The following data was obtained from a tensile test on Load (kN ) Extension (mm) 16 32 56 72 95 110 132 142 140 135 0.2 0.4 0.7 0.9 1.5 2.5 5.0 8.5 10.0 12.0 a specimen of 10mm diameter and gauge length 60mm. Using the graph paper supplied, plot the load-extension diagram and determine: (1) The tensile strength (2) 0.1% Proof Stress (3) Young's Modulus for the specimen

The following data was obtained from a tensile test on Load (kN ) Extension (mm) 16 32 56 72 95 110 132 142 140 135 0.2 0.4 0.7 0.9 1.5 2.5 5.0 8.5 10.0 12.0 a specimen of 10mm diameter and gauge length 60mm. Using the graph paper supplied, plot the load-extension diagram and determine: (1) The tensile strength (2) 0.1% Proof Stress (3) Young's Modulus for the specimen

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

In a tensile test on a specimen of black mild steel of 12 mm diameter, the following results were obtained for a gauge length of 60 mm. Load W(kN) 5 10 15 20 25 30 35 40 Extension x (10-3 mm) 14 27.2 41 54 67.6 81.2 96 112 When tested to destruction. Maximum load = 65 kN; load at fracture = 50 kN, diameter at fracture = 7.5 mm, total extension on gauge length = 17 mm. Find young's modulus, specific modulus, ultimate tensile stress, breaking stress, true stress at fracture, limit of proportionality, percentage elongation, percentage reduction in area. The relative density of the steel is 7.8. Draw the straight line graph. Answer: breaking stress,true stress at fracture and limit of proportionality.
The following results were obtained in a tensile test on a mild steel specimen of original diameter 28 mm and gauge length 56 mm. Load at limit of proportionality : 96 kN Extension at 96 kN load : 0.068 mm Load at yield point : 105 kN Maximum load : 170 kN When the two parts were fitted together after being broken, the length between gauge length was found to be 65.8 mm and the diameter at the neck was 18.8 mm. Calculate: (a). E, (b).σy, (c).σu, (d). PRIA and PE
Question Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the yield strength (in MPa) of the material. - Calculate the percent elongation of the specimen at yield point. (Use at least five decimal units) - Calculate the stiffness (in MPa) of the specimen material. - Calculate the ultimate strength (in MPa) of the material. - Calculate the percent elongation of the specimen at point of ultimate strength.
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Determine the true stress (in MPa) at yield point. - Determine the true stress (in MPa) at point of ultimate strength. - Determine the true stress (in MPa) at fracture point. - Determine the true strain (in mm/mm) at yield point. (Use at least five decimal units) - Determine the true strain (in mm/mm) at point of ultimate strength. (Use at least five decimal units) - Determine the true strain (in mm/mm) at fracture point. (Use at least five decimal units)
Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. Question 1 ;Determine the elastic energy absorption capacity (in N.mm) of that specimen. Question 2; Determine the plastic energy absorption capacity (in N.mm) of that specimen.
The following data were obtained from a standard tensile stress test on a mild steel specimen. Graph the result and determine proportional limit stress and Young’s Modulus.
I want answers to all four questions if possible. Thanks for help :) Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) - Determine the toughness index number (in N.mm/mm3) of the material.
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
A test rod of rust-resistant steel, with a diam. of 12.8 mm and a measuring length of 50.8 mm is subjected to a tensile test. The data from the test is shown in the table below.
A) An engineer works for a company that has many gray cast iron rods of different diameters and would like to design an equivalent rod that could handle a force of P= 10.0 kipkip without fracturing. What is the minimum diameter that this new rod must have to support P? B)A tensile test is being conducted on a steel-rod specimen with a gauge length of L0 = 4.0 in and an initial diameter of d0 = 0.75 in. If the final length of the rod at fracture is Lf= 5.53 in , find the percent elongation of the rod at fracture.
A tension test specimen had a gauge length of 2.5 in. After the test, the gauge length had increased to 6.5203 in. What is the uncertainty in the percentage elongation calculation of the specimen, if a caliper having an uncertainty of 0.001 in was used for measuring the length?
Annealed low-carbon steel has a flow curve with strength coefficient = 80,000 lb/in2 and strain-hardening exponent = 0.25. A tensile test specimen with gage length = 2.0 in is stretched to a length = 3.5 in. Determine the flow stress and average flow stress that the metal experienced during this deformation. use correct stratgy and correct E 0.55962