A cylinder with a 150 mm diameter and 300mm length is put under a compressive load of 665 kips. The modulus of elasticity for this specimen is 55 GPa and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region

A cylinder with a 150 mm diameter and 300mm length is put under a compressive load of 665 kips. The modulus of elasticity for this specimen is 55 GPa and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 6.2P

See similar textbooks

Similar questions

The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
A tensile test was performed on a metal specimen having a circular cross section with a diameter of 1 2 inch. The gage length (the length over which the elongation is measured) is 2 inches. For a load 13.5 kips, the elongation was 4.6610 3 inches. If the load is assumed to be within the linear elastic rang: of the material, determine the modulus of elasticity.
A cylinder with a 6.0 in. diameter and 12.0 in. length is put under a compressive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region.
A cylinder with a 6.0 in. diameter and 12.0 in. long is put under a compressive load of 150,000 lbs. The modulus of elasticity for this specimen is 8,000,000 psi. and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region.
A metal rod with 0.5 in. diameter and 12.0 in. length is put under a compressive load of 150 kips. The modulus of elasticity for this specimen is 8,000 ksi and Poisson’s ratio is 0.35. Calculate the final length and the final diameter of this specimen under this load assuming that the material remains within the linear elastic region
A stainless-steel rod 16mm in diameter and 300mm long is put under a tensile load of 250 kN. Assuming that the modulus of elasticity for this specimen is 250,000 MPa and the final diameter is 15.96 mm. Calculate the final length, in mm, and the Poisson’s ratio of this specimen under this load assuming that the material remains within the linear elastic region.
A cylinder with a 150 mm diameter and 300 mm length is put under a com-pressive load of 665 kN. The modulus of elasticity for this specimen is 55 GPa and Poisson’s ratio is 0.35. Calculate the final length and the final diameter ofthis specimen under this load assuming that the material remains within thelinear elastic region.
In a simple tensile test using a cylindrical test specimen (Dia.=10mm), the applied force was 120 kN and the extension was 2%. Find the modulus of elasticity of that specimen. If the standard modulus of elasticity is 200 GPa, is this material accepted or not? and why?
a liquid compressed in a cylinder has a volume of 1500cm³ at 1 mn/m² and a volume of 1495 cm³ at 2mn/m² . determine the bulk modulus of elasticity. answer must be correct.
A specimen is originally 300mm long and has a diemter of 11mm and it subjected to a force of 4kN. When the force is increased from 4kN to 7.5kN the specimen elongates 0.225mm. Determine the modulus of elasticity for the material if it remains linear elastic.
Consider a bar with a rectangular cross-section area with a thickness of t = 0.5 in. and height of h = 3.5 in. When force P = 19 kips is applied to the bar, the strain gages attached to the surface of the bar reads εx = 740 µε along the direction of the force and εy = -170 µε in the perpendicular direction. Determine Poisson's ratio for this specimen? Determine the modulus of elasticity for this specimen?in Ksi
To stretch a 200 mm long tensile test specimen (a) of steel elastically by 0.08 mm. How many loads do I need to apply? (b) What is the maximum length of this sample without plastic deformation? How long can it be extended? (The modulus of elasticity of steel is 210 GPa, yield strength 580 MPa, tensile strength 920 MPa specified as.