steel and explain important points and regions in detail. What fracture behavior does this steel exhibit?
Please elaborate the following: Typical stress-strain characteristics of steel in simple tension and the evaluation of its mechanical properties .
As the tempering temperature of a heat treated steel increases the associated values of Brinnell hardness also increase, while the values of tensile strength and yield strength decrease. True or false
Q24. What is toughness of a material? Is it the same as hardness? Is it also measured in pascals? 3 Q25. What is brittle transition temperature? 2 Q26. What is the risk of using steels at temperatures above 350O?

SEE MORE QUESTIONS

Recommended textbooks for you

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Control Systems Engineering

Mechanical Engineering

ISBN:

9781118170519

Author:

Norman S. Nise

Publisher:

WILEY

Mechanics of Materials (MindTap Course List)

Mechanical Engineering

ISBN:

9781337093347

Author:

Barry J. Goodno, James M. Gere

Publisher:

Cengage Learning

Engineering Mechanics: Statics

Mechanical Engineering

ISBN:

9781118807330

Author:

James L. Meriam, L. G. Kraige, J. N. Bolton

Publisher:

WILEY

SEE MORE TEXTBOOKS

7.32 (a) What is the approximate ductility (%EL) of a brass that has a yield strength of 345 MPa (50,000 psi)? (b) What is the approximate Brinell hardness of a 1040 steel having a yield strength of 620 MPa (90,000 psi)?