Which of the following is true about open die forging process? Forged pieces have accurate dimensions therefore there is usually no need for additional finishing operations such as heat treatment or machining. O Forged pieces have outstanding grain structure and the best combination of mechanical properties. O Forging is carried out at temperature above re-crystallization temperature O Forged pieces are small in size since the forging process is incapable of doing large components such as turbine shafts.

Which of the following is true about open die forging process? Forged pieces have accurate dimensions therefore there is usually no need for additional finishing operations such as heat treatment or machining. O Forged pieces have outstanding grain structure and the best combination of mechanical properties. O Forging is carried out at temperature above re-crystallization temperature O Forged pieces are small in size since the forging process is incapable of doing large components such as turbine shafts.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

QUESTION 3 Extrusion and drawing have numerous application in manufacturing continuous as well as discrete products from a wide variety of metals and alloys. There are three types of extrusion. Please describe and draw the schematic illustration to represent each of them. Question 4 Selection of die in forging process is very important in order to control the quality of the product. List four general requirements for die material.
(USCS units) A part is hot forged in an impression die. The projected area of the part, including flash, = 17.3 in2. After trimming, the part has a projected area of 12.5 in2. Part geometry is complex. As heated the work metal yields at 13,000 lb/in2and no strain hardening occurs. At room temperature, the metal yields at 30,000 lb/in2. Determine the maximum force required to perform the forging operation. (use table 18.1 for Kf )
An automated blanking and forming line is designed to from 2 mm thick sheet, made from 2024 Aluminum, T4 temper, into a square sheet metal part. Elongation at 50mm 20% Young’s Modulus 70GPa Yield strength 325 MPa UTS 470 A) What is the force required to punch a square piece that is 500 mm on each edge? B) If the sheet blank was bent to a radius of 5 mm, what will be the radius after springback occurs? C) What is the required bend angle to achieve a 90° final bend angel for a bend radius of 5 mm?
3XPL@!N THE PROCESS @ND PROVIDE EXAMPLES FORMING OPERATIONS 1. Forging is mechanically working or deforming a single piece of a usually hot metal; this may be accomplished by the application of successive blows or by continuous squeezing. 2. Rolling, the most widely used deformation process, consists of passing a piece of metal between two rolls; a reduction in thickness results from compressive stresses exerted by the rolls. 3. Extrusion, a bar of metal is forced through a die orifice by a compressive force that is applied to a ram; the extruded piece that emerges has the desired shape and a reduced cross-sectional area. 4. Drawing is the pulling of a metal piece through a die having a tapered bore by means of a tensile force that is applied on the exit side.
1) A upset forging operation is performed in an open die. The initial size of the workpart is: Do = 63 mm, and ho = 100 mm. The part is upset to a diameter = 70 mm. The work metal has a flow curve with strength coefficient = 600 MPa and strain hardening exponent= 0.22. Coefficient of friction at the die-work interface = 0.40. Determine (a) final height of the part, and (b) maximum force in the operation.
Please answer to both parts: (a) Explain the function of a dummy block in the Direct Extrusion Process. (b) Explain the differences between Forward Extrusion and Reverse Extrusion processes.
Which would you recommed based on your understanding and explain on it each of isa. hot forging and heat treating a workpiece orb. cold forging it and relying upon strain hardening for strengthening? Manufacturing Process
1) Selection of die in forging process is very important in order to control the quality of the product. List four general requirements for die material.
How can you tell if a metal part is forged or cast. Describe the properties you would have investigated.
The following shapes of parts are desired to blanked from a sheet metal of 3mm, half-hard cold rolled steel whose shear strength = 330 MPa. Determine (a) the appropriate punch and die diameters, (b) blanking force.
A cylindrical billet that is 100 mm long and 50 mm in diameter is reduced by indirect (backward) extrusion to a 20 mm diameter. The die angle is 90°. In the Johnson equation, a = 0.8 and b = 1.4. In the flow curve for the work metal, the strength coefficient = 800 MPa and strain hardening exponent = 0.13. Determine (a) extrusion ratio, (b) true strain (homogeneous deformation), (c) extrusion strain, (d) ram pressure, and (e) ram force Please answer d and e (a) Calculate the extrusion ratio. r=6.25 (b) Calculate the true strain. εtrue=1.8333 (c) Calculate the extrusion strain by using Johnson's equation. εext =3.366
1. A component is designed to be hot forged in an impression die. The projected area of the product is 5800 mm2. During the forging process flashing is formed so that the area including the flash will be 8900 mm2. The part geometry is considered to be simple and the heated work material yields at 92 MPa. Calculate the maximum force required to perform the operation. 2. What are the advantages and disadvantages to forge a product through the open forging process, rather than to machine it from the same material?