Q.1: Ifa material is cast iron (ultimate tensile strength = 300 Mpa, ultimate compressive strength - 900 Mpa) and the stress state at a point is shown in Fig. 1. Using a graphical method, find safety factor against static failure using 100 Mpa (a) Rankine failure theory (b) Coloumb - Mohr theory (c) Modified Coloumb - Mohr theory 50 Mpa 20 Mga

Q.1: Ifa material is cast iron (ultimate tensile strength = 300 Mpa, ultimate compressive strength - 900 Mpa) and the stress state at a point is shown in Fig. 1. Using a graphical method, find safety factor against static failure using 100 Mpa (a) Rankine failure theory (b) Coloumb - Mohr theory (c) Modified Coloumb - Mohr theory 50 Mpa 20 Mga

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter8: Applications Of Plane Stress (pressure Vessels, Beams, And Combined Loadings)

Section: Chapter Questions

Problem 8.2.4P: Solve the preceding problem if the internal pressure is 3,85 MPa, the diameter is 20 m, the yield...

See similar textbooks

Similar questions

Solve the preceding problem if the internal pressure is 3,85 MPa, the diameter is 20 m, the yield stress is 590 MPa, and the factor of safety is 3.0. (a) Determine the required thickness to the nearest millimeter. (b) If the tank wall thickness is 85 mm, what is the maximum permissible internal pressure?
answer this ; The factors of safety predicted at point H by the maximum shear stress theory of failure (Tresca criterion)
A material is subjected to plane stress. Express the distortion energy theory of failure in terms of sx, sy, and txy.
Strength of Material TextbookTopic: Factor of Safety for Stress LimitsProvide step by step solution
A spherical pressure vessel 300 mm in diameter has a uniform thickness of 6 mm. The vessel contain gas under pressure of 6000 kPa. If the ultimate tensile stress is 450 MPa, what is the factor safety with respect to tensile failure?
If d=40 mm, L=796 mm, F=29 kN, T=1.7 kNm and fail stress=156 MPa, calculate the apparent factor of safety for this loading condition. Give your answer to 2 decimal places.
-Define the maximum shear stress theory and sketch its failure envelope.-Define the maximum shear strain energy theory and sketch its failure envelope
A spherical pressure vessel 400-mm in diameter has a uniform thickness of 6 mm. The vessel contain gas under a pressure of 8,000 KPa. If the ultimate tensile stress of the material is 420 MPa, what is the factor of safety with respect to tensile failure?
The factors of safety at point H predicted by the maximum-distortion-energy theory (von Mises criterion) can be calculated as The von Mises equivalent stresses at point H can be calculated as MPa
See the set of bars for made of a material that has a yield strength of 350 MPa, determine the minimum h1 and h2 dimensions required. Apply a safety factor F.S. = 1.5 without flow. Each bar is 12 mm thick
1. A part made of Aluminum 6061-T6 has a yield strength = 400 MPa. For each stress state below, draw all 3 Mohr's circles, find the principal stresses, and calculate the safety factor against yield using both the distortion-energy (von Mises) and maximum shear stress (Tresca) criterions. (If relevant) A clearly labeled diagram (or diagrams) clearly pertaining to your analysis with a coordinate system and relevant labels. Final answer with appropriate units and significant figures. You can use the fprintf() command in MATLAB to format numerical results A 2-3 sentence reflection on your answer. Does it make sense? Why or why not? What are some implications?
Determine the yield strength of a material required such that the component would not fail when subject to the following stresses sigma1 = 2 MPa and sigma 2= -15 MPa sigma 3 = 10 MPa). Use a yield criterion that assumes that yield failure will occur when the maximum shear stress in the complex system becomes equal to the limiting shear strength in a simple tensile test.