The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: load(KN) 0 40 80 95 90 135 150.2 145 130 120 elongation(mm) o 0.022 0.13 0.25 0.55 2.01 3.88 4.12 5.22 6 Plot engineering and True (stress-strain) curves, then determine the (oy, ɛy), (ou, ɛu), (of, , ɛf), ductility, modulus of elasticity .

The following data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: load(KN) 0 40 80 95 90 135 150.2 145 130 120 elongation(mm) o 0.022 0.13 0.25 0.55 2.01 3.88 4.12 5.22 6 Plot engineering and True (stress-strain) curves, then determine the (oy, ɛy), (ou, ɛu), (of, , ɛf), ductility, modulus of elasticity .

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter1: Tension, Compression, And Shear

Section: Chapter Questions

Problem 1.6.7P: A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The...

See similar textbooks

Similar questions

A wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The wire is made of a copper alloy having a stress-strain relationship that may be described mathematically by =18,0001+30000.03(=ksi) in which is nondimensional and has units of kips per square inch (ksi). (a) Construct a stress-strain diagram for the material. (bj Determine the elongation, of the wire due to the Forces P. (c) IF the forces are removed, what is the permanent set of the bar? (d) If the forces are applied again, what is the proportional limit?
Civil engineers often use the straight-line equation, = b 0 + b 1x, to model the relationship between the shear strength y of masonry joints and precompression stress, x. To test this theory, a series of stress tests were performed on solid bricks arranged in triplets and joined with mortar. The precompression stress was varied for each triplet and the ultimate shear load just before failure (called the shear strength) was recorded. The stress results for n = 7 resulted in a Coefficient of Determination of 0.8436. Given that r 2= 0.8436, give a practical interpretation of r 2, the coefficient of determination for the least squares model. a. We expect to predict the shear strength of a triplet test to within about 0.8436 tons of its true value. b. About 84.36% of the total variation in the sample of y-values can be explained by (or attributed to) the linear relationship between shear strength and precompression stress. c. In repeated sampling, approximately 84.36% of…
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph.
In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
The stress-strain diagram of a reinforcement steel having a cross-sectional diameter of 12 mmdiameter and 100 mm gage length is determined after its tensile strength test as follows. Based on the stressstrain diagram determine the followings properties of the material (Poisson’s ratio of the material is 0.32) : a) Modulus of elasticityb) Yield strengthc) Toughnessd) Resiliencee) Shear modulusf) Bulk modulusg) Ductility as described bypercent change in length
A mild steel bar went through a tensile test conducted at the University of San Carlos Mechanical Engineering Laboratory. The following data was obtained from the test: i. Diameter of the steel bar = 30 mm ii. Gauge length of the bar = 200 mm iii. Load at the elastic limit = 250 kN iv. Extension at a load of 150 kN = 0.21 mm v. Maximum load = 380 kN vi. Total extension = 60 mm vii. Diameter of the rod at the failure = 22.5 mm Determine the Young’s modulus, the stress at the elastic limit, the percentage elongation, and the percentage decrease in area.
A Copper specimen of circular cross-section is subjected to a tensile test. The data obtainedare:Length of Specimen = 329 mm;Diameter of Specimen = 39 mm;Load at Yield Point = 130 kN;Maximum Load = 219 kN;Load at fracture = 118kNDetermine the following:1) Find initial area of the test specimen2) Yield Stress3) Ultimate Stress4) Fracture stress5) Find the strain for 0.058mm elongation.6) Mark Yield stress, Ultimate stress and Fracture stress on a Stress-Strain diagram.
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 150 kN. - Length of the specimen is 24 mm. - The yield strength is 78 kN/mm2. - The percentage of elongation is 42 %. Determine the following iii) Stress under an elastic load of 14 kN, iv) Young's Modulus if the elongation is 1.7 mm at 14 kN and (v) Final diameter if the percentage of reduction in area is 26 %. I wont answer for this three questions only: 1)Final Area of the Specimen at Fracture (in mm) 2)Final Diameter of the Specimen after Fracture (in mm) 3)Initial Cross-sectional Area (in mm2)
A tensile test is conducted on a mild steel bar. The following data was obtained from the test : diameter of the steel bar= 3cm, Gauge Length of the bar = 20cm, Load at Elastic limit= 250kN, Extension at a load of 150kN= 0.21 mm, Maximum Load = 380kN, Total Extension= 60mm, Diameter of the rod at failure=2.25cm, determine young's modulus?
A sheet metal cutting machine cuts the sheet metal via shear force, V as shown in Fig. 1. The crosssection of sheet metal is rectangular with width, b = 3m and thickness, d = 5mm. The sheet metal ishaving yield strength σy = 220 MPa; Young’s modules, E = 200 GPa and Poisson’s ratio, ν = 0.3.Conduct the following analyses at the state of stress when maximum stress reaches σy and beforeshearing commences. (Need answer Question c) & d) c. Sketch the YIELD LOCI for both cases above. d. As a sheet-metal engineer, which failure criterion in (b) will you use to determine the cuttingshear force? Explain the reason for your answer.