b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further reduced to 0.16 cm. Determine I. The total percent cold work and Il- Predict the properties of the metal at the calculated cold work? 0.16 cm I cm 0.5 cm Figure-2

b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further reduced to 0.16 cm. Determine I. The total percent cold work and Il- Predict the properties of the metal at the calculated cold work? 0.16 cm I cm 0.5 cm Figure-2

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: You are given three metal test samples, with the same chemical composition and differing grain…

A: Given data grain dia of sample A = 5 micron = 0.005 mm grain dia of sample B = 10 micron = 0.01 mm…

Q: Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a…

A: Solution: Note: Dear Student! As per our guidelines, we are only allowed to answer a single…

Q: Consider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are…

A: Strain-Hardening: Strain hardening (also known as work-hardening or cold-working) is the process of…

Q: Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a…

A: Minimum hardness HRC 40 d =3.75cm 4320 steel

Q: he figure shows two work pieces of steel of 0.3 %C nd 1.3 %C with different dimensions. compare…

A: For structure 1: The carbon percentage is 0.3% which means it will be more ductile and the structure…

Q: process which work above recrystallization temperature

Q: 2) A 1 in Dia x 3 in long mild steel hammer head is to be heat treated for surface hardening. If the…

Q: Answer by true (T) or false (F) for the folling sentences 1... meane shat sha melina d. 3. pve n…

A: Hot working and work hardening features are to be recalled. The effect of hot working on metal…

Q: -If the amont of the aded Carlbon is 2.2%s purity 78%) to 6000 kg iron . what is the e xepected…

A: Amount of the added carbon to pure iron = 2.2% Carbon Purity = 78% Mass of iron = 6000 kg rate of…

Q: c). Interpret the following diagram? The effect of carbon and heat treatment on the properties of…

A: Tempering heat treatment expands the extension however diminishes the ductile strength.The…

Q: The figure shows two work pieces of steel of 0.3 %C and 1.3 %C with different dimensions. compare

A: This is Fe-Fe 3C diagram. If the annealing process is carried out at controlled heating and cooling…

Q: A part made from hot-rolled AISI 1212 steel undergoes a certain amount of cold-work operation. If…

Q: Annealing is a process that can release the residual stress and make the grain size grow larger,…

A: Hardness inversely proportional to squere of grain size so option a was wrong.

Q: Answe rite the sentence on for 10 only 1- Mn Ni Cr, W, Mo, V are the most important elements that…

A: Given questions: 1. Mn, Ni, Cr, W, Mo, V are the most important elements that form austenite.2.…

Q: Consider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are…

A: Alloy: Alloy is a combination of two or more substances out of which one substance must be a metal…

Q: As shown in Fig. Q8, a uniform tensile stress creates a shear stress on crystal slip planes that lie…

A: Given: Applied tensile stress=σ=FA=100 MPaAngle = θ=45°

Q: Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340:…

A: Solution:

Q: Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a…

A: Solution: Note: Dear Student! As per our guidelines, we are only allowed to answer a single…

Q: Brass metal is subjected to a 156 Kgf load, with a 2.23 mm diameter of indenter. The indentation of…

Q: Q4: Answer with True or False: 1-Cooling rate when quenching steel in agitated water is faster than…

A: Note: Since you have posted a question with multiple sub-parts, we will solve first three sub- parts…

Q: (b) Figure 1 shows, the tensile engineering stress-strain curve for an aluminum alloy. Based on…

A: According to the details provided in the question, we need to calculate 1. yield strength 2.…

Q: Quenching is a process that can reduce the grain size and form a lot of grain boundaries in the…

A: Quenching: In this process metal is heated above its recrystallization and than cool it rapidly. The…

Q: You are given three metal test samples, with the same chemical composition and differing grain…

Q: he fatigue resistance of a material is reduced by: a)Poor surface finish b)A permanent residual…

A: The maximum stress that a material can endure for a predetermined number of cycles without…

Q: A sheet of a 70% Cu-30% Zn alloy is cold-rolled 20% to a thickness of 3.0mm. The sheet is then…

Q: Hall-Petch Constants Material Y; (MPa) k (MPa.ma) Copper 25 0.12 Titanium 80 0.40 Mild Steel 70 0.74…

Q: How do I manually calculate the Final temperature of Aluminum, unknown solid 1, unknown solid 2? How…

A: Specific heat of aluminium = . 89J/gC

Q: HOME WORK 1 The figure shows two work pieces of steel of 0.3 %C and 1.3 %C with different…

A: If the annealing process is carried out at controlled heating and cooling rates, Size will not…

Q: b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further reduced to 0.16 cm.…

A: Write the given data:

Q: You are given three metal test samples, with the same chemical composition and differing grain…

Q: For a steel alloy, specify the amount of deformation (%CW) that is necessary to give a minimum…

Q: Q3/ A-Define the following: Duplex stainless steel, Super alloy, Martinsite, Muntiz metal, Flam…

A: A. Duplex Stainless Steel - These are formed due the combination of ferritic and austenitic steel.…

Q: In your experiment, you select one piece of metal and heat it to 100.0 °C, and then select a second…

A: Given data: One piece of metal is heated to 100°C and another is cooled to -10°C The following are…

Q: By using the following figure, suppose aluminum alloy and carbon steel have the same tensile…

A: As, from the given graph it is clear that energy absorption for fcc material is very high.

