(a) A bar AISI 1035 steel forged and heat treated with minimum yield strength of_MPa is subjected to bending moment of _Nm and a torsional moment of Nm. Assuming a factor of safety of 2, determinethe diameter of rod using thefollowing theories of failure (i) Maximum Shear stresstheory and (ii) Distortion Energy theory (ii) Maximumstresstheory, alsospecifywhich diameter is considered as safe yield strength = 555MPA bending moment = 285NM torsional moment = 315NM

(a) A bar AISI 1035 steel forged and heat treated with minimum yield strength of_MPa is subjected to bending moment of _Nm and a torsional moment of Nm. Assuming a factor of safety of 2, determinethe diameter of rod using thefollowing theories of failure (i) Maximum Shear stresstheory and (ii) Distortion Energy theory (ii) Maximumstresstheory, alsospecifywhich diameter is considered as safe yield strength = 555MPA bending moment = 285NM torsional moment = 315NM

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A component is subjected to a maximum cyclic stress of 750 MPa and a minimum of 70 MPa. The steelfrom which it is manufactured has an ultimate tensile strength, σu, of 1050 MPa and a measured endurancelimit, σe, of 400 MPa. The fully reversed stress at 1000 cycles is 750 MPa. Using both the Goodman and Gerbermean stress correction procedures, calculate the component life.
6 cans containing soda made out of aluminum ( E = 69 GPa, σY = 240 MPa ) material are shaken. Shaking them creates an internal pressure of 0.14 MPa in each can. A uniform load of W is applied to the cans through a plate which has a negligible weight. The inner diameter of each can is 2R = 62 mm, the wall thickness is t = 0.25 mm and the length is L = 112 mm. According to the von - Mises yield criterion, determine the maximum magnitude of the applied load W. Note: The weight of the cans will be neglected in calculations. Accept that the liquid in the cans does not provide any support to the cans and no buckling occurs in the cans.
Tensile and fully reversed loading fatigue tests were conducted for a certain steelalloy and revealed the tensile strength and endurance limit to be 1200 and 550 MPa,respectively. If a rod of this material supply were subjected to a static stress of 600MPa and fully-reversed oscillating stresses whose total range was 700 MPa. Assuming garber relationship will this rod fail by fatigue failure
Tensile and fully reversed loading fatigue tests were conducted for a certain steel alloy and revealed the tensile strength and endurance limit to be 1200 and 550 MPa, respectively. If a rod of this material supply were subjected to a static stress of 600 MPa and oscillating stresses whose total range was 700 MPa, would you expect the rod to fail by fatigue processes? Hint: You may want to plot a diagram to aid in presenting your answer.
Analyse the differences between the 2 attached stress-strain curves for 0.9% carbon steel and 0.15% carbon steel.
An application requires ultimate tensile strength and yield strength ofa steel at 110 ksi and 91 ksi, respectively. Answer the following 4 questions:4.1. Can SAE 1040 steel be selected for this application?4.2. If “no” is the answer in Part I, the following Part II, III, and IV can beignored. If “yes” is the answer in Part I, which condition of SAE 1040 shouldbe selected?4.3. Why is that steel with the condition in part II selected?4.4. Is the selected steel brittle or ductile? and Why?
1. A part made of Aluminum 6061-T6 has a yield strength = 400 MPa. For each stress state below, draw all 3 Mohr's circles, find the principal stresses, and calculate the safety factor against yield using both the distortion-energy (von Mises) and maximum shear stress (Tresca) criterions. (If relevant) A clearly labeled diagram (or diagrams) clearly pertaining to your analysis with a coordinate system and relevant labels. Final answer with appropriate units and significant figures. You can use the fprintf() command in MATLAB to format numerical results A 2-3 sentence reflection on your answer. Does it make sense? Why or why not? What are some implications?
Produced from xCy steel material by machining method, the shaft is bedded at C and D points. With the shaft, constant Fy= 870 N forces in the vertical direction and constant Fx= 4,7 kN forces in the axial direction, which do not rotate together. The tensile strength of the shaft material is (sigma)tensile = 670 MPa and the yield strength is (sigma)yield = 470 MPa. For 50% reliability, analyze the fatigue damage condition of the shaft sections A and B separately. Note: Take SI unit and make the solutions legit and clear please
A high-strength steel has a yield strength of 1,460 MPa and a KIC of 98 MPa √m. Calculate the size of a surface crack that will lead to catastrophic failure at an applied stress of 3/4Y.S.
A bar AISI 1035 steel forged and heat treated with minimum yield strength of 570MPa is subjected to bending moment of 290Nm and a torsional moment of 310Nm. Assuming a factor of safety of 2, determine the diameter of rod using the following theories of failure (i) Maximum Shear stress theory and (ii) Distortion Energy theory (iii) Maximum stress theory, also specify which diameter is considered as safe
If you could produce AISI 1020 steel with a grain size of 50 nm, what would be the expectedyield stress, assuming a Hall--Petch response? (  MPa, k=0.56 MN/m3/2). Explain eachterm in H-P relation.
A gauge # 10 HSLA steel for an automotive application has a Young’s modulus of 200 GPa, a yield strength of 370 MPa and a ultimate tensile strength of 440 MPa. What is the punch force needed to punch a square hole with a side length of 20 mm on this HSLA steel? Show your work.