or a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and rystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and rystalline states is 0.870 g/cm³ and 0.998 g/cm3 respectively) This question has only one correct answer) O a. % Crystallinity = 55.45% O b. % Crystallinity = 57.25% O C. % Crystallinity = 76.99% O d. % Crystallinity = 82.30% O e.

or a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and rystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and rystalline states is 0.870 g/cm³ and 0.998 g/cm3 respectively) This question has only one correct answer) O a. % Crystallinity = 55.45% O b. % Crystallinity = 57.25% O C. % Crystallinity = 76.99% O d. % Crystallinity = 82.30% O e.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In solid state sintering of compacted metal powder material, discuss how the progress of microstructure changes in sintering can be observed by microscopy. Support your discussion with suitable schematic diagram.
What happens in the powder mixture if granulation is over wetted and under wetted? How can this be prevented?
In powder processing, a cylinder with a diameter of 2 inches and a height of 10 inches is to be made from fine copper powders. A single-action press is used for compaction. If the average density of the green product is 7 g/cm3 at the bottom half of the cylinder, estimate the compaction pressure at the punch surface. Assume no friction between the powders. The coefficient of friction between particles and containers is 0.2.
The part shown in Figure is to be pressed from fine copper powders using a compaction pressure of 1000 MPa. Dimensions are milimetres. Determinea) the required press tonnage to perform this operationb) the final weight of the part if the porosity is 15%. Assume shrinkage during sintering can be neglected. (the desity of copper =8,97g/cm3 )
Discuss the effect of monomodal and bimodal particle size distribution of powderson the microstructure and properties of advanced ceramics. Which starting powders would youprefer and WHY?
GKN Sinter Metals Company pressed iron powders using a compaction pressure of 600 MPa to produced a cylindrical bearing which is 70 cm long and has internal and external diameters of 8 cm and 16 cm, respectively. Determine (a) the most appropriate pressing direction, (b) the required press tonnage to perform this operation, and (c) the final weight of the part if the porosity is 12%, given that the density of iron, ρ = 7.87 g/cm3. Assume shrinkage during sintering can be neglected
Is reconstitution the act of mixing a liquid with a powder to make a liquid form?
What were the main needs to develop colloidal technique for powder processing, explain your arguments clearly?
A process that is used to make high-quality technical ceramics is called sintering (see images below). During the early stage of sintering, individual particles are attached by the formation of necks. How do the so-called necks form? (In other words, what processes are occurring that cause the necks to form?)
1. How did the consistency of the jelly change when you changed the ratio of sugar to pectin? 2. Why did the consistency change when you changed the ratio of sugar to pectin?
1- List all steps involved in powder metallurgy (P/M) process. 2- Briefly explain each step taken plagiarism into consideration, please.
Should green compacts be brought up to the sintering temperature slowly or rapidly? Explain your reasoning.