Q: Metal y (mJ/m).n Šlip Character (a) Discuss why Planar slip is associated with a small stacking…

A: (a) it is asking the reason by which the planer slip is associated with small stacking fault energy.…

Q: Q3B) A metal is fabricated by drawing at 125 °C. The metal melting temperature is 400 °C. Find by…

A: Given dataFabricated Temperature (T) (a) Working Temperature=125°CMelting Temperature=400°C Tm

Q: 2) Explain the reason for the quenching cracking that may occur when hardening some parts. By…

Q: The carbon content of the steels increases, the steels befome more and the DBTT I. ductile,…

Q: Are there any procedures to prevent grain growth of heat affected zone (HAZ)?

A: Solution:

Q: A brass plug is to be placed in a ring made of iron. At 20°C, the diameter of the plug is 8.755 cm…

Q: A flat plate subjected to a tensile force <N is an shown in Fig. Q2(c). The plate erial is gray cast…

Q: Hot working of metals can be done at below recrystallization temperature. Select one: True False

A: Forming operation on metals can be done broadly in two ways: Hot working Cold working

Q: (d-1) From the graph shown, which point(s) represent(s) a state of the alloy (%CW) where it starts…

A: The following points should be kept under mind which considering the correct options- 1)In the…

Q: 1. Explain in 1-3 bullets how as a practicing engineer you determine the yield strength of a metal…

Q: 1600 Question 4. An austenitized 4340 standard steel bar is cooled at different rates (see Figure…

Q: Question-1 A 70% Cu-30% Zn brass wire is cold-drawn 20 percent to a diameter of 2.80 mm. The wire is…

Concept explainers

Engineering Drawing

Technical drawing has been around since ancient times. As in the ancient Renaissance, complicated drawings were created, including Leonardo da Vinci's drawing. Modern engineering drawing, including its specific orthographic projection with scale conventions, began in Europe (France) during the early stages of Industrialization. L.T. C. Rolt also made some of Marc's drawings for its block-making machinery (in 1799) that also may have contributed significantly to British engineering technology. Since he learned the art of presenting three-dimensional(3D) items in a two-dimensional(2D) plane, as we now term mechanical drawing. 

Question

b) A 1-cm-thick copper plate is cold-reduced to 0.50 cm and later further
reduced to
0.16 cm. Determine
I. The total percent cold work and
Il- Predict the properties of the metal at the calculated cold work?
0.16 cm
I cm
0.5 cm,
Figure-2

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Trending now

This is a popular solution!

Step by step

Solved in 4 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

A 2.0-inch diameter 4140 steel bar is austenized and tempered in oil without Agitation, determine the resulting hardness at 0.6 inches below the surface, present all the Procedure to arrive at the answer (include sketch of the piece and graph used with steps Using word forms)
Seems to be Option E) is Right. But What formula we need to use? Please quick. 1) Determine the hardening exponent of the metal with 2/3 of the average yield stres. a 0. 383 B. 0.35 C.0.3 D.0.333 E. 0.5
A 2.0-inch diameter 4140 steel bar is austenized and tempered in oil without Agitation, determine the resulting hardness at 0.6 inches below the surface, present all the Procedure to get to the answer
As the tempering temperature of a heat treated steel increases the associated values of Brinnell hardness also increase, while the values of tensile strength and yield strength decrease. True or false
1-llustrate the process which work above recrystallization temperature with neat sketch?
The figure shows two work pieces of steel of 0.3 %C and 1.3 %C with different dimensions. compare between them regarding the diagram that shows the stages of softening annealing treatments. Subject: Metallurgy
Using the graphs in Figures for Q2 (b) & (c), select a metal alloy for an application that requires a tensile strength of at least 370 MPa while maintaining a minimum ductility of 27%. If the metal may be cold worked, decide which of the following is a suitable material; copper, brass or 1040 steel. You need to explain your selection process.
Are there any procedures to prevent grain growth of heat affected zone (HAZ)?
What is the hardening exponential n and deformation rate sensitivity exponential m ? Comment similar or different aspects, their numerical values should be big or small and changes with temperature
Q2. Explain hot working process with respect to microstructure. Also draw the diagram of microstructure. briefly.
Explain the effect of annealing to cold worked metal when the heating is done in range of recovery, recrystallization and grain growth stage.
If you could produce AISI 1020 steel with a grain size of 50 nm, what would be the expectedyield stress, assuming a Hall--Petch response? (  MPa, k=0.56 MN/m3/2). Explain eachterm in H-P relation.