HW1The following data were obtained from a tensile test on a specimen of10 mm diameter and gauge length 60mm , the diameter after fracture was7mm . Using the graph paper supplied, plot the load-extension diagram andthen1- Plot the data as engineering stress versus engineering strain.2- Determine Young Modulus3- Determine the yield strength at a strain offset of 0.002.4- Determine maximum tensile strength of this alloy.5- What is the approximate ductility?Load (kN)Extension (mm) | 0.2132 | 142140 1358.5 10.0 12.016325672951100.40.70.91.52.55.0

Answered: Image /qna-images/answer/843417e2-3feb-4673-8522-e7c9a5f0ad5a.jpg

The following data were obtained from a tensile test on a specimen of 10 mm diameter and gauge length 60mm , the diameter after fracture was 7mm . Using the graph paper supplied, plot the load-extension diagram and then

The following data were obtained from a tensile test on a specimen of 10 mm diameter and gauge length 60mm , the diameter after fracture was 7mm . Using the graph paper supplied, plot the load-extension diagram and then

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Draw a typical stress vs strain tensile test curve for the following material and label the axis. A typical brittle material subjected to a tensile stress that has been applied to the material till the sample breaks. 1- label the axis and draw the curve for a brittle material. 2- indicate the maximum strength of the material. 3- show on the portion of the curve where young's modulus can be calculated.
A tensile test specimen has a starting gage length 50 mm and a cross-sectional area 200 mm2. During the test, the specimen yields under a load of 30,000 N (this is the 0.2% offset) at a gage length of 52 mm.The maximum load of 63,000 N is reached at a gage length of 57 mm just before necking begins. Final fracture occurs at a gage length of 63.5 mm. Determine (a) yield strength, (b) modulus of elasticity, (c) tensile strength, (d) engineering strain at maximum load, and (e) percent elongation.
Tensile test under 40,000 N load was applied to a low carbon steel with a sample diameter of 6 mm. As the diameter of the specimen under load decreases to 5 mm, calculate a) Engineering stress and% elongation values, b) Actual stress and% elongation values.
Answer as soon as possible please Sketch the typical engineering stress-strain diagram behaviour to fracture point, F and the tensile strength TS, together with the geometry of the deformed specimen at various point along the curve.
During stress-strain test, the unit deformation at a stress of 35 MPa was observed to be 167 x 10^-6 m/m and at a stress of 140 MPa it was 667 x 10^-6. If the proportional limit was 200 MPa, what is the modulus of Elasticity (GPa)? What is the strain corresponding to a stress of 80 MPa?
Sketch the typical engineering stress-strain diagram behaviour to fracture point, F and the tensile strength TS, together with the geometry of the deformed specimen at various point along the curve.
A sample of giant reed is shaped into a beam with a square cross section of 15.5 mm by 15.5 mm. Two supports placed 22.1 mm apart support thesample and a load is applied halfway between the support points in order to test the force required to fracture the sample. If ultimate tensile strength is912 MPa, what would be the force F (newtons) required to cause failure?
A hot rolled steel tension test sample has a diameter of 6 mm and the original gage lenght of 30 mm. In a test to fracture, the stress and strain data below were obtained. Complete table.
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
When an aluminum tensile sample with an initial diameter of 12.827 mm was tested, a maximum load of 66.72 kN was recorded at an engineering strain of 0.4 . What is the load on an identical tensile sample with an engineering strain of 0.2 ?
(Suppose you need to design a tension test machine capable of testing specimens that have nominal ultimate stresses as high as σu = 100 ksi . How much force must the machine be capable of generating? Assume the testing specimen has the ASTM shape shown. Answer for this is 19.6 kip) (If the maximum nominal strain is ϵf = 0.7 just before the test specimen fractures and the test machine operates by moving only one grip, how far must that grip be designed to travel? The total length of the deforming part of the specimen is 3 in. Answer for this is 2.10 in) Do not know if this info is needed but this was the other 2 parts
You are called as an expert witness to analyze the fracture of a sintered silicon carbide plate that was fractured in bending when a blunt load was applied to the plate center. Measurement of the distance between the fracture origin and the mirror/mist boundary on the fracture surface gives a radius of 0.796 mm. You are given three pieces of the same SiC to test, and you determine that the mirror radius is 0.603, 0.203, and 0.162 mm for bending failure stress levels of 225, 368, and 442 MPa, respectively. What is your estimate of the stress present at the time of fracture for the original plate?