Following is the Tensile stress-strain data for several hypothetical metals to be used. Answer the following questions referring to table 1.1. Table 1.1: Material Property Data Material Tensile Strength Fracture Strength Strain at Strength (MPa) (MPa) 340 265 550 505 112 150 Fracture before yielding B C D 0.23 0.15 0.40 a. Which will experience the greatest percent reduction in area? Why? b. Which is the strongest? Why? c. Which is the stiffest? Why? Elastic Modulus (GPa) 210 310 180 400

Following is the Tensile stress-strain data for several hypothetical metals to be used. Answer the following questions referring to table 1.1. Table 1.1: Material Property Data Material Tensile Strength Fracture Strength Strain at Strength (MPa) (MPa) 340 265 550 505 112 150 Fracture before yielding B C D 0.23 0.15 0.40 a. Which will experience the greatest percent reduction in area? Why? b. Which is the strongest? Why? c. Which is the stiffest? Why? Elastic Modulus (GPa) 210 310 180 400

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

a) Compression tests are generally performed on brittle materials-why?b) How a cast iron specimen fails under compression load?c) Define secant modulus?
Answer the following questions briefly,a) Compression tests are generally performed on brittle materials-why? b) How a cast iron specimen fails under compression load? c) Define secant modulus? d) Why alignment of the specimen is is important in compression test? e) Which is the IS code used for compression test on metals?
A material has the following properties, ultimate Sul = σul = 350mpa, the strain hardening exponent n=0.20. Determine the value for the strength coefficient K.
Determine the tensile yield strength (0.2% offset) and the maximum strength of a metal alloy having the following tensile stress-strain diagram. Select one: The tensile yield strength Sy = 100 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 170 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 150 Mpa and the maximum strength Smax = 200 Mpa. The tensile yield strength Sy = 240 Mpa and the maximum strength Smax = 250 Mpa. The tensile yield strength Sy = 80 Mpa and the maximum strength Smax = 250 Mpa.
(SI Units) In a tensile test on a steel specimen, true strain = 0.11 at a stress of 245 MPa. When true stress = 340 MPa, true strain = 0.31. Determine the strength coefficient and the strain-hardening exponent in the flow curve equation.
For a certain high-temperature alloy, failure was reported after 4100 hrs at 680°C when subjected to a stress level of 270 MPa. If the same stress were applied at 725°C, how long would the sample be expected to last? State any assumptions you must make to allow you to make this determination.
Draw the tensile curves of the following materials, taking into account the appropriate elongation at break, modulus of elasticity and tensile stress, on the side stress-strain graph. a)Low carbon steel (Ecelik=200Gpa),(Syield=300MPa),(Stensile=400MPa) b)High carbon steel (Esteel=200GPa),(Stensile=700MPa) c)Aluminum (Ealuminum=70GPa), (Syield=200MPa),(Stensile=300MPa) d)Cast iron (Ecast iron=120GPa),(Stensile=200MPa)
Note: Kindly give me both right answers. A) Did the ductile materials (annealed and aluminium) react differently to the two different testing methods (hardness test vs. tensile test)? What does this say about the behaviour of ductile materials in compression vs. tension? B) Did the brittle material (quenched) react differently to the two different testing methods (hardness test vs. tensile test)? What does this say about the behaviour of brittle materials in compression vs. tension? （Three to five sentence answers are good）（engineering material)
information: "When performing a tensile test of a metal, these values were found for stress and strain. the yield strength (YS) is stress at 0.2% plastic strain" The task: A 5 meter long rod of this material is loaded axially with a stress of 244 MPa.i. How long is the rod under load?ii. Then the bar is relieved, how long is it now?
Q1a) A sample of an aluminum alloy has a tensile strength of 275 MPa, What will be the maximum force that can be withstood by a rod of that alloy with a cross-sectional area of 2.09 cm2?
As the tempering temperature of a heat treated steel increases the associated values of Brinnell hardness also increase, while the values of tensile strength and yield strength decrease. True or false
Consider the tensile stress-strain diagram below. If samples 1 and 2 are identical except that they were tested at different temperatures, which sample was tested at a lower temperature? Note: This question will be marked negatively so consider your answer carefully. A. Sample 1 B. Both were tested at the same temperature/ Alby is by die dieselfde temperatuur getoets C. Sample 